一种聚碳酸酯、熔融酯交换的技术，应用在支化芳香族聚碳酸酯领域，能够解决没有提及支化点与氧杂蒽酮结构比例等问题

Inactive Publication Date: 2011-12-14
COVESTRO DEUTSCHLAND AG
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Other patents describing branching points in MeltPC using THPE as branching agent are: JP-04-089824, JP-04-175368, JP-06-298925 and EP1472302A1, but do not mention branching in the polymer chain Ratio of dots to xanthone structures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Branched molten polycarbonate with low defect structure
  • Branched molten polycarbonate with low defect structure
  • Branched molten polycarbonate with low defect structure

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0083] Examples of catalysts suitable for the preparation of polycarbonates according to the invention are those compounds represented by the general formula (VII):

[0084]

[0085] in:

[0086] R 9 , R 10 , R 11 and R 12 denote the same or different C independently of each other 1 -C 18 Alkylene moiety, C 6 -C 10 aryl moiety, or C 5 -C 6 a cycloalkyl moiety, and

[0087] x - Represents an anion, where the corresponding acid-base pair H + +X - → pK of HX b Values ​​less than 11.

[0088] The preferred catalyst is tetraphenyl Fluoride, tetraphenyl tetraphenyl-borate and tetraphenyl phenoxide. Most preferably tetraphenyl phenoxide. An example of a preferred content of salt catalyst is 10 -2 to 10 -8 mol per mol of diphenol, and the most preferred content of catalyst is 10 -4 to 10 -6 mol per mol of diphenol.

[0089] Polycarbonate can be prepared in steps, the temperature can be controlled step by step in the range of 150 to 400 °C, the residenc...

Embodiment

[0197] Characterization of the Molding Compositions According to the Invention (Test Methods)

[0198] Melt viscosity

[0199] Rheological properties by measuring the melt viscosity of the molding composition according to the invention in [Pa s] at 320°C as a function of the shear gradient (η) varying from 100 to 1000 [1 / s] To measure. The measurement is done with a capillary rheometer according to ISO11443.

[0200] Determination of relative viscosity ( n rel.)：

[0201] The relative solution viscosity ηrel. is determined in dichloromethane (0.5 g polycarbonate / l) at 25° C. in an Ubbelohde viscometer.

[0202] Average molecular weight (Mw)

[0203] The average molecular weight Mw is determined from a 0.2% strength solution of the polymer in dichloromethane by gel permeation chromatography (GPC) and UV detection. GPC is calibrated by linear PC standards.

[0204] Melt volume flow rate (MVR)

[0205] The melt volume flow rate (MVR) is measured according to ISO...

Embodiment 23

[0244] Compounding materials comprising phosphines or phosphites and if appropriate sterically hindered phenols (Examples 12, 22-24) are significantly more stable during heat aging than Example 11 containing no additives, as can be seen from ΔYI 1000h worth seeing. Unexpectedly, Example 23, which contained an aromatic phosphite, was more effective than Example 23, which contained a combination of phosphine and n-octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate. 24 is superior in yellowing. This characteristic could not have been foreseen according to the German published application DE 10 2009 043509.3, which was not published at the filing date of the present application. Said unpublished publication at the filing date of the present application describes THPE-free MeltPCs in which phosphine is combined with n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propane The combination of esters provides the best anti-yellowing effect during heat aging and is superior to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to view more

Abstract

Aromatic branched polycarbonate prepared by transesterifying bisphenols with diaryl carbonates in melt transesterification process using branching agents, is new. The ratio of internal branching agent and sum of xanthen-9-one derivative (I) in melt polycarbonate is 8-200. The content of (I) is 5-450 mg / kg. Aromatic branched polycarbonate prepared by transesterifying bisphenols with diaryl carbonates in melt transesterification process using branching agents, is new. The ratio of internal branching agent and sum of xanthen-9-one derivative of formula (I) in melt polycarbonate is 8-200. The content of (I) is 5-450 mg / kg. X : 1-6C alkylene, 2-5C alkylidine, 5-6C cycloalkylidene (all substituted by 1-6C alkyl, preferably CH 3or ethyl) or single bond. An independent claim is also included for a composition comprising at least one above mentioned polycarbonate and at least one organophosphorus compound comprising phosphines, phosphites, diphosphites or phosphates. [Image]

Description

[0001] related application [0002] This application claims the benefit of European Patent Application No. 10159245.9 filed April 7, 2010, which is hereby incorporated by reference in its entirety for all useful purposes. technical field [0003] The present invention relates to branched aromatic polycarbonates having defined polymer chain branching points and the ratio of defect structures in the polymer chain to each other, and also to a process for the preparation of these branched aromatic polycarbonates. The present invention relates in particular to branched aromatic polycarbonates which, since their preparation is by transesterification of bisphenols with diaryl carbonates in the melt, contain not only target polymer chains Branching points, such as polymer chain branching points obtained by trifunctional branching agent molecules, also contain defect structures present in the polymer chain as undesired by-products. These defect structures can adversely affect the rheo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G64/04C08G64/38C08G64/30C08L69/00C08K5/50C08K5/524C08K5/521
CPCC08K5/50C08K5/49C08L69/00C08G64/307C08K5/13C08G64/14C08G64/04C08K5/5397
Inventor S·康拉德H-W·霍伊尔K-H·克勒C·明尼希R·韦尔曼
Owner COVESTRO DEUTSCHLAND AG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap