Composite heat-insulating material and preparation method thereof

A technology of composite thermal insulation materials and raw materials, which is applied in the field of thermal insulation material manufacturing, can solve the problems of large dry shrinkage, easy cracks, high thermal conductivity, and poor adaptability of glass wool boards, and achieve small bulk density, small thermal conductivity, and strong fire resistance. Effect

Inactive Publication Date: 2017-10-20
合肥易美特建材有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of cement and aerated concrete are relatively large bulk density and large thermal conductivity
Benzene board and glass wool board are easy to crack due to large drying shrinkage, and have poor adaptability to complex-shaped building joints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] One aspect of this embodiment provides a composite thermal insulation material, which includes the following components: 90 parts of modified glass wool, 10 parts of polystyrene particles, 10 parts of white carbon black, 0.5 parts of penetrant, 1.5 parts of aluminum silicate wool, 0.6 parts of binder, and 2.5 parts of activator. The modification method of the modified glass wool is soaking with a modifier for 30-60 minutes and curing. The modifier includes the following parts: Raw materials: 0 parts of sodium silicate solution, 4 parts of barium hydroxide, 10 parts of melamine, 4 parts of propanol, 4 parts of antimony trioxide, 2 parts of chlorinated paraffin, 3 parts of curing agent.

[0024] As a preferred solution, the fineness of the white carbon black is 60-80 mesh.

[0025] As a preferred solution, the penetrating agent includes the following raw materials: 50 parts of fatty alcohol polyoxyethylene ether, 10 parts of emulsifier, 15 parts of turpentine, and 10 part...

Embodiment 2

[0032] One aspect of this embodiment provides a composite thermal insulation material, which includes the following components: 80-90 parts of modified glass wool, 10 parts of polystyrene particles, 10 parts of white carbon black, 0.5 parts of penetrant part, 1.5 parts of aluminum silicate wool, 0.6 part of binder, and 2.5 parts of activator. The modification method of the modified glass wool is soaking with a modifier for 30-60 min and curing. The modifier includes The raw materials are as follows: 30 parts of sodium silicate solution, 20 parts of barium hydroxide, 4 parts of melamine, 5 parts of propanol, 2 parts of antimony trioxide, 5 parts of chlorinated paraffin, and 1 part of curing agent.

[0033] As a preferred solution, the fineness of the white carbon black is 60-80 mesh.

[0034] As a preferred solution, the penetrating agent includes the following raw materials: 20 parts of fatty alcohol polyoxyethylene ether, 25 parts of emulsifier, 5 parts of turpentine, and 65 ...

Embodiment 3

[0041] One aspect of this embodiment provides a composite thermal insulation material, which includes the following components: 90 parts of modified glass wool, 14 parts of polystyrene particles, 10 parts of white carbon black, 0.7 parts of penetrant, 1.5 parts of aluminum silicate wool, 0.8 parts of binder, and 1.5 parts of activator. The modification method of the modified glass wool is soaking with a modifier for 30-50 minutes and curing. The modifier includes the following parts: Raw materials: 60 parts of sodium silicate solution, 11 parts of barium hydroxide, 10 parts of melamine, 3 parts of propanol, 4 parts of antimony trioxide, 2 parts of chlorinated paraffin, and 2 parts of curing agent.

[0042] As a preferred solution, the fineness of the white carbon black is 60-80 mesh.

[0043] As a preferred solution, the penetrating agent includes the following raw materials: 50 parts of fatty alcohol polyoxyethylene ether, 10 parts of emulsifier, 15 parts of turpentine, and 6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of manufacturing of a heat-insulating material, and provides a composite heat-insulating material and a preparation method thereof. The heat-insulating material comprises the following components: 80 to 90 parts of modified glass cotton, 10 to 20 parts of polyphenyl granules, 4 to 10 parts of white carbon black, 0.5 to 1.1 parts of a penetrating agent, 0.3 to 1.5 parts of aluminum silicate wool, 0.6 to 1.9 parts of an adhesive and 0.9 to 2.5 parts of an excitant; the modification method of the modified glass cotton comprises the steps of soaking with a modifier for 30 to 60 minutes and curing; the modifier comprises the following raw materials: 30 to 70 parts of a sodium silicate solution, 4 to 20 parts of barium hydroxide, 4 to 10 parts of melamine, 2 to 5 parts of propyl alcohol, 2 to 4 parts of antimonous oxide, 2 to 5 parts of chlorinated paraffin and 1 to 3 parts of a curing agent. The preparation method of the composite heat-insulating material is simple in process; the cement loving property of the prepared heat-insulating material is improved, the volume weight is small, the heat-conducting coefficient is small, and the fire-resistant capability is high.

Description

technical field [0001] The invention belongs to the technical field of thermal insulation material manufacturing, and in particular relates to a composite thermal insulation material and a preparation method thereof. Background technique [0002] Insulation materials can be divided into three categories: metal insulation materials, organic insulation materials, and inorganic insulation materials. [0003] Metal insulation materials, but the supply of this material is very small and the price is very expensive. As a building insulation material, it will greatly increase the cost and cannot be widely used. [0004] Organic thermal insulation materials are easy to burn, easy to produce toxic gas at high temperature, and have poor aging resistance and fire resistance. These shortcomings limit the wide use of organic thermal insulation materials. [0005] At present, cement, aerated concrete, benzene board, glass wool board, phenolic foam insulation board, etc. are widely used i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/02C04B20/10C04B14/42
CPCC04B18/021C04B20/1066C04B20/1074C04B14/4643C04B16/08C04B14/42C04B14/06C04B14/4656C04B14/38C04B2103/0068C04B24/32C04B24/34C04B20/1022C04B20/1044
Inventor 朱明静
Owner 合肥易美特建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap