Inorganic fiber composite thermal insulation material and preparation method thereof

A composite thermal insulation material and inorganic fiber technology, applied in the direction of thermal insulation, building components, etc., can solve the problems of large thermal insulation materials, inability to adapt to building nodes, large thermal conductivity, etc., to achieve small bulk density, strong fire resistance, and small thermal conductivity Effect

Inactive Publication Date: 2012-07-18
HEJIAN TIANHAO INSULATION MATERIAL
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an inorganic fiber composite thermal insulation material, which solves the problem tha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An inorganic fiber composite thermal insulation material, the thermal insulation material is composed of the following components by weight percentage: 5kg of polyphenylene particles, 30kg of silicon dioxide, 60kg of white carbon black, 30kg of glass wool, and 25kg of aluminum silicate wool.

[0018] The preparation method of the above-mentioned inorganic fiber composite thermal insulation material:

[0019] (1) Get 5kg of polyphenylene particles, 30kg of silicon dioxide, 60kg of white carbon black, 30kg of glass wool, and 25kg of aluminum silicate wool, reversely disperse and stir under the condition of airflow intensity 4atm, and make rubber powder particles;

[0020] (2) Spray the silica sol on the rubber powder particles.

[0021] The inorganic fiber composite thermal insulation material prepared in this example is named TH-200, and the bulk density of the thermal insulation material is 180 kg / m 3 . The thermal conductivity of the thermal insulation material is 0....

Embodiment 2

[0023] An inorganic fiber composite thermal insulation material, the thermal insulation material is composed of the following components by weight percentage: 3kg of polyphenylene particles, 20kg of silicon dioxide, 50kg of white carbon black, 20kg of glass wool, and 15kg of aluminum silicate wool.

[0024] The preparation method of the above-mentioned inorganic fiber composite thermal insulation material:

[0025] (1) Get 3kg of polyphenylene particles, 20kg of silicon dioxide, 50kg of white carbon black, 20kg of glass wool, and 15kg of aluminum silicate cotton, reversely disperse and stir under the condition of airflow intensity 5atm, and make rubber powder particles;

[0026] (2) Spray the silica sol on the rubber powder particles.

[0027] The inorganic fiber composite thermal insulation material prepared in this example is named TH-200, and the bulk density of the thermal insulation material is 190 kg / m 3 . The thermal conductivity of the insulation material is 0.032w.k...

Embodiment 3

[0029] An inorganic fiber composite thermal insulation material, the thermal insulation material is composed of the following components by weight percentage: 8kg of polyphenylene particles, 40kg of silicon dioxide, 70kg of white carbon black, 40kg of glass wool, and 35kg of aluminum silicate wool.

[0030] The preparation method of the above-mentioned inorganic fiber composite thermal insulation material:

[0031] (1) 8kg of polyphenylene particles, 40kg of silicon dioxide, 70kg of white carbon black, 40kg of glass wool, and 35kg of aluminum silicate wool, reversely disperse and stir under the condition of airflow intensity 7atm, and make rubber powder particles;

[0032] (2) Spray the silica sol on the rubber powder particles.

[0033] The inorganic fiber composite thermal insulation material prepared in this example is named TH-200, and the bulk density of the thermal insulation material is 200 kg / m 3 . The thermal conductivity of the thermal insulation material is 0.033w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Wire diameteraaaaaaaaaa
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic fiber composite thermal insulation material and a preparation method thereof, which belong to the technical field of thermal insulation material preparation. The thermal insulation material is formed by dispersing and mixing polyphenyl granules, silica, white carbon black, glass wool and aluminum silicate wool through a strong airflow. The thermal insulation material disclosed by the invention has the advantages of light volume weight and small heat conductivity factor, can adapt to complex building nodes and is suitable for thermal insulation of outer walls of buildings.

Description

technical field [0001] The invention belongs to the technical field of thermal insulation material preparation, and in particular relates to an inorganic fiber composite thermal insulation material and a preparation method thereof. Background technique [0002] At present, cement, aerated concrete, benzene board, glass wool board, phenolic foam insulation board, etc. are widely used in buildings as insulation materials for building interior or exterior walls. The disadvantages of cement and aerated concrete are relatively large bulk density and large thermal conductivity. The benzene board and the glass wool board are prone to cracks due to large drying shrinkage, and have poor adaptability to complex-shaped building joints. Phenolic foam insulation board is easy to release formaldehyde gas when heated. Therefore, there is an urgent need for a new type of thermal insulation material with small bulk density, low thermal conductivity, safety, green and environmental protecti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/24E04B1/76
Inventor 孙德胜
Owner HEJIAN TIANHAO INSULATION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap