Zinc alloy large-plane die casting dressing technology

A die-casting and large-plane technology, applied in the field of zinc alloy large-plane die-casting shaping technology, can solve the problems of not meeting the requirements of quality and production efficiency, low production efficiency, product surface damage, etc., to meet product quality and production High requirements for efficiency, high production efficiency and good stability

Active Publication Date: 2012-10-03
DONGGUAN XINGHE PRECISION DIECASTING MOLD CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to its own structure, zinc alloy die castings contain a large amount of internal stress that needs to be released, so it is common to deform after the mold is released. The traditional leveling and shaping methods are all processed by hand, that is, gently knocked flat with a rubber hammer, so that The product releases stress slowly. This operation method is easy to cause damage to the product surface, and the production efficiency is not high, and the rework phenomenon is more serious. It often becomes the bottleneck process that restricts the mass production of products, and cannot meet the requirements of modern production for product quality and production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] The present invention is a zinc alloy large-plane die-casting shaping process, said process comprising the following steps:

[0015] ①Use the jig composed of the upper splint and the lower splint to lock and shape the die-casting, so that the die-casting is in a state of elastic deformation and the flatness reaches 10 microns. The lower surface of the upper splint and the upper surface of the lower splint are equipped with The evacuation position matching the protruding bone position of the die-casting part;

[0016] ②Put the above-mentioned jig into the oven and heat up to 150°C. After baking for 60 minutes, the die-casting part 3 undergoes plastic deformation, releases the stress, and the flatness meets the requirements;

[0017] ③Open the oven door, take out the die-casting parts, and let the die-casting parts cool down to room temperature naturally. During the cooling process, fans can be used to assist in cooling to reduce the cooling time;

[0018] ④ Loosen the j...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a zinc alloy large-plane die casting dressing technology. The technology comprises the following steps: utilizing a jig consisting of an upper clamping plate and a lower clamping plate to lock and shape a die casting, thus the die casting is in an elastic deformation state and the flatness of the die casting is up to 10-15 microns; placing the jig in an oven, and heating so that the die casting is subjected to elastic deformation, the stress is relieved, the demand on the flatness can be met; opening the door of the oven, taking out the die casting, and cooling the diecasting naturally to the room temperature; and loosening the jig, and taking out the die casting for the next working procedure. The technology provided by the invention is simple in operation, and has the advantages of good stability, high production efficiency, great market value and huge market potential, no need of plentiful manpower and material resources and no damage to surface of the product; the stress of the product can be eliminated automatically, the product stability is good, the product can not deform again; and large-plane die castings can be effectively shaped, and the high demands of modern production on the product quality and the production efficiency can be met.

Description

technical field [0001] The invention relates to the technical field of die-casting processing technology, in particular to a zinc alloy large-plane die-casting shaping process. Background technique [0002] The deformation of an object is divided into elastic deformation and plastic deformation. Among them, elastic deformation can be recovered, while plastic deformation cannot be recovered. The expected result of die casting in the mold industry is plastic deformation, that is, the product is shaped after it is flattened. [0003] Due to its own structure, zinc alloy die castings contain a large amount of internal stress that needs to be released, so it is common to deform after the mold is released. The traditional leveling and shaping methods are all processed by hand, that is, gently knocked flat with a rubber hammer, so that The product releases stress slowly. This operation method is easy to cause damage to the product surface, and the production efficiency is not high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/16
Inventor 唐金元
Owner DONGGUAN XINGHE PRECISION DIECASTING MOLD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products