Method for preparing colored fabric containing polylactic acid fiber and silk components

A technology of polylactic acid fiber and manufacturing method, which is applied in textiles and papermaking, weft knitting, knitting, etc., can solve the problems of low strength, low modulus, poor moisture permeability, etc., and achieve cost reduction and good skin-friendliness , the effect of great market prospects

Inactive Publication Date: 2013-07-10
HENAN LONGDU BIOLOGY TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at the same time, there are also disadvantages such as low strength, poor moisture permeability, low modulus, unsuitable care and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A method for manufacturing a colored fabric containing polylactic acid fibers and silk components, comprising the following process steps:

[0012] (a) Preparation of polylactic acid fiber skein: two 75D / 36F polylactic acid fiber draft yarns are used as raw materials, and the first polylactic acid fiber draft yarn has 400 twists / m after being processed by a two-for-one twister, and the Z twist direction , set by hot and humid steam at 90°C for 30 minutes; the second polylactic acid fiber is processed by a two-for-one twister with 400 twists / m, Z twist direction, and set by hot and humid steam at 90°C for 30 minutes; the two fibers after setting Plying, with 400 twists / m after being processed by a two-for-one twister, S twist direction, and set by hot and humid steam at 90°C for 30 minutes. Rewind to obtain skein.

[0013] (b) Polylactic acid fiber skein dyeing: Dyeing with Runtu brand SR74# disperse red dye, adjusting the pH value of the dyeing solution to 5-6 with ace...

Embodiment 2

[0016] A method for manufacturing a colored fabric containing polylactic acid fibers and silk components, comprising the following process steps:

[0017] (a) Preparation of polylactic acid fiber skein: two 75D / 48F polylactic acid fiber draft yarns are used as raw materials, and the first polylactic acid fiber draft yarn has 400 twists / m after being processed by a two-for-one twister, and the S twist direction , set by hot and humid steam at 90°C for 30 minutes; the second polylactic acid fiber is processed by a two-for-one twister with 400 twists / m, Z twist direction, and set by hot and humid steam at 90°C for 30 minutes; the two fibers after setting Plying, after processing by a two-for-one twisting machine, it has 400 twists / m, Z twisting direction, and is made into a plying yarn with a mesh stainless steel bobbin, and is set at 100°C for 30 minutes by hot and humid steam.

[0018] (b) Dyeing of polylactic acid fiber skein: use disperse dye (disperse yellow 8GFF) to dye the...

Embodiment 3

[0021] A method for manufacturing a colored fabric containing polylactic acid fibers and silk components, comprising the following process steps:

[0022] (a) Preparation of polylactic acid fiber bobbins: two 75D / 36F polylactic acid fiber draft yarns were used as raw materials to prepare polylactic acid fiber bobbins. The first polylactic acid fiber drawn yarn has 400 twists / m after being processed by a two-for-one twisting machine, S twist direction, and is set at 90°C for 30 minutes by humid steam; the second polylactic acid fiber is processed by a two-for-one twisting machine and has 400 twists / m, Z-twisting direction, shaped by hot and humid steam at 90°C for 30 minutes; the two fibers after the setting are plyed, and processed by a two-for-one twister with 400 twists / m, Z-twisting direction, and stainless steel bobbins with meshes will be used The plied yarn was boiled in atmospheric boiling water for 15 minutes.

[0023] (b) Polylactic acid fiber yarn dyeing: Dyeing wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a colored fabric containing polylactic acid fiber and silk components, which comprises the following steps of: dyeing polylactic acid fibers and silk fibers respectively, and weaving into the colored fabric. By the method, the respective advantages of the polylactic acid fibers and silk are fully exerted, high skin affinity is achieved, the cost of areal silk fabric can be reduced, and the prepared fabric has a wide market prospect.

Description

technical field [0001] The invention relates to a method for manufacturing colored fabrics containing polylactic acid fibers and silk components, belonging to the field of textiles. Background technique [0002] Polylactic acid fiber is a completely degradable green ecological fiber, which can be processed from starch-rich corn, cassava and other plants through fermentation, synthesis and spinning. Polylactic acid fiber has high strength, good skin affinity, antibacterial and flame retardant, good anti-ultraviolet performance, smooth and breathable, has a luster similar to real silk, and the price is only one-fifth of real silk. Moreover, the modulus of polylactic acid fiber is relatively high. The three Chinese patent applications whose publication numbers are CN101082153A, CN1010821154A and CN1651645A respectively disclose three dyeing processes of fabrics (fabrics) made of polylactic acid fibers, but when polylactic acid fibers are used as some fabric components, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/12
Inventor 兰平汪蔚吴文吕佳
Owner HENAN LONGDU BIOLOGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com