Production method for chemical fiber and polyester composite yarns

A technology of polyester composite yarn and production method, which is applied in stretch spinning, artificial filament heat treatment, textiles and papermaking, etc., and can solve the problems of unstable composite yarn quality and cohesion, increased production cost of composite yarn products, and low production efficiency and other problems, to achieve the effect of good cohesion, reduced equipment footprint, and reliable quality

Inactive Publication Date: 2012-08-01
北京德厚朴化工技术股份有限公司
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the past, the common process of chemical fiber spinning was to spin POY and FDY two kinds of filaments separately in the first step, and then perform paralleling on another machine in the second step. Three different equipments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for chemical fiber and polyester composite yarns
  • Production method for chemical fiber and polyester composite yarns
  • Production method for chemical fiber and polyester composite yarns

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] In order to produce composite yarns of POY and FDY with only one equipment in one step, the polyester pre-oriented yarn POY and polyester fully-drawn yarn FDY to be produced separately are composite-spun on the same winding frame. Silk, the silk road process must be able to meet the process required for the production of these two kinds of silk at the same time, and the two kinds of silk can be mixed to form a composite silk.

[0016] The concrete operation method of producing composite yarn with the present invention can be by adopting the hot roll of different size diameter and unheated small-diameter dividing roll to cooperate, and then the fiber composite yarn processed through different spinning and winding silk paths, concrete operation method as follows:

[0017] Such as figure 1 As shown: FDY yarn 8 first passes through the first pair of drafting rollers (the two drafting rollers are hot rollers 1 and 2), and then passes through a godet roller 3 together with P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production method for chemical fiber and polyester composite yarns, in particular to a method for producing chemical fiber and polyester composite yarns of partially oriented yarns (POY) and fully drawn yarns (FDY) by one kind of equipment through a one-step method. The POY and the FDY are subjected to composite spinning on the same winding frame, and the spinning process can simultaneously meet process flows required by producing the two kinds of yarns; the FDY and the POY enter a draft area from the same side of a first pair of drawing rollers, wherein the FDY pass through the first pair of drawing rollers consisting of a large-diameter heat roller and a large-diameter heat roller, and, together with the POY, pass through a yarn guide roller below the first pair of drawing rollers, and the FDY and the POY are combined and compounded into a bundle of yarns on the yarn guide roller; and the composite yarn bundle passes through a second pair of drawing rollers consisting of a large-diameter heat roller and a non-heating small-diameter separator roller to form the composite yarns. The effects of saving a production space and saving energy are obvious, the processed fiber composite yarns are reliable in quality, stable in process and high in cohesiveness and the dying property is superior to that of the conventional product.

Description

Technical field [0001] The invention relates to a production method of chemical fiber polyester composite yarn, in particular to a production method of chemical fiber polyester composite yarn which can produce POY and FDY composite yarn by adopting one equipment and one-step method. Background technique [0002] Chemical fiber polyester composite yarn is a composite yarn made of polyester pre-oriented yarn (Partially Oriented Yarns, abbreviated as POY) and polyester fully drawn yarn (Fully Drawn Yarn, abbreviated as FDY) produced by one-step spinning method. [0003] The method of POY spinning is usually: after the polyester filament is cooled and oiled, it passes through a pair of godet discs, and then reaches the winding machine to be wound to form a silk cake. The method of FDY spinning is usually: after the polyester filament is cooled and oiled, it first passes through the first pair of drafting rollers, then is drawn by the second pair of drafting rollers, and then rea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G1/18D01D5/16D01D10/02
Inventor 张吉张瑞光
Owner 北京德厚朴化工技术股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap