Quake-proof construction steel with yield strength of 100MPa and production method thereof

A yield strength and production method technology, applied in temperature control, rolling mill control device, metal rolling, etc., can solve the problems of high production alloying cost, complex chemical composition, etc., and achieve high toughness, simple process and stable performance. Effect

Inactive Publication Date: 2010-07-14
武钢集团有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the performance of the steel is adjusted by adding a large amount of alloying elements, its chemical composition is complex, and the production cost of alloying is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Below in conjunction with specific embodiment, the anti-seismic building steel of yield strength 100MPa grade of the present invention and production method thereof are described in further detail:

[0024] Table 1 has listed the chemical composition weight percentages of anti-seismic construction steels in Examples 1 to 5 of the present invention (the balance is Fe and unavoidable impurities), and the chemical composition weight percentages of commercially available common construction steels (the remainder is Fe and unavoidable impurities). The amount is Fe and unavoidable impurities).

[0025] Table 1:

[0026]

[0027]

[0028]The steel products in the above-mentioned Examples 1-5 are produced according to the usual ultra-clean steel process, through hot metal desulfurization, converter top-bottom blowing, adding Mg alloy during vacuum treatment for alloying, continuous casting, hot rolling, and cooling to room temperature. During hot rolling, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses quake-proof construction steel with the yield strength of 100MPa and a production method thereof. The steel comprises the following chemical components in percentage by weight: less than or equal to 0.002 percent of C, less than or equal to 0.01 percent of Si, less than or equal to 0.10 percent of Mn, less than or equal to 0.010 percent of P, less than or equal to 0.005 percent of S, 0.002 to 0.007 percent of Mg, 0.020 to 0.070 percent of Ti, 0.010 to 0.020 percent of Nb, 0.001 to 0.003 percent of N, less than or equal to 0.050 percent of Al, and the balance of Fe and inevitable impurities. The production method thereof comprises the steps of desulfuration of molten iron, converter blowing, vacuum treatment, continuous casting, hot rolling, cooling and the like. When the yield strength of steel products exceeds 120Mpa, an annealing treatment step is added after the cooling step. Experiments prove that the quake-proof construction steel with the yield strength of 100MPa has the characteristics of low yield strength, high elongation and excellent impact toughness; and the production method of the steel has the advantages of simple process flow and low production cost.

Description

technical field [0001] The invention relates to building steel, in particular to an anti-seismic building steel with a yield strength of 100 MPa and a production method thereof. Background technique [0002] With the development of steel structure construction, especially the rapid increase of high-rise and super high-rise steel structure buildings, improving the seismic performance of steel structures has become one of the necessary measures to ensure building safety. In the seismic design of steel structure buildings, the energy generated by the earthquake can be absorbed through the plastic deformation of the steel structure, which requires the steel to have better plastic deformation capacity, lower yield strength and good elongation. The domestic and foreign construction circles have begun to consider incorporating the seismic performance of construction steel into building codes. [0003] Before the present invention, there were few patent reports on low-yield-strengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14B21B37/74B21B37/16C21D1/26C21D1/84
Inventor 张开广卜勇童明伟陈晓陈先猛董汉雄习天辉郭斌董中波芮晓龙刘文斌梅荣利
Owner 武钢集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products