Dry preparation process of fibre reinforced composite tetrahedral lattice batten board
A composite material and fiber-reinforced technology, which is applied in the field of dry preparation technology of fiber-reinforced composite tetrahedral lattice sandwich panels, can solve the problems of no dry method preparation process of fiber-reinforced composite tetrahedral lattice sandwich panels , to achieve the effect of high specific stiffness and high specific strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment approach 1
[0014] Specific implementation mode one: as Figure 1~2 As shown, the dry preparation process steps of the fiber-reinforced composite tetrahedral lattice sandwich panel in this embodiment are as follows:
[0015] Step 1, mold treatment: clean the surface of the mold with acetone solution, and then treat the outer surface of the mold with a release agent;
[0016] Step 2. Fix the mold: Fix the mold with a fixture;
[0017] Step 3, laying dry fiber cloth: lay 1 to 20 layers of dry fiber cloth on the upper and lower surfaces of the mold, and keep the same number of layers of dry fiber cloth laid on the upper and lower surfaces of the mold;
[0018] Step 4, wear long fiber bundles: between the three through holes formed by the second circular through holes 1-2-1 corresponding to the first circular through holes 1-1-1 of the dry fiber cloth mould. Sew the long fiber bundle back and forth until the three through holes can no longer pass through the long fiber bundle until the dry ...
specific Embodiment approach 2
[0024] Specific embodiment two: 3-18 layers of dry fiber cloth are laid on the upper and lower surfaces of the mold in step three of this embodiment. With such settings, fiber reinforced composite lattice sandwich panels of different thicknesses can be produced according to different needs of products. Others are the same as in the first embodiment.
specific Embodiment approach 3
[0025] Specific embodiment three: 5-15 layers of dry fiber cloth are laid on the upper and lower surfaces of the mold in step three of this embodiment. With such settings, fiber reinforced composite lattice sandwich panels of different thicknesses can be produced according to different needs of products. Others are the same as in the second embodiment.
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap