Composite blending material of slag powder and use method

A technology of composite admixture and slag powder, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., to achieve high activity excitation, increase hydration temperature, and increase the speed of hydration reaction

Inactive Publication Date: 2011-09-07
蒋元海
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the cementitious materials used in the production of cement concrete products are Portland cement or ordinary Portland cement or composite Portland cement with a strength grade above 32.5. Invention patents ZL 95116762.6, ZL 03112836.X, ZL 03113366.5, In ZL 03113256.1, it is proposed to add one or two kinds of materials such as ground construction sand, ground slag, ground steel slag, and ground high silica sand to compound and make concrete admixtures after grinding. application, but the three components of slag powder, quicklime and calcined gypsum are prepared in a certain proportion and ground to a certain fineness to develop a slag powder composite admixture, and replace part of the silicon with a certain proportion and equivalent amount under steam curing conditions There is no report on the technology of producing cement concrete products with salt cement or ordinary Portland cement or composite Portland cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1. The three components of slag, quicklime and calcined gypsum are prepared as 90%: 2.5%: 7.5% by mass percentage, wherein the CaO content of quicklime is 91%; the three-component materials are mixed and ground to specific surface area 430m 2 / kg, SO in slag powder composite admixture 3 5.0%; the addition amount of the grinding aid triisopropanolamine during grinding is 0.06‰ of the total weight of the three-component materials. The slag powder composite admixture is used to replace 30% of the ordinary Portland cement with a strength grade of 42.5 to produce concrete drainage pipes. After the concrete is stirred and fed, the centrifugal molding operation is carried out, and then it is stopped for 1.5 hours, and atmospheric pressure steam is used to produce concrete drainage pipes. Curing process, the constant temperature of atmospheric steam curing is 90°C, and the total curing time is 6 hours; demoulding operation is carried out after atmospheric steam curi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite blending material of slag power and a use method. Slag, quick lime and calcined gypsum are mixed according to a certain proportion, and then, are finely ground into the composite blending material with specific surface area of 400m<2> / kg to 600m<2> / kg. When the composite blending material is used for producing cement concrete products with a steam curing process, the composite blending material can replace 10-40% of cement with the strength grade above 32.5 in an equal quantity manner; and by using the composite blending material, the production cost of the cement concrete products is lowered, resources are saved, and favorable economic benefits and social benefits are achieved.

Description

technical field [0001] The invention relates to a method for making and using a concrete admixture. Background technique [0002] In the prior art, the cementitious materials used in the production of cement concrete products are Portland cement or ordinary Portland cement or composite Portland cement with a strength grade above 32.5. Invention patents ZL 95116762.6, ZL 03112836.X, ZL 03113366.5, In ZL 03113256.1, it is proposed to add one or two kinds of materials such as ground construction sand, ground slag, ground steel slag, and ground high silica sand to compound and make concrete admixtures after grinding. application, but the three components of slag powder, quicklime and calcined gypsum are prepared in a certain proportion and ground to a certain fineness to develop a slag powder composite admixture, and replace part of the silicon with a certain proportion and equivalent amount under steam curing conditions There is no report on the technology of producing cement ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/14C04B28/04
CPCC04B40/0039Y02W30/91C04B18/141C04B22/064C04B22/143C04B28/02C04B2103/52
Inventor 蒋元海
Owner 蒋元海
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap