Fill type stirring friction plug repair welding method and welding tool thereof

A welding tool and repair welding technology, which is applied in the field of repairing welding seam defects and keyholes of friction stir welding, can solve problems such as poor mechanical properties and reduced strength of welded joints, achieve small deformation of workpieces, ensure one-time forming and welding. The effect of low residual stress in the joint

Inactive Publication Date: 2011-06-15
HARBIN INST OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of weld defects and weld keyholes in friction stir welding, which are repaired by fusion welding or friction plug welding, resulting in reduced strength and poor mechanical properties of welded joints, and provides a welding tool and The method of using this welding tool to realize the repair welding of filled friction stir plug

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fill type stirring friction plug repair welding method and welding tool thereof
  • Fill type stirring friction plug repair welding method and welding tool thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0008] Specific embodiment one: this embodiment is realized through the following steps: one, the selection of the material of the stirring pin: the material of the stirring pin is the same as the material of the parts to be repaired; Make a positioning hole at the welding seam defect or the keyhole of the welding seam, and use a type drill to expand the positioning hole into a tapered hole according to the repair welding requirements, which is the preset hole for repairing the defect to be repaired; 3. Determine the size of the stirring needle: Stir The outer contour size of the needle should be larger than the inner contour size of the tapered defect repair preset hole to ensure that the stirring needle and the defect repair preset hole have sufficient friction and sufficient filling volume; 4. Positioning: positioning the defect repair preset hole , so that the defect repair preset hole coincides with the axis of the stirring pin; 5. Repair welding: the moving length of the ...

specific Embodiment approach 2

[0009] Specific implementation mode two: combination figure 1 Describe this embodiment, this embodiment includes a welding tool holding body 1 and a stirring body 2, the welding tool holding body 1 is composed of a coaxial upper cylinder 1-1 and a lower cylinder 1-2, the upper cylinder The diameter of 1-1 is smaller than the diameter of the lower cylinder 1-2, the upper cylinder 1-1 and the lower cylinder 1-2 are integrated, and the outer surface of the upper cylinder 1-1 is provided with a welding tool clamping surface 1 -1-1, at least one annular heat insulation groove 1-2-1 is provided on the outer surface of the lower cylinder 1-2, and a clamp for placing the stirring body 2 is provided at the center of the lower end of the lower cylinder 1-2 Holding hole 1-2-2, the side wall of the holding hole 1-2-2 of the lower cylinder 1-2 is provided with a threaded through hole 1-2-3 perpendicular to the axis of the lower cylinder 1-2, the stirring body 2. It consists of a stirring ...

specific Embodiment approach 3

[0010] Specific implementation mode three: combination figure 1 To illustrate this embodiment, the lower end surface of the lower cylinder 1-2 in this embodiment is a concave shoulder surface 1-2-4 whose outer edge is higher than the center. The concave shoulder surface 1-2-4 effectively prevents the plasticized material from the stirring needle 2-1 from flowing out. Other components and connections are the same as those in the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a welding tool and a method for implementing fill type stirring friction plug repair welding by using the welding tool, and relates to a welding tool for a stirring friction welding and a method thereof, which overcomes strength reduction of the welding joints caused by repair welding by using fusion welding or friction plug welding when welding line defects and keyholes exist in the stirring friction welding. The welding tool is characterized in that the side wall of a clamping hole of a lower cylinder is provided with a thread through hole; a stirring body consists of the stirring pin and a stirring pin seat which are combined into a whole from top to bottom; the outer surface of the stirring pin seat is provided with a stirring pin clamping surface; the stirring pin is a cone; the stirring body is arranged in the clamping hole on the lower cylinder; the stirring pin clamping surface aligns to the thread through hole; and the stirring pin is exposed at the outside of the lower end surface of the lower cylinder. The method comprises the following steps: (1) the material of a stirring pin is same as that of the part which repairs welding; (2) a conical preset hole is opened; (3) the size of the stirring pin is determined; (4) positioning is carried out; and (5) welding of the stirring friction plug is repaired. The invention is used for repair welding of the welding defects and keyholes of stirring friction welding.

Description

technical field [0001] The invention relates to a friction stir welding welding tool and a method thereof, which are used for repair welding of friction stir welding seam defects and keyholes. Background technique [0002] Since the British Welding Institute (TWI) invented the friction stir welding method in 1991, this technology can eliminate welding defects such as pores, inclusions, cracks, etc. And it does not produce arc light, smoke, noise pollution, etc., and at the same time can significantly reduce costs, save materials, optimize structures, and reduce the structural weight of aircraft, etc., which have attracted the attention of scientific research institutions in various countries. Because this technology has many remarkable features that other methods do not have, it will soon be used in the aerospace field, and this method is selected for the welding of the longitudinal seam of the core tank section of the new generation of launch vehicles. Although the frictio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K20/12B23K20/24
Inventor 黄永宪冯吉才吕世雄刘会杰田英韩冰吴建飞范煊赫石俊秒
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com