Silicone foam and production method thereof

A technology of silicone foam and production method, applied in the field of fireproof materials, can solve problems such as inconvenient maintenance of easily damaged surrounding walls, pipes and cables, inability to compensate for mechanical displacement, etc., and achieve the effect of good fireproof performance and easy maintenance.

Active Publication Date: 2010-09-29
JIANGSU XIN AN NEW MATERIALS TECH
View PDF7 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Organic fireproof blockages are prohibited to be used in some occasions with strict environmental requirements because they contain toxic volatiles; although inorganic fireproof cement is non-toxic, it will solidify into hard blocks after the sealing is completed, without stretching and compression elasticity, and cannot be used Compensate for the mechanical displacement caused by the vibration of mechanical pipelines and the settlement of buildings, and the maintenance and replacement of wall-penetrating objects such as pipes and cables needs to be knocked out by gravity, which is very easy to damage the surrounding walls, and the maintenance of pipes and cables is very inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Silicone foam, composed of A component and B component, A component and B component are mixed in a ratio of 1:1;

[0050] Component A is composed of base material M and hydrogen-containing polysiloxane, and the weight percentage of each component in component A is:

[0051] Base M 75%

[0052] Hydrogen polysiloxane 25%;

[0053] The base material M is a combination of hydroxyl-terminated polysiloxane, vinyl-terminated polysiloxane and alkyl-terminated polysiloxane, and the weight percentage of each component in the base material M is:

[0054] Hydroxy-terminated polysiloxane 15%

[0055] Vinyl terminated polysiloxane 50%

[0056] Alkyl-terminated polysiloxane 35%;

[0057] B component is made up of base material N and platinum group metal catalyst, and the weight percentage of each component in B component is:

[0058] Base N 99.8%

[0059] Platinum group metal catalyst 0.2%;

[0060]Platinum group metal catalyst is the catalyst of rhodium, ruthenium, palladium, ...

Embodiment 2

[0074] Silicone foam, composed of A component and B component, A component and B component are mixed in a ratio of 1:1;

[0075] Component A is composed of base material M and hydrogen-containing polysiloxane, and the weight percentage of each component in component A is:

[0076] Base M 97%

[0077] Hydrogen polysiloxane 3%;

[0078] The base material M is a combination of hydroxyl-terminated polysiloxane, vinyl-terminated polysiloxane and alkyl-terminated polysiloxane, and the weight percentage of each component in the base material M is:

[0079] Hydroxy-terminated polysiloxane 55%

[0080] Vinyl terminated polysiloxane 40%

[0081] Alkyl terminated polysiloxane 5%

[0082] B component is made up of base material N and platinum group metal catalyst, and the weight percentage of each component in B component is:

[0083] Base N 99.99%

[0084] Platinum group metal catalyst 0.01%;

[0085] Platinum group metal catalyst is the catalyst of rhodium, ruthenium, palladium, ...

Embodiment 3

[0104] Silicone foam, composed of A component and B component, A component and B component are mixed in a ratio of 1:1;

[0105] Component A is composed of base material M and hydrogen-containing polysiloxane, and the weight percentage of each component in component A is:

[0106] Base M 90%

[0107] Hydrogen polysiloxane 10%;

[0108] The base material M is a combination of hydroxyl-terminated polysiloxane, vinyl-terminated polysiloxane and alkyl-terminated polysiloxane, and the weight percentage of each component in the base material M is:

[0109] Hydroxy-terminated polysiloxane 45%

[0110] Vinyl terminated polysiloxane 10%

[0111] Alkyl terminated polysiloxane 45%

[0112] B component is made up of base material N and platinum group metal catalyst, and the weight percentage of each component in B component is:

[0113] Base N 99.9%

[0114] Platinum group metal catalyst 0.1%;

[0115] Platinum group metal catalyst is the catalyst of rhodium, ruthenium, palladium, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a silicone foam and a production method thereof, belonging to the field of fireproofing materials. The silicone foam comprises hydrogenpolysiloxane, monohydric polysiloxane, vinylpolysiloxane, alkylpolysiloxane and platinum group metal catalysts, and a reinforced filler, flame retardant components, a black paint and a yellow paint can be added to prepare a dual-component silicone foam glue material. When in use, the materials are mixed in a proportion of 1:1 on site, and foamed and vulcanized on site at a normal temperature to form a high-density elastic fireproof foam. The silicone foam does not contain toxic or harmful components, and has fireproof performance, ray penetration protection, tensibility and pressure elasticity. The silicone foam can compensate displacement caused by vibration of mechanical pipelines and subsidence of a building, and is favorable to fire proof blockage for pipeline maintenance or cable maintenance.

Description

technical field [0001] The invention belongs to the field of fireproof materials, and relates to a fireproof foam glue, in particular to a silicone foam and a production method thereof. Background technique [0002] Most of the existing fireproofing blockages use organic fireproofing materials and inorganic fireproofing cement. Organic fireproof blockages are prohibited to be used in some occasions with strict environmental requirements because they contain toxic volatiles; although inorganic fireproof cement is non-toxic, it will solidify into hard blocks after the sealing is completed, without stretching and compression elasticity, and cannot be used Compensate for the mechanical displacement caused by the vibration of mechanical pipelines and the settlement of buildings, and the maintenance and replacement of wall-penetrating objects such as pipes and cables needs to be knocked out by gravity, which is very easy to damage the surrounding walls, and the maintenance of pipe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/06C08L83/07C08L83/04C08L83/05C08J9/02
Inventor 王旭莹
Owner JIANGSU XIN AN NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More