Production process for laminating hot melt adhesive with TPU (thermoplastic urethane)
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production process, hot-melt adhesive technology, applied in the field of hot-melt adhesive production process, can solve the problems of poor flatness, unevenness, beauty, bubbles and wrinkles of the diaphragm
Inactive Publication Date: 2012-05-09
DONGGUAN XIONGLIN NEW MATERIAL TECH
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The existing hot-melt adhesive laminating TPU production process has relatively poor flattening of the diaphragm and is easy to roll, and the bonding su
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0023] Below in conjunction with accompanying drawing, the present invention will be further described:
[0024] A kind of production technique of hot-melt adhesive bonding TPU of the present invention, it comprises the following steps:
[0025] Step A, prepare hot melt adhesive raw material and TPU raw material;
[0026] Step B, if the double-layer co-extrusion extruder is selected, first set the set temperature value of the double-layer co-extrusion extruder during production, the double-layer co-extrusion extruder starts to heat up, when the temperature reaches the set temperature value, the double-layer co-extrusion The screw of the layer co-extrusion extruder starts to work and enters step C; if a single extruder is selected, first set the set temperature value of the single extruder production, and the single extruder starts to heat up, when the temperature reaches the set temperature value Finally, the screw of the single extruder starts to work and enters step D; the ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of a production process of a hot melt adhesive, and in particular relates to a production process for laminating a hot melt adhesive with TPU (thermoplastic urethane). The production process comprises the following modes of: if a double-layer co-extruder is selected for extruding the hot melt adhesive and the TPU at the same time, laminating to form a membrane after the hot melt adhesive is adhered to the TPU, then forming and coiling; if a single extruder is selected for sequentially extruding the hot melt adhesive and the TPU, producing a single-sided misty or transparent hot melt adhesive product by adopting the mode of directly pressing an embossing roller by a rubber roll, then laminating the single-sided misty or transparent hot melt adhesive with the TPU to form a membrane, then forming and coiling; and if a single extruder is selected for sequentially extruding the TPU and the hot melt adhesive, producing a TPU product by adopting the mode of directly pressing an embossing roller by a rubber roll, then laminating the TPU with the hot melt adhesive to form a membrane, then forming and coiling. The membrane produced by the production process has the advantages of better flatness, less possibility of curliness, uniform surface lamination tension and no bubbles and wrinkles, thus the obtained product is more flat and beautiful.
Description
Technical field: [0001] The invention relates to the technical field of hot melt adhesive production technology, in particular to a production technology of hot melt adhesive bonding TPU. Background technique: [0002] Hot-melt adhesive film is a kind of plastic adhesive, which can replace industrial liquid glue, solid glue and PU glue. It has the advantages of environmental protection, non-toxic and no side effects. As an ideal environmentally friendly adhesive material, hot melt adhesive film has low melting point, high elasticity, acid resistance, alkali resistance, washing resistance, dry cleaning resistance, strong tensile strength, strong adhesion, and low melting point. It has been widely used in embroidery labels. , armbands, trademark bonding, suitable for clothing, shoes and hats, bags, medical, military coats, sportswear, toys and other fields. Due to the superior performance of the hot-melt adhesive film, and in line with the general bonding processing standards...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.