[0039] Example 1: A relatively pure molten steel is obtained by smelting, and then continuously casted into a slab through a continuous casting machine. The weight percentage of the composition is: C: 0.045%, Si: ≤0.023%, Mn: 0.21%, P: ≤0.015 %, S: ≤0.004%, Als: 0.02%.
[0040] Heat the cast slab to 1190°C and keep it for 30 minutes, then turn on the high pressure water for descaling, and the pressure is 19Mpa; the cast slab after descaling is subjected to 3+3 rough rolling, the rough rolling opening temperature is 1170°C, and the final rolling temperature It is 1020℃ to ensure that the secondary descaling water pressure is not less than 18Mpa; after the rough rolling mill, the heat preservation cover is fully opened, the temperature setting of the finishing rolling inlet is 990℃, and the cooling water between the stands is opened for 3-4 groups. The temperature setting value of the finish rolling exit is 880℃, the thickness range is 4.5-3.5mm, and the finish rolling exit speed i...
Example Embodiment
[0041] Example 2: A relatively pure molten steel is obtained by smelting, and then continuously cast into a slab through a continuous casting machine. The weight percentages of the components are: C: 0.033%, Si: 0.015%, Mn: 0.22%, P: ≤0.0104% , S: ≤0.0156%, Als: 0.0189%.
[0042] Heat the cast slab to 1180℃ for 40 minutes, then turn on the descaling high-pressure water at a pressure of 20bar; the cast slab after descaling is subjected to 3+3 rough rolling, the roughing opening temperature is 1170℃, and the final rolling temperature It is 1010℃ to ensure that the secondary descaling water pressure is not less than 19Mpa; after the rough rolling mill, the heat preservation cover is fully opened, the temperature setting of the finishing rolling inlet is 990℃, and the cooling water between the stands is opened for 3-4 groups. The temperature setting value of the finishing rolling exit is 874℃, the temperature setting value of the finishing rolling exit is 880℃, and the thickness rang...
Example Embodiment
[0043] Example 3: A relatively pure molten steel is obtained by smelting, which is then continuously cast into a slab by a continuous casting machine. The weight percentages of the components are: C: 0.032%, Si: ≤ 0.011%, Mn: 0.177%, P: 0.0087%, S: 0.010%, Als: 0.0209%.
[0044] Heat the cast slab to 1200°C for 20 minutes, then turn on the descaling high-pressure water at a pressure of 20 Mpa; the cast slab after descaling is subjected to 3+5 rough rolling, the rough rolling opening temperature is 1180°C, and the final rolling The temperature is 1020℃, to ensure that the secondary descaling water pressure is not less than 20Mpa; after the rough rolling mill, the heat preservation cover is fully opened, the temperature setting of the finishing rolling entrance is 1100℃, and the cooling water between the stands is opened for 3-4 groups. The temperature setting of the finishing rolling exit is 890℃, the thickness range is 3.0-2.5 mm, and the finishing exit speed is increased by 9% c...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap