Dual-direction high-elastic warp-knitted fabric and production method thereof

A technology of warp knitted fabric and production method, applied in warp knitting, knitting, textile and papermaking, etc., can solve the problems of increased load, increased resistance, discomfort, etc., and achieves the effects of convenient operation and simple manufacturing method

Inactive Publication Date: 2010-08-18
TORAY FIBER RES INST(CHINA) CO LTD
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But another disadvantage is that it is moisture permeable and not waterproof. If you wear a swimsuit made of this kind of fabric underwater, the water flow will definitely soak the whole swimsuit and increase the load. In addition, the water flow will fill between the swimsuit and the body, increasing the resistance of advancement; As outdoor sports clothing, rock climbing clothing must be able to adapt to the harsh weather conditions outside
According to various data, there are few professional rock climbing clothes on the market, so they wear ordinary sportswear. Ordinary sportswear may be sloppy in terms of comfort, but as outdoor sports, people-body-environment interact with each other. In order to avoid harsh Many woven fabrics have also made corresponding countermeasures against the invasion of the climate, coating the surface of the fabric, but the effect is that although it is windproof and waterproof, it is impervious to moisture. In this case, it makes people feel uncomfortable. People's health is also very bad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Warp the polyurethane yarn of 40D and the cationic modified polyester filament of 40D / 12f respectively, wherein the draft ratio of the polyurethane yarn is 180%, and then weave it on a warp knitting machine to obtain gray fabric of elastic fabric. The structural organization of the fabric is warp velvet weave, in which the polyurethane yarn is placed on the rear bar to weave the warp weave; the cationic modified polyester filament is placed on the front bar to weave the warp plain weave.

[0026] Warp knitting machine 32 needles / 2.54cm Tricot machine

[0027] Structural organization Front bar 1-0 / 1-2 / /

[0028] Back bar 2-3 / 1-0 / /

[0029] Let-off amount Front bar 1050mmR

[0030] Rear comb 533mmR

[0031] Polyurethane content 22%

[0032] Vertical density on machine 64c / in

[0033] The elastic fabric gray fabric obtained under the weaving conditions is subjected to scouring at 95°C, intermediate setting at 185°C, and then dyed at 110°C with ca...

Embodiment 2

[0036] Warp the polyurethane yarn of 40D and the cationic modified polyester filament of 40D / 12f respectively, wherein the draft ratio of the polyurethane yarn is 200%, and then weave it on a warp knitting machine to obtain gray fabric of elastic fabric. The structural organization of the fabric is warp velvet weave, in which the polyurethane yarn is placed on the rear bar, weaving heavy warp plain weave; the cationic modified polyester filament is placed on the front bar, weaving heavy warp plain weave.

[0037] Warp knitting machine 32 needles / 2.54cm Tricot machine

[0038] Structural organization Front bar 1-2 / 1-0 / /

[0039] Back bar 2-0 / 1-3 / /

[0040] Let-off amount Front bar 1000mm / R

[0041] Rear bar 600mm / R

[0042] Polyurethane content 23%

[0043] Longitudinal density on machine 70c / in

[0044] Post-processing finishing is the same as embodiment 1.

[0045] The obtained fabric is suitable for making close-fitting sportswear such as swimwear a...

Embodiment 3

[0047] Warp the polyurethane yarn of 40D and the cationic modified polyester filament of 40D / 12f respectively, wherein the draft ratio of the polyurethane yarn is 200%, and then weave it on a warp knitting machine to obtain gray fabric of elastic fabric. The structural organization of the fabric is a three-bar warp-knitted weave, in which the polyurethane yarn is placed on the rear bar to weave the warp weave; the cationic modified polyester filament is placed on the front and middle bars to weave the warp and flat weave.

[0048] Warp knitting machine 32 needles / 2.54cm Tricot machine

[0049] Structural organization Front bar 1-0 / 2-3 / /

[0050] Middle comb 1-2 / 1-0 / /

[0051] Back bar 1-0 / 2-3 / /

[0052] Let-off amount Front bar 1480mm / R

[0053] Middle bar 1110mm / R

[0054] Rear bar 780mm / R

[0055] Polyurethane content 15%

[0056] Vertical density on machine 64c / in

[0057] Post-processing finishing is the same as embodiment 1. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a dual-direction high-elastic warp-knitted fabric and a production method thereof. The dual-direction high-elastic warp-knitted fabric is formed by interweaving polyurethane yarns and other non-elastic yarns, and when in weaving, guide bar for guiding the coiling of the polyurethane yarns transversely moves for 2 to 4 stitch lengths and is opposite to the moving direction of other guide bar yarn inlays. The dual-direction high-elastic warp-knitted fabric has balanced elasticity proportion in the longitudinal and the transverse directions and has excellent elasticity recoverability. Swimsuits made of the warp-knitted fabric have strong guide effect and excellent hydrophobic effect. Moreover, the dual-direction high-elastic warp-knitted fabric has low running water resistance and is particularly suitable for producing close-fitted sportswear with high elasticity requirements such as swimsuit, rock climbing clothing, exercise clothing and the like.

Description

technical field [0001] The invention relates to a two-way high elastic warp knitted fabric and a production method thereof. Background technique [0002] Elastic fabrics (knitted fabrics) that are stretchable both longitudinally and transversely are called two-way elastic fabrics (knitted fabrics). Two-way stretch warp knitted fabrics are warp knitted fabrics that contain elastic yarns. The leading two-way elastic warp knitted fabrics on the market are generally interwoven with elastic yarns and non-elastic yarns, but the elastic yarns are mostly formed into loops with a transverse movement of 1 gauge. Although this type of elastic knitted fabric also has two-way elasticity, there is a large difference between the longitudinal elasticity and the transverse elasticity, and often the longitudinal elastic elongation remains, and the transverse elastic elongation is too small, resulting in uneven distribution of longitudinal and transverse elastic ratios, which restricts the la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04B21/00D04B21/04D06M15/19D06M15/01D06M101/30
Inventor 葛乃梅施一娇张晴
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com