Aluminum alloy material and manufacturing method for dual-zero aluminium foils

A technology of aluminum alloy materials and manufacturing methods, which is applied in the field of manufacturing aluminum alloy materials and double-zero aluminum foils, can solve problems such as low production efficiency and yield, poor rolling performance, and low alloy content, so as to improve production efficiency and finished products High efficiency, good rolling stability and high surface quality

Inactive Publication Date: 2010-08-11
JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
View PDF3 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of 1235 alloy to produce double-zero foil has the advantages of good surface quality and fewer pinholes in the aluminum foil, but due to the low alloy content and soft strength, it leads to poor rolling performance, resulting in problems such as low production efficiency a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The composition and weight percentage of the embodiment of the material of the present invention are: Si 0.30%, Fe 0.80%, Cu0.10%, Mn 0.05%, Mg 0.05%, Cr 0.05%, Zn 0.10%, Ti 0.05%, Al balance . The total amount of impurities in the ingredients is not allowed to exceed 0.15% of the total mass, and a single impurity element is not allowed to exceed 0.05% of the total mass.

[0013] Embodiments of the method of the present invention go through the following steps successively:

[0014] a. Smelting, smelting the ingredients in the above proportions, the smelting must be degassed, slag removed, fully and evenly stirred; the temperature of the guide furnace is controlled within the range of 750±5°C; the hydrogen content is controlled at 0.15ml / 100g Al Below, three-stage filtering is used to ensure the quality of the melt.

[0015] b. Casting and rolling, using the rotary blowing method for online degassing, filtering using 30PPi+50PPi double-stage filtration, the modifier m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to an aluminum alloy material and manufacture technology of aluminum foils, in particular to an aluminum alloy material and a manufacturing method for dual-zero aluminium foils. The aluminum alloy material comprises the following components in percentage by weight: 0.2 to 0.35 percent of Si, 0.70 to 0.90 percent of Fe, 0.10 percent of Cu, 0.05 percent of Mn, 0.05 percent of Mg, 0.05 percent of Cr, 0.10 percent of Zn, 0.05 percent of Ti, and the balance of Al; and the components are smelted into an alloy. The manufacturing method orderly comprises the following steps: smelting the components into the alloy; carrying out casting and rolling on the alloy; carrying out cold rolling, intermediate annealing and second cold rolling on the rolled alloy; carrying out aluminum foil rolling; and carrying out final annealing on the finished product. The dual-zero aluminium foil product prepared from the materials by the method integrates the respective advantages of an alloy 1235 and an alloy 8011, has a few pinhole, high surface quality and good rolling stability, and can effectively improve the production efficiency and finished product ratio. The finished product quality and the rolling performance can be comparable with those of the hot-rolled aluminum-foil sheet.

Description

technical field [0001] The invention belongs to the manufacturing technology of aluminum alloy material and aluminum foil, and relates to a manufacturing method of aluminum alloy material and double-zero aluminum foil. Background technique [0002] At present, the aluminum alloys used in the market to produce double zero foils with a thickness of less than 0.01mm are generally 1235 and 8011 alloys. The use of 1235 alloy to produce double-zero foil has the advantages of good surface quality and fewer pinholes in the aluminum foil, but due to the low alloy content and soft strength, it leads to poor rolling performance, resulting in problems such as low production efficiency and yield; while using 8011 When the alloy is used to produce double-zero foil, although the strength is high and the rolling stability is good, due to the characteristics of the alloy itself, the number of pinholes often exceeds the standard, which affects the use of aluminum foil. Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/00C22F1/04
Inventor 董则防张安乐
Owner JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap