Thermosetting moisture-resistant welding seam sealant

A sealant and thermal hardening technology, which is applied in the field of weld sealants, can solve the problems of insufficient waterproof and moisture resistance, waste of labor and material resources, and unsatisfactory waterproof and moisture resistance functions.

Inactive Publication Date: 2011-09-14
张家港爱科思汽车配件有限公司
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The original weld sealant PVC resin is used as the main component, and contains fillers, plasticizers, tackifiers, hygroscopic agents, and stabilizers. During the high humidity season, the moisture in the atmosphere will slowly penetrate into the applied weld seal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting moisture-resistant welding seam sealant
  • Thermosetting moisture-resistant welding seam sealant
  • Thermosetting moisture-resistant welding seam sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The following is a detailed description based on Examples and Comparative Examples.

[0015] Table 1 is a comparison table of each component composition of the embodiment and comparative examples 1 and 2.

[0016]

[0017]

[0018] Table I

[0019] Table 2 is the moisture-resistant time test. Comparative examples 1, 2 and the examples are made of test pieces by the same smearing method, and then stored in 1, 2 storage chains. After being placed for 7 days, Comparative Examples 1, 2 and Examples were stored for different days in each storage chain to evaluate the appearance of bubbles after heating and hardening.

[0020]

[0021] Table II

[0022] According to the results in Table 2, it can be seen that under high temperature and high humidity conditions, comparative examples 1 and 2 will have poor appearance quality after being placed in the 1 storage chain for 24 hours, and after being placed in the 2 storage chain for 48 hours, while the examples are place...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a thermosetting moisture-resistant welding seam sealant. The sealant comprises the following components by weight percent: 20-35wt% of PVC (polyvinyl chloride) resin, 20-35wt% of filler, 25-35wt% of plasticizer, 1-15wt% of tackifier, 5-10wt% of hygroscopic agent and 1-5wt% of stabilizer, wherein, the hygroscopic agent is composed of 2.5-5wt% of uncoated calcium oxide and 2.5-5wt% of coated calcium oxide. The thermosetting moisture-resistant welding seam sealant has the advantages of good waterproof and moisture-resistant effect and long-acting water and moisture resistance so as to prevent rework of the product due to poor appearance quality caused by moisture absorption, thus improving production efficiency and lowering production cost.

Description

technical field [0001] The invention relates to a weld seam sealant, in particular to a heat-hardening and moisture-resistant weld seam sealant acting between the joints of the inner panel and the outer panel of the automobile. Background technique [0002] Generally speaking, the joints of the inner and outer plates of most automobile steel plates are coated with weld sealant to play the role of waterproof, anti-rust, and noise reduction. The weld sealant is applied before paint spraying, and then primed → The hardening reaction is completed after the middle coat → top coat is baked in the oven. [0003] The original weld sealant PVC resin is used as the main component, and contains fillers, plasticizers, tackifiers, hygroscopic agents, and stabilizers. During the high humidity season, the moisture in the atmosphere will slowly penetrate into the applied weld sealant, and then after baking, bubbles will appear in the welded part, resulting in poor appearance quality of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K13/06C08K9/10C08K3/22C09K3/10C09J127/06C09J11/04
Inventor 裴仁哲朴一西张世俊
Owner 张家港爱科思汽车配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap