Polyurethane composite material having shape memory function sponge, and preparation and using method thereof

A polyurethane combination material and memory technology, applied in the field of polyurethane, to achieve the effect of promoting blood circulation, alleviating fatigue, and improving hardness and strength

Active Publication Date: 2012-12-05
SHANDONG INOV POLYURETHANE
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many types of materials for the raised part, most of which are relatively soft materials to reduce the pressure on the hands, but they must have a certain amount of support. For the time being, we have not found an ideal material that can do it at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Group A is divided into:

[0026] Polyether polyol 1#: 45

[0027] CPOP-290E: 33

[0028] Y1030: 20

[0029] Water: 1.5

[0030] B8002: 0.5

[0031] Group B is divided into:

[0032] Polyether polyol 1#: 25

[0033] ED-28: 11

[0034] 1,4-Butanediol: 2

[0035] Pure MDI: 50

[0036] Liquefied MDI: 10

[0037] SK1900: 2

[0038] Group C is divided into:

[0039] DMEA: 20

[0040] A300: 80

[0041] Among them, polyether polyol 1# is a polyoxypropylene triol capped with ethylene oxide, which uses glycerin as the initiator, the primary hydroxyl content is ≥80%, and the number average molecular weight is 9000.

[0042] A component material: first put the polyether polyol 1#, CPOP-290E, Y1030 based on the formula amount into the mixing tank and stir, then add the measured water and B8002 in turn, at room temperature, the speed is 80 rpm Minutes, stirring for 1.5 hours, the qualified product of component A is obtained;

[0043] B component material: Put polyethe...

Embodiment 2

[0047] Group A is divided into:

[0048] Polyether polyol 1#: 25

[0049] CPOP-290E: 33

[0050] Y1030: 40

[0051] Water: 1.5

[0052] B8002: 0.5

[0053] Group B is divided into:

[0054] Polyether polyol 1#: 25

[0055] ED-28: 11

[0056] 1,4-Butanediol: 2

[0057] Pure MDI: 50

[0058] Liquefied MDI: 10

[0059] SK1900: 2

[0060] Group C is divided into:

[0061] DMEA: 20

[0062] A 300: 80

[0063] Among them, polyether polyol 1# is a polyoxypropylene triol capped with ethylene oxide, with glycerin as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight of 8000.

[0064] A component material: first put the polyether polyol 1#, CPOP-290E, Y1030 based on the formula amount into the mixing tank and stir, then add the measured water and B8002 in turn, at room temperature, the speed is 80 rpm Minutes, stirring for 1.5 hours, the qualified product of component A is obtained;

[0065] B component material: preparation method is the same as...

Embodiment 3

[0069] Group A is divided into:

[0070] Polyether polyol 1#: 25

[0071] CPOP-290E: 33

[0072] Y1030: 40

[0073] Water: 1.5

[0074] B8002: 0.5

[0075] Group B is divided into:

[0076] Polyether polyol 1#: 10

[0077] ED-28: 20

[0078] 1,4-Butanediol: 3

[0079] Pure MDI: 55

[0080] Liquefied MDI: 10

[0081] SK1900: 2

[0082] Group C is divided into:

[0083] DMEA: 20

[0084] A300: 80

[0085] Among them, polyether polyol 1# is a polyoxypropylene triol capped with ethylene oxide, which uses glycerin as the initiator, the primary hydroxyl content is ≥80%, and the number average molecular weight is 9000.

[0086] A component material: preparation method is the same as embodiment 1;

[0087] B component material: put polyether polyol 1#, ED-28, SK1900 based on the formula into the reaction kettle at room temperature, stir and heat up to 100°C, dehydrate and degas under vacuum (≤-0.098MPa) for 2.5 hours, Then when the temperature is lowered to 30°C, add me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of polyurethane, and relates to a polyurethane composite material having a shape memory function sponge, and a preparation and using method thereof. The composite material comprises a component A, a component B and a component C, wherein the component A comprises polyether polyol and polymer polyol, a foam stabilizer and a foaming agent, and the component B comprises polyether polyol, isocyanate, a hardening agent and a polyether opening agent. The shape memory sponge can generate memory deformation along with temperature sensing and pressure, and has the advantages of moderate rebound speed, no obstructing and shrinkage, large physical mechanical strength, certain support strength and the like. By a mouse pad manufactured by the polyurethane composite material having the shape memory sponge, on one hand, the hardness and strength of the traditional memory sponge is improved, and the mouse pad has a certain support function for wrists; and on the other hand, the memory sponge has a temperature sensing effect and a shape memory function, so that the memory sponge can generate zero-pressure support for each part of the wrist, promote blood circulation for each part of the wrist, and relieve fatigue.

Description

technical field [0001] The invention belongs to the technical field of polyurethane, and relates to a polyurethane composite material with a shape memory function sponge and a preparation and use method thereof, in particular to a polyurethane composite material used for a mouse pad with a shape memory function and a preparation method and a use method thereof. Background technique [0002] As we all know, with the continuous advancement of science and technology, computers have increasingly become an essential tool for people to play games and entertain, obtain information, input and store information, and many people are directly engaged in computer-related work, and many people spend their time on computers. an average of more than six hours a day. The mouse is the main part of the computer control operation, according to its working principle and its internal structure, it can be divided into mechanical type, optical mechanical type and photoelectric type. Most computer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08G18/12C08G101/00
Inventor 徐军牛富刚孙清峰罗杰
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com