Preparation method of iron oxide desulfurizer having controllable textural properties

A technology of iron oxide desulfurizer and desulfurizer, which is applied in combustible gas purification, combustible gas purification/transformation, petroleum industry, etc., can solve problems such as failure to realize industrialization, instability of gas desulfurizer, etc., and achieve detailed and accurate values , low cost and short regeneration time

Inactive Publication Date: 2013-06-05
TAIYUAN UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Integrated coal gasification combined cycle power generation technology, referred to as IGCC, is a promising clean coal utilization technology in the 21st century. Among them, high-temperature gas desulfurization is the key to IGCC technology, but the instability of gas desulfurizers makes this technology unrealized so far. industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of iron oxide desulfurizer having controllable textural properties
  • Preparation method of iron oxide desulfurizer having controllable textural properties
  • Preparation method of iron oxide desulfurizer having controllable textural properties

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0073] The present invention will be further described below in conjunction with accompanying drawing:

[0074] figure 1 As shown in the figure, in order to prepare the state diagram of polystyrene microsphere emulsion, the position of each part must be correct, the ratio should be proportioned, and the operations should be performed in sequence.

[0075] Quantities of chemicals used in preparation are determined according to pre-set ranges in grams, milliliters, centimeters 3 is the unit of measurement.

[0076] The preparation of the polystyrene microsphere emulsion is carried out in a four-necked flask, and is completed under heating, stirring, argon protection, and water reflux condensation; a display screen 2, an indicator light 3, Stirring switch 4, temperature controller 5; on the upper part of the electric heating stirrer 1 is an electric heating mantle 6, on the upper part of the electric heating mantle 6 is a four-necked flask 7, and on the upper part of the four-n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of an iron oxide desulfurizer having controllable textural properties. The iron oxide desulfurizer comprises steel-making red mud as a raw material, bentonite as a binder, styrene as a pore forming agent, potassium persulfate as an initiator, sodium bicarbonate and sodium hydroxide as a pH regulating agent, and deionized water as a solvent. The preparation method comprises the following steps: firstly preparing a polystyrene microsphere emulsion as the pore forming agent, then mixing the polystyrene microsphere emulsion with steel-making red mud, bentonite, and calcium stearate, kneading and extruding into strips, drying and carrying out high temperature sintering on the strips to obtain the iron oxide desulfurizer having controllable texturalproperties. The iron oxide desulfurizer having controllable textural properties is brownish red. The use of the steel-making red mud in the method is a recycling of waste, thus the cost is low. The preparation method has the advantages of short process flow, few devices used herein, detailed and accurate data, high product purity, high desulfuration efficiency which can reach 98 %, short regeneration time of the desulfurizer, and good regeneration effect. The preparation method is an ideal method for preparing the desulfurizer through recycling wastes.

Description

technical field [0001] The invention relates to a preparation method of an iron oxide desulfurizer with controllable texture properties, belonging to the technical field of preparation and application of high-temperature gas desulfurizers. Background technique [0002] Integrated coal gasification combined cycle power generation technology, referred to as IGCC, is a promising clean coal utilization technology in the 21st century. Among them, high-temperature gas desulfurization is the key to IGCC technology, but the instability of gas desulfurizers makes this technology unrealized so far. industrialization. [0003] The texture parameters of the gas desulfurizer have a great influence on the performance, and the pore volume of the catalyst directly affects the stability of the catalyst. It is found that when the pores are within a certain range, the desulfurization effect of the desulfurizer will increase with the increase of the specific surface area ; but when the specifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10K1/20
Inventor 林建英樊惠玲上官炬刘生昕宋瑾沈芳梁丽彤苗茂谦任军孙肖
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap