Cleaning agent for stainless steel cold-rolling piece and preparation method thereof

A stainless steel and cleaning agent technology, applied in the field of chemical cleaning, can solve problems such as difficult cleaning, air pollution, human hazards, etc., achieve good cleaning effect, maintain gloss, and save costs

Active Publication Date: 2012-04-04
响水巨合金属制品有限公司
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the cleaning of stainless steel cold-rolled parts is difficult to control. In order to remove the sintered matter and dirt inside and outside the tube, the traditional method is to use nitric acid and hydrofluoric acid for heating. The smaller the tube, the more difficult it is to clean.
Strong acid is highly corrosive to the surface of stainless steel cold-rolled parts. Often the outside of the tube has been clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cleaning agent for stainless steel cold-rolling piece and preparation method thereof
  • Cleaning agent for stainless steel cold-rolling piece and preparation method thereof
  • Cleaning agent for stainless steel cold-rolling piece and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method of a cleaning agent for stainless steel cold-rolled parts, which has the following steps: (1), at normal temperature, add 658 kilograms of water in a mixer; (2), add 70 kilograms of citric acid with a content of 99.3% while stirring; (3) ), adding 110 kilograms of content 99.6% oxalic acid while stirring; (4), adding 2 kilograms of content 99% sodium molybdate while stirring; (5), adding 50 kilograms of content 85% triethanolamine while stirring; (6), (7), throw in 10 kilograms of emulsifier OP-10 while stirring; (8), throw in 10 kilograms of 31% hydrochloric acid while stirring; (9), throw in while stirring 10 kilograms of hydrofluoric acid with a content of 90%; (10), stirring for 20-30 minutes after all the feeding is finished is the finished product.

Embodiment 2

[0029] A preparation method of a cleaning agent for stainless steel cold-rolled parts has the following steps: (1), at normal temperature, add 563 kilograms of water in a mixer; (2), add 90 kilograms of citric acid with a content of 99.3% while stirring; (3) ), adding 140 kilograms of content 99.6% oxalic acid while stirring; (4), adding 2 kilograms of content 99% sodium molybdate while stirring; (5), adding 60 kilograms of content 85% triethanolamine while stirring; (6), (7), throw in 13 kilograms of emulsifier OP-10 while stirring; (8), throw in 17 kilograms of content 31% hydrochloric acid while stirring; (9), throw in while stirring 15 kilograms of hydrofluoric acid with a content of 90%; (10), stirring for 20-30 minutes after all the feeding is finished.

Embodiment 3

[0031] A preparation method of a cleaning agent for stainless steel cold-rolled parts has the following steps: (1), at normal temperature, add 449 kilograms of water in the mixer; (2), add 130 kilograms of citric acid with a content of 99.3% while stirring; (3) ), stirring while putting in 170 kilograms of content 99.6% oxalic acid; (4), stirring while putting in 3 kilograms of content 99% sodium molybdate; (5), stirring while putting in 80 kilograms of content 85% triethanolamine; (6), Throw in 120 kilograms of JFC penetrating agents while stirring; (7), throw in 17 kilograms of emulsifier OP-10 while stirring; (8), throw in 13 kilograms of content 31% hydrochloric acid while stirring; (9), throw in while stirring 18 kilograms of hydrofluoric acid with a content of 90%; (10), stirring for 20-30 minutes after all the feeding is finished.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of chemical cleaning, in particular to a cleaning agent suitable for a stainless steel cold-rolling piece and a preparation method thereof. The cleaning agent for the stainless steel cold-rolling piece is manufactured at normal temperature by mixing the following raw materials by weight percentage: 31.6 percent to 65.8 percent of water, 7 percent to 14 percent of citric acid, 11 percent to 22 percent of oxalic acid, 0.2 percent to 0.4 percent of sodium molybdate, 5 percent to 10 percent of triethanolamine, 8 percent to 16 percent of fatty alcohol-polyoxyethylene ether, 1 percent to 2 percent of alkylphenol ethoxylates, 1 percent to 2 percent of hydrochloric acid and the balance of hydrofluoric acid. The chemical cleaning and the preparation method have the advantages that the operation is simple, the cleaning effect is good, the surface of the stainless steel cold-rolling piece cannot be corroded at the same time, and the glossiness of the stainless steel cold-rolling piece is maintained; the cleaning agent for the stainless steel cold-rolling piece can be repeatedly used and cannot harm skin when being contacted with the skin; and as not containing zinc or nitrogen, the cleaning agent is low-carbon and environmentally friendly, and the cost is saved.

Description

technical field [0001] The invention relates to the technical field of chemical cleaning, in particular to a cleaning agent suitable for stainless steel cold-rolled pieces and a preparation method thereof. Background technique [0002] At present, the cleaning of stainless steel cold-rolled parts is difficult to control. In order to remove the sintered matter and dirt inside and outside the tube, the traditional method is to use nitric acid and hydrofluoric acid for heating. The smaller the tube, the more difficult it is to clean. Strong acid is highly corrosive to the surface of stainless steel cold-rolled parts. Often the outside of the tube has been cleaned, but the sintered material inside the tube has not fallen off. After a long time, the sintered material in the tube has fallen off, and the outside of the tube has been severely corroded; and due to nitric acid and hydrogen Fluoric acid is heated to produce acid mist, which not only has great harm to the human body, bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/08
Inventor 杨细龙
Owner 响水巨合金属制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap