Antibacterial, moisture-absorbent and warming knitted fabric and manufacturing method thereof

A knitted fabric, moisture absorption and warmth retention technology, applied in knitting, weft knitting, textiles and papermaking, etc., can solve the problems of difficult discharge of sweat, only sweat absorption without antibacterial and antibacterial safety performance, reduced wearing performance, etc. Warm and washable effect

Inactive Publication Date: 2013-07-10
SHANGHAI JIALE
View PDF6 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the knitted fabrics at this stage only absorb sweat without antibacterial properties or have antibacterial properties but poor antibacterial safety performance (because ordinary products are achieved by a layer of chemical artificial additives attached to the fiber surface)
[0003] Cellulose fibers such as cotton and viscose have good hygroscopicity and warmth retention properties, but after absorbing moisture, cellulose fibers evaporate slowly, making it uncomfortable to wear after the human body sweats
Although the conventional synthetic fiber has better quick-drying performance, it has poor hygroscopicity, which makes it difficult to discharge sweat when wearing, and greatly reduces the wearing performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial, moisture-absorbent and warming knitted fabric and manufacturing method thereof
  • Antibacterial, moisture-absorbent and warming knitted fabric and manufacturing method thereof
  • Antibacterial, moisture-absorbent and warming knitted fabric and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Selection of raw materials:

[0023] Outer material: 32sJC (combed cotton) / CLEANCOOL 65 / 35 polyester-cotton blended yarn

[0024] That is: CLEANCOOL antibacterial, moisture-absorbing and quick-drying polyester fiber 65%, combed cotton 35%

[0025] Middle connecting part material: 100D / 72F DTY (Y-section polyester filament) stretched textured yarn

[0026] Inner layer material: 100D / 72F DTY CLEANCOOL nano-silver antibacterial moisture absorption quick-drying stretch textured wire

[0027] 2. Weaving process:

[0028] Use Meyer-4-1 1.6QC type double-sided machine, machine number 26#, 24G gauge, cylinder diameter 34", knitting needles according to figure 1 Arrangement of knitting needles shown in the diagram, the triangles are as follows figure 2 The triangular pareto shown is arranged according to image 3 Weaving according to the weaving diagram, the weaving process is as follows:

[0029] Rib to needle, one row of upper needles and four rows of lower needles ...

Embodiment 2

[0036] 1. Selection of raw materials:

[0037] Outer material: 21sJC (combed cotton) / CLEANCOOL 75 / 25 polyester-cotton blended yarn

[0038] That is: CLEANCOOL antibacterial, moisture-absorbing and quick-drying polyester fiber 75%, combed cotton 25%

[0039] Middle connection part 100D / 144F FDY (Y-section polyester filament) fully drawn yarn

[0040] Inner layer material: 75D / 72F DTY CLEANCOOL nano-silver antibacterial, moisture-absorbing and quick-drying stretch textured silk

[0041] 2. Weaving process:

[0042] Use Meyer-4-1 1.6QC type double-sided machine, machine number 26#, 24G gauge, cylinder diameter 34", knitting needles according to figure 1 Arranged as shown, the triangles are arranged as figure 2 Arranged as shown, press image 3 Weaving according to the weaving diagram, the weaving process is as follows:

[0043] Rib to needle, one row of upper needles and four rows of lower needles 1234; the knitting process is eight-way and one cycle, of which the yarn us...

Embodiment 3

[0049] 1. Selection of raw materials:

[0050] Outer material: 32sJC / CLEANCOOL 80 / 20 polyester-cotton blended yarn

[0051]That is: CLEANCOOL antibacterial, moisture-absorbing and quick-drying polyester fiber 80%, combed cotton 20%

[0052] Middle connection part 75D / 72F DTY (Y-section polyester filament)

[0053] Inner layer material: 50D / 96F DTY CLEANCOOL nano-silver antibacterial, moisture-absorbing and quick-drying stretch textured wire

[0054] 2. Weaving process:

[0055] Use Meyer-4-1 1.6QC type double-sided machine, machine number 26#, 24G gauge, cylinder diameter 34", knitting needles according to figure 1 Arranged as shown, the triangles are arranged as figure 2 Arranged as shown, press image 3 Compile the diagram for weaving, the weaving process is as follows:

[0056] Rib stitching, one row of upper needles and four rows of lower needles 1234; the knitting process is eight-way and one cycle, of which the yarn used for the outer layer is 32sJC / CLEANCOOL 80 / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antibacterial, moisture-absorbent and warming knitted fabric and a manufacturing method thereof. The antibacterial, moisture-absorbent and warming knitted fabric has a double-layer structure, wherein an outer layer of the fabric has a mesh structure woven from blended yarns which are blended from cellulosic fibers and nanosilver antibacterial agent-containing profiled polyester fibers; an inner layer of the fabric has a plain structure woven from the nanosilver antibacterial agent-containing profiled polyester fibers; and the inner layer and the outer layer are connected through polyester filaments with grooved sections. The manufacturing method comprises the following steps: for the outer layer of the fabric, manufacturing the mesh structure woven from the blended yarns which are blended from the cellulosic fibers and the nanosilver antibacterial agent-containing profiled polyester fibers; for the inner layer of the fabric, manufacturing the plain structure woven from the nanosilver antibacterial agent-containing profiled polyester fibers; and connecting the inner layer and the outer layer through the polyester filaments with the grooved sections. The antibacterial, moisture-absorbent and warming knitted fabric can meet requirements on moisture absorption for quick drying as well as wearing comfort, can meet an increasingly strong requirement on antibacterial sanitation and has a good warming effect.

Description

technical field [0001] The invention belongs to the technical field of knitting, and relates to an antibacterial, moisture-absorbing and warm-keeping knitted fabric and a processing method thereof. Background technique [0002] With the continuous improvement of people's living standards, people not only have higher requirements for the appearance and comfort of clothes, but also have higher requirements for antibacterial and hygienic properties of clothes. However, most of the knitted fabrics at this stage are only sweat-absorbing and not antibacterial, or have antibacterial properties but poor antibacterial safety performance (because ordinary products are achieved by a layer of chemical artificial additives attached to the fiber surface). [0003] Cellulose fibers such as cotton and viscose have good hygroscopicity and warmth retention properties, but after absorbing moisture, cellulose fibers evaporate slowly, making it uncomfortable to wear after the human body sweats. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/00D04B1/14D04B1/16
Inventor 詹永宝陈建峰杨建国杜方东党高峰宋志平顾成塞高庆锋高华林
Owner SHANGHAI JIALE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap