Method for preparing candle

A technology for candles and recipes, which is applied to candle preparation devices, etc., can solve the problems of low production efficiency and high energy consumption, and achieve the effects of high production efficiency, low energy consumption, and wide adaptability

Inactive Publication Date: 2010-07-07
QINGDAO KINGKING APPL CHEM CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing method for making candles needs to be heated to a relatively high temperature, and needs to be kept for a long time, so the energy consumption is high and the production efficiency is relatively low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of candle preparation method, carries out as follows:

[0015] A. Pretreatment raw materials: mix 94% of the total mass of paraffin, 2% of polyethylene polymer AC-400, 1% of pigment, and 3% of essence, then heat up to 60°C to soften and keep softening State for 1.5 hours; B. Press the softened raw material into a mold with a temperature of 35°C at a pressure of 5 MPa, and the demoulding time is 1 hour, and the product is obtained after cooling and molding.

[0016] The mass percent of each component is: additive, 2-3 percent; pigment, 0.2-1 percent; flavor, 2-3 percent; saturated hydrocarbon mixture, balance.

Embodiment 2

[0018] A kind of candle preparation method, carries out as follows:

[0019] A. Pretreatment raw materials: mix 94.5% of the total mass of paraffin, 3% of polyethylene polymer AC-400, 0.5% of pigment, and 2% of essence, then heat up to 70°C to soften and keep softening State for 1.5 hours; B. Press the softened raw material into a mold at a temperature of 25°C with a pressure of 5 MPa, and the demoulding time is 1 hour, and the product is obtained after cooling and molding.

Embodiment 3

[0021] A kind of candle preparation method, carries out as follows:

[0022] A. Pretreatment raw materials: mix 94.8% of the total mass of paraffin, 2.5% of polyethylene polymer AC-400, 0.2% of pigment, and 2.5% of essence, then heat up to 65°C to soften and keep softening State for 1.5 hours; B. Press the softened raw material into a mold with a temperature of 30°C at a pressure of 5 MPa, and the demoulding time is 1 hour, and the product is obtained after cooling and molding.

[0023] Each of the above-mentioned embodiments is to apply the method of the present invention and adopt the method of cold processing and pressing to produce candle products with unique appearance. Using the method to make candles has the characteristics of low energy consumption, high production efficiency and wide adaptability.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a candle, which comprises the following steps: mixing a saturated hydrocarbon mixture, additives, pigment and essence according to the formula, and heating to 60-70 DEG C to soften the raw materials for 1.5 hours; pressing the softened raw materials into a mold of 25-35 DEG C by applying a pressure of 5 MPa, demolding after 0.5-1 hour, and cooling to form, thereby obtaining the product. The candle comprises the following components in percentage by mass: 2-3% of additive, 0.2-1% of pigment, 2-3% of essence and balance of saturated hydrocarbon mixture. The candle has the characteristics of low energy consumption, high production efficiency and wide adaptability.

Description

technical field [0001] The invention relates to a preparation method of a candle, which belongs to the field of fine chemicals. Background technique [0002] There are many types of candles, and the methods of making them vary widely. The main raw material for making candles is paraffin, and the auxiliary materials added include white oil, stearic acid, polyethylene, essence, pigment, etc. The specific auxiliary materials to be added depend on the type of candle produced. The traditional way of making candles is to use the thermoplastic principle of candle raw materials to melt and cast at high temperature. Crystalline materials usually have a sharp melting point, while amorphous materials generally do not have a true melting point, because there is no specific temperature for a sudden phase transition, but gradually softens and melts within a certain temperature range. Candle raw materials have a wide melting range, and within a certain temperature range, the wax is in a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11C5/02
Inventor 陈索斌
Owner QINGDAO KINGKING APPL CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com