1750 DEG C high-temperature corundum and mullite push plate formula and preparation process
A technology of mullite and fused mullite, which is applied in the field of 1750°C high-temperature corundum mullite push plate formulation and preparation technology, can solve the problems of different application fields and different components, and achieve good wear resistance, Effects of extended service life and high thermal vibration stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
example 1
[0036] A 1750°C high-temperature corundum mullite push plate formula consists of: 20 parts of fused mullite, 36 parts of fused white corundum, 20 parts of platy corundum, 12 parts of a-Al2O3 micropowder, 8 parts of kaolin, activated 2 parts of agent, 2 parts of binder.
[0037] A process for preparing a 1750°C high temperature corundum mullite push plate is as follows:
[0038] Step 1, carry out blank mixing according to the above composition quality formula;
[0039] Step 2, complete green body forming through mold making;
[0040] Step 3, complete green body shaping;
[0041] Step 4, carry out microwave green body drying;
[0042] Step 5, firing the dried green body at 1780°C to obtain the finished push plate;
[0043] Step 6. Inspection of the finished product out of the kiln;
[0044] Step 7, the finished product is marked and put into storage.
[0045] Through Example 1, the obtained 1750°C high-temperature corundum-mullite push plate can achieve the following prope...
example 2
[0047] A 1750°C high-temperature corundum mullite push plate formula consists of 28 parts of fused mullite, 35 parts of fused white corundum, 15 parts of platy corundum, 12 parts of a-Al2O3 micropowder, 7 parts of kaolin, activated 1 part of agent, 2 parts of binder.
[0048] The process flow for preparing a 1750°C high-temperature corundum-mullite push plate is the same as Example 1.
[0049] Through Example 2, the obtained 1750°C high temperature corundum mullite push plate can achieve the following properties: 1. It can be used for a long time without deformation under the condition of 1750°C high temperature and high pressure; 2. The service life is extended to about 6 months; 3. It has extremely high thermal vibration stability, and the push plate does not crack from the high temperature zone to the low temperature zone; 4. It has sufficient normal temperature strength and high temperature strength, and good wear resistance.
example 3
[0051] A 1750°C high-temperature corundum mullite push plate formula consists of 23 parts of fused mullite, 40 parts of fused white corundum, 16 parts of platy corundum, 10 parts of a-Al2O3 micropowder, 8 parts of kaolin, activated 2 parts of agent, 1 part of binder.
[0052] The process flow for preparing a 1750°C high-temperature corundum-mullite push plate is the same as Example 1.
[0053] Through Example 3, the obtained 1750°C high temperature corundum mullite push plate can achieve the following properties: 1. It can be used for a long time without deformation under the condition of 1750°C high temperature and high pressure; 2. The service life is extended to about 6 months; 3. It has extremely high thermal vibration stability, and the push plate does not crack from the high temperature zone to the low temperature zone; 4. It has sufficient normal temperature strength and high temperature strength, and good wear resistance.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap