Pure fluff pulp cigarette filter rod and preparation method thereof

A fluff pulp and filter rod technology, which is applied in e-liquid filter, tobacco, application, etc., can solve the problem of inability to effectively deal with the loss of hair and powder from filter paper, difficult to control the suction resistance of filter rods, and inhalable substances that cannot meet the requirements for use, etc. problem, to achieve the effect of reducing tar content, reducing harm, and strong filtration and adsorption capacity

Inactive Publication Date: 2011-01-05
谢义斌 +1
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

ZL200510024998.X announced the dry-laid paper cigarette filter rod and its preparation method. Because it cannot effectively deal with the problem of filter paper hair loss and powder loss, the inhalables cannot meet the use requirements. The suction resistance of the tip stick is difficult to control. Based on this, the same inventor revised the patent and applied for "Air-laid Cigarette Filter Stick and Its Preparation Method" (Application No. 200610024267.X). The improved technology uses Man-made fibers and / or man-made fibers, which are not accepted by the tobacco industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The pure fluff pulp cigarette filter rod has a filter core composed of 60% fluff pulp and 40% cured latex.

[0018] The preparation method of pure fluff pulp cigarette filter rod comprises the following steps: (1) the fluff pulp is opened and humidified, then air-laid to form fluff pulp paper, and then hot-pressed at 90°C and 3kN / m; (2) The latex with a solid content of 10% is sprayed on the front side of the fluff pulp paper, and dried at 130°C after completion; (3) Continue to spray the reverse side of the fluff pulp paper with latex with a solid content of 10%, and dry at 135°C after completion, and then solidify The final latex is covered on the front and back sides of the fluff pulp paper; (4) into a roll, cut into a disc with a width of 120mm; (5) Unwind the disc, and when unrolling, carry out the process at intervals of 2 mm along the length of the fluff pulp paper. Indentation, the indentation is along the length of the filter rod, at an angle of 0° with the cen...

Embodiment 2

[0020] The pure fluff pulp cigarette filter rod has a filter core composed of 90% by mass of fluff pulp and 10% of cured starch glue.

[0021] The preparation method of pure fluff pulp cigarette filter rod comprises the following steps: (1) the fluff pulp is opened and humidified, then air-laid to form fluff pulp paper, and then hot-pressed at 140°C and 0.1kN / m; (2) Starch glue with a solid content of 15% is used for sizing the front surface of the fluff pulp paper, and dried at 200°C after completion; (3) continue to use starch glue with a solid content of 15% for sizing the reverse surface of the fluff pulp paper, and after completion, 220°C Drying, at this time, the cured starch glue covers the front and back of the fluff pulp paper; (4) rolls, cut into discs with a width of 140mm; (5) unroll the discs, along the length of the fluff pulp The indentation is carried out at intervals of 5mm in the length direction of the paper, and the indentation is along the length direction...

Embodiment 3

[0023] The pure fluff pulp cigarette filter rod has a filter core composed of 80% fluff pulp and 20% cured latex.

[0024] The preparation method of pure fluff pulp cigarette filter rod comprises the following steps: (1) after the fluff pulp is opened and humidified, air-laid to form fluff pulp paper, and then hot-pressed at 120°C and 2kN / m; The latex with a solid content of 20% is sprayed on the front side of the fluff pulp paper, and dried at 170°C after completion; (3) continue to spray the reverse side of the fluff pulp paper with latex with a solid content of 20%, and after completion, it is dried at 180°C and solidified at this time The final latex is covered on the front and back sides of the fluff pulp paper; (4) into a roll, cut into a disc with a width of 90mm; (5) unwind the disc, and when unrolling, proceed along the length of the fluff pulp paper at an interval of 8mm. Indentation, the indentation is along the length of the filter rod, at an angle of 45° with the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of cigarette filter rods, and specifically relates to a pure fluff pulp cigarette filter rod and a preparation method thereof. A filter element of the pure fluff pulp cigarette filter rod consists of 60 to 90 mass percent of fluff pulp and 10 to 40 mass percent of cured binding agent. The pure fluff pulp cigarette filter rod is prepared by adopting pure fluff pulp as a raw material, has strong filtering and absorptive capacity, can reduce the tar content very well to reduce harms caused by cigarettes to a human body; besides, the pure fluff pulp cigarette filter rod can be degraded naturally after being used and cannot cause harms to the environment.

Description

technical field [0001] The invention belongs to the technical field of cigarette filter rods, and in particular relates to a pure fluff pulp cigarette filter rod and a preparation method thereof. Background technique [0002] Fibrous tow filter rods, paper rods, nonwoven rods and composite rods are known in the industry. The raw material preparation equipment and process of fiber tow filter rod are complicated, the material cost is high and pollutes the environment during use, it is difficult to degrade naturally, and the filtration and adsorption performance is not good. The paper stick is severely deformed or even fiber disintegrated after being damp or absorbing moisture, so it cannot directly touch the mouth. Due to the addition of chemical fibers or artificial fibers to the filter material, non-woven rods have poor adsorption and filtration performance, and are not easy to degrade in the natural environment. Tar reduction and harm reduction in the tobacco industry hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A24D3/06A24D3/02
Inventor 贾英智谢义斌
Owner 谢义斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap