Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Low-temperature pulverization inhibitor for sintered ore

A technology of inhibitor and sinter, which is applied in the field of smelting aids in iron and steel plants, can solve the problems of affecting the gas permeability of the upper column of the blast furnace, destroying the forward running of furnace conditions, reducing the utilization rate of gas, etc., so as to improve the gas permeability and utilization rate of gas, The effect of improving the gas passage and securing the heat strength

Inactive Publication Date: 2012-07-25
通化耐博新材料股份有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In severe cases, it will affect the air permeability of the upper material column of the blast furnace, reduce the gas utilization rate, and destroy the furnace condition.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The low-temperature pulverization inhibitor for sinter is made of the following raw materials in mass percentage: carboxymethyl starch 10%, boric acid (99.6%) 62%, silicon micropowder (3000 mesh) 23%, and fast penetrating agent T 5%.

Embodiment 2

[0020] The low-temperature pulverization inhibitor for sinter is made of the following raw materials in mass percentage: carboxymethyl starch 9%, boric acid 59%, silicon micropowder 25%, and fast penetrating agent T 7%.

Embodiment 3

[0022] The low-temperature pulverization inhibitor for sinter is made of the following raw materials in mass percentage: carboxymethyl starch 10%, boric acid 60%, silicon micropowder 25%, and fast penetrating agent T 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a smelting assistant for steel works, namely a low-temperature pulverization inhibitor for sintered ore. The low-temperature pulverization inhibitor is prepared by mixing carboxymethyl starch, boric acid, silicon micropowder and a permeate agent in designated proportion; compared with CaCl, Cl ion drag-in quantity is reduced more than 50%, the low-temperature pulverization inhibitor can not generate a replacement reaction with K and Na alkali metals in a furnace charge, therefore, the problem of continuous and circulating enrichment of KCl (kirchhoff's circuit laws) and NaCl in a blast furnace is solved, the reactivity of coke is restrained, the melting loss reaction is reduced, the heat intensity of the coke is ensured, low temperature reduction pulverization rate of the sintered ore is reduced, the destructive effect of the alkali metal on the coke and the blast furnace is basically solved, the furnace condition is smooth, and the output is increased.

Description

technical field [0001] The invention relates to a smelting auxiliary agent for iron and steel plants, that is, a low-temperature pulverization inhibitor for sintered ore. Background technique [0002] In the prior art, it is well known that blast furnaces require high-grade, low-silicon charge for the charge, so many domestic iron and steel plants have made great efforts to improve the grade of sintered ore and reduce harmful impurities, but low Silicon sintering inevitably leads to an increase in the pulverization rate of low-temperature reduction, which has a negative impact on the blast furnace. [0003] Low-temperature reduction pulverization means that the sintered ore regenerates Fe 2 o 3 upon reduction to Fe 3 o 4 In the process of sintering, the structure of the crystal changes greatly, resulting in great internal stress and volume expansion, which weakens the structure of the sintered ore, causes pulverization, and produces more powder. Due to the large amount ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/16
Inventor 邵建秋魏宇珩马守义高义陈洪伟
Owner 通化耐博新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com