Dry-process desulphurized fly ash dry-mixed mortar

A dry-process desulfurization ash and dry-mixed mortar technology, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of small desulfurization ash consumption, limited contribution to environmental protection and energy saving, and achieve an easy-to-achieve effect

Active Publication Date: 2011-11-23
山东丞华企业投资控股有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the amount of desulfurization ash in the mortar is very small, and the contribution to waste application, environmental protection and energy saving is very limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dry-process desulphurized fly ash dry-mixed mortar
  • Dry-process desulphurized fly ash dry-mixed mortar
  • Dry-process desulphurized fly ash dry-mixed mortar

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0023] Preparation Example 1 (interior wall plastering dry-mixed mortar):

[0024] formula:

[0025] Ordinary silicon cement 425#: 9Kg Dry desulfurization ash: 15Kg

[0026] Machine-made sand: 76Kg (fineness less than 4mm) Composite activator: 0.25Kg

[0027] Composite water retaining agent: 0.07Kg Composite anti-cracking agent: 0.2Kg

[0028] The composite activator is compounded by alum and aluminum sulfate with a weight ratio of 1:1;

[0029] The composite water retaining agent is compounded by hydroxypropyl methylcellulose and carboxymethyl cellulose with a weight ratio of 4:3;

[0030] The composite anti-cracking agent is compounded by perlite (40 mesh) and sodium dodecylbenzenesulfonate with a weight ratio of 3:1.

[0031] Preparation:

[0032] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

Embodiment 2

[0033] Embodiment 2 (external wall plastering dry-mixed mortar):

[0034] Ordinary silicon cement 425#: 9Kg Dry desulfurization ash: 15Kg

[0035] Machine-made sand: 76Kg (fineness less than 4mm) Composite activator: 0.25Kg

[0036] Composite water retaining agent: 0.085Kg Composite anti-cracking agent: 0.2Kg

[0037] Sodium stearate: 0.1Kg

[0038] The composite activator is compounded by alum and aluminum sulfate with a weight ratio of 1:1;

[0039] The composite water retaining agent is compounded by hydroxypropyl methylcellulose and carboxymethyl cellulose with a weight ratio of 4:3;

[0040] The composite anti-cracking agent is compounded by perlite (40 mesh) and sodium dodecylbenzenesulfonate with a weight ratio of 3:1.

[0041] Preparation:

[0042] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

Embodiment 3

[0043] Embodiment three (interior wall plastering dry-mixed mortar):

[0044] formula:

[0045] Ordinary silicon cement 425#: 10Kg Dry desulfurization ash: 18Kg

[0046] Construction waste crushed particles: 72Kg (fineness less than 4mm) Composite activator: 0.3Kg

[0047] Composite water retaining agent: 0.07Kg Composite anti-cracking agent: 0.25Kg

[0048] The composite activator is compounded by alum and aluminum sulfate with a weight ratio of 1:1;

[0049] The composite water retaining agent is compounded by hydroxypropyl methylcellulose and carboxymethyl cellulose with a weight ratio of 4:3;

[0050] The composite anti-cracking agent is compounded from perlite (50 mesh) and sodium dodecylbenzenesulfonate with a weight ratio of 3:1.

[0051] Preparation:

[0052] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses dry-process desulphurized fly ash dry-mixed mortar, which belongs to the field of pre-agitated dry-mixed mortar materials for buildings. The mortar is formed by mixing the following materials in a ratio by weight: 8-12 parts of cement, 15-20 parts of dry-process desulphurized fly ash, 68-77 parts of aggregate, 0.25-0.4 part of composite excitant, 0.07-0.1 part of compositewater retaining agent, 0.2-0.3 part of composite anti-cracking agent and 0-0.3 part of water repellent agent. Compared with the prior art, the dry-process desulphurized fly ash dry-mixed mortar adopts extremely fine ash formed by a dry-process desulfurizing technology as a main material and has the characteristics of energy saving, environment friendliness, low material cost and the like.

Description

technical field [0001] The invention relates to a ready-mixed dry-mixed mortar material for construction, in particular to a dry-process desulfurized ash dry-mixed mortar. Background technique [0002] At present, there are three main types of gas desulfurization processes for coal-fired boilers in my country: wet desulfurization process, semi-dry desulfurization process, and dry desulfurization process. Baosteel alone produces 170,000 tons of desulfurization ash every year. In the existing technology, there are some relatively mature utilization methods for calcium sulfate dihydrate produced by wet desulfurization process, but there is basically no mature utilization method for desulfurization ash. . [0003] On the other hand, with the development of society, people's requirements for project quality, environmental protection requirements and civilized construction are constantly improving, and the advantages of dry-mixed mortar are favored by more and more people. How t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B18/10
CPCC04B28/04Y02W30/91C04B14/02C04B14/18C04B18/062C04B20/0076C04B22/148C04B24/20C04B40/0608C04B2103/46C04B2103/65C04B24/26C04B24/383C04B2103/58C04B2103/0057
Inventor 王爱民王庆珍赵兵赵同习张培清张萍
Owner 山东丞华企业投资控股有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com