Method for processing hollow glass with lined aluminum plate

A processing method and glass technology, applied to the processing field of lined aluminum plate insulating glass, can solve the problems of easy displacement, waste of resources, inaccurate installation position, etc., and achieve the effect of accurate installation position and resource saving.

Inactive Publication Date: 2010-02-24
江苏蓝星新材料有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the common insulating glass is to press two pieces of coated glass together through a hollow aluminum frame. In order to meet the requirements of customers, an aluminum plate needs to be added between the two pieces of coated glass. Generally, both sides of the aluminum plate are coated with butyl glue, and then Paste the two pieces of coated glass separately, which will make the installation position inaccurate, easy to shift, and cause scratches to the film surface. At the same time, such a large area of ​​glue is also a waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0016] A kind of embodiment of the processing method of the aluminum-lined hollow glass of the present invention is: comprise the following steps:

[0017] A: Choose 6mm glass, cut it into glass pieces according to the predetermined size with a cutting machine, edge the glass piece with an edge grinder, clean the glass piece with a washing machine, and then temper the glass piece. , it needs to be heated to 700°C, and then cooled rapidly and then slowly by changing the wind pressure until the temperature reaches 50°C;

[0018] B: Send the tempered glass sheet into the coating chamber for coating;

[0019] C: Remove the edge film from the coated glass sheet, clean it at a speed of 4 m / min, and put the cleaned glass sheet into the lamination chamber, the room temperature of the lamination chamber is 24°C, and the relative humidity is 30%;

[0020] D: Apply butyl glue to the bent hollow aluminum frame for the first time, place the glue-coated hollow aluminum frame on the glass s...

Embodiment approach 2

[0027] A: Choose 9mm glass, cut it into glass pieces according to the predetermined size with a cutting machine, edge the glass piece with an edge grinder, clean the glass piece with a washing machine, and then temper the glass piece. , it needs to be heated to 720°C, and then cooled rapidly and then slowly by changing the wind pressure until the temperature reaches 40°C;

[0028] B: Send the tempered glass sheet into the coating chamber for coating;

[0029] C: Remove the edge film from the coated glass sheet, clean it at a speed of 4 m / min, and put the cleaned glass sheet into the lamination chamber, the room temperature of the lamination chamber is 26°C, and the relative humidity is 28%;

[0030] D: Apply butyl glue to the bent hollow aluminum frame for the first time, place the glue-coated hollow aluminum frame on the glass sheet without edge film, and position it;

[0031] E: Fill the hollow aluminum frame with desiccant;

[0032] F: Paste double-sided tape along the in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for processing hollow glass of a lined aluminum plate, which comprises the steps of: selecting a piece of glass, and cutting the glass into glass sheets for edging, cleaning and toughening; placing the glass sheets into a coating chamber for coating; removing edge films of the coated glass sheets, cleaning the same and then putting the same into a sheet-combining chamber; gluing a hollow aluminum frame for the first time, and putting hollow aluminum frame / the same over the glass sheets for positioning; filling the hollow aluminum frame with driers; adhering double sided adhesive tapes along four internal frames of the hollow aluminum frame, and pasting an aluminum plate with the hollow aluminum frame; gluing the hollow aluminum frame for the second time, putting the second piece of coated sheet sequentially into a cleaner, the sheet-combining chamber for positioning, and a sheet presser for combination; drilling a small hole in the upper and lower edgeparts of the hollow aluminum frame, respectively, for inflation; rubberizing the butyl rubber around the hollow aluminum frame for the final sealing. The processing method has the advantages of accurate location for mounting, no scratch on film surfaces and resource saving.

Description

Technical field: [0001] The invention relates to a processing method of an aluminum-lined hollow glass. Background technique: [0002] At present, the common insulating glass is to press two pieces of coated glass together through a hollow aluminum frame. In order to meet the requirements of customers, an aluminum plate needs to be added between the two pieces of coated glass. Generally, both sides of the aluminum plate are coated with butyl glue, and then Paste the two pieces of coated glass separately, which will make the installation position inaccurate, easy to shift, and cause scratches to the film surface. At the same time, such a large area of ​​glue is also a waste of resources. Invention content: [0003] The purpose of the present invention is to overcome the above disadvantages and provide a method for processing insulating glass lined with aluminum plates that is accurate in installation position, does not cause scratches to the membrane surface, and saves reso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C27/00
Inventor 赵恕波王贤荣陈靖
Owner 江苏蓝星新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com