Wire rope lubricating grease composition having dual effects of lubrication and anti-corrosion

A steel wire rope grease, dual-effect technology, applied in the field of steel wire rope grease composition, can solve the problem of inability to balance lubrication and anti-rust performance, and achieve the purpose of delaying corrosion and wear speed, improving wear resistance, good permeability and coating. Effect

Inactive Publication Date: 2012-12-19
CHINA PETROLEUM & CHEM CORP
View PDF4 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The object of the present invention is to overcome the defect that the lubricating grease composition in the prior art can not take into account the lubricating and antirust performance, and to provide a semi-fluid steel wire rope grease with good lubricating and antirust effects at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wire rope lubricating grease composition having dual effects of lubrication and anti-corrosion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A steel wire rope grease composition with dual functions of lubrication and rust prevention, the components and mass percentages are as follows:

[0032] (1) No. 2 complex calcium sulfonate base grease 61.2%;

[0033] (2) Low pour point base oil 34.0%;

[0034] (3) Diphenylamine 0.4%;

[0035] (4) Colloidal graphite 2.1%;

[0036] (5) ozokerite 2.3%.

[0037] No. 2 composite calcium sulfonate base grease [cone penetration 269, dropping point 335°C, similar viscosity (-10°C, 10s -1 )483Pa·s〕612g into the kettle, and then add polyα-olefin synthetic oil (100℃ kinematic viscosity 12.0mm 2 / s, freezing point -42°C) 340g, stir and heat up. When the temperature rises to 115-135°C, stop heating and keep stirring at the temperature for 23 minutes. Cool the material. When the temperature reaches 95-110°C, add 4g of diphenylamine, 21g of colloidal graphite (particle size<25μm), and 23g of pre-melted ozokerite (melting point: 75°C). Stir for 15 minutes, then get out of the ...

Embodiment 2

[0039] A steel wire rope grease composition with dual functions of lubrication and rust prevention, the components and mass percentages are as follows:

[0040] (1) No. 2 complex calcium sulfonate base grease 63.5%;

[0041] (2) Low pour point base oil 31.0%;

[0042] (3) Diphenylamine 0.6%;

[0043] (4) Colloidal graphite 1.8%;

[0044] (5) ozokerite 3.1%.

[0045] No. 2 composite calcium sulfonate base grease [cone penetration 271, dropping point 336°C, similar viscosity (-10°C, 10s -1 )513Pa·s〕635g into the kettle, and then add low pouring mineral base oil (100℃ kinematic viscosity 8.0mm 2 / s, freezing point -36°C) 310g, stir and heat up. When the temperature rises to 115-135°C, stop heating and keep stirring at the temperature for 27 minutes. Cool the material. When the temperature reaches 95-110°C, add 6g of diphenylamine, 18g of colloidal graphite (particle size<25μm), and 31g of pre-melted ozokerite (melting point 70°C). Stir for 18min, then get out of the kettl...

Embodiment 3

[0047] A steel wire rope grease composition with dual functions of lubrication and rust prevention, the components and mass percentages are as follows:

[0048] (1) No. 2 complex calcium sulfonate base grease 51.0%;

[0049] (2) Low pour point base oil 38.0%;

[0050] (3) Diphenylamine 1.0%;

[0051] (4) Colloidal graphite 5.5%;

[0052] (5) ozokerite 4.5%.

[0053] No. 2 composite calcium sulfonate base grease [cone penetration 295, dropping point 330°C, similar viscosity (-10°C, 10s -1 )420Pa·s〕510g is put into the kettle, and then add low pouring mineral base oil (100℃ kinematic viscosity 5.0mm 2 / s, freezing point -40°C) 380g, stir and heat up. When the temperature rises to 115-135°C, stop heating and keep stirring at the temperature for 20 minutes. Cool the material. When the temperature reaches 95-110°C, add 10g of diphenylamine, 55g of colloidal graphite (particle size<25μm), and 45g of pre-melted ozokerite (melting point: 72°C). Stir for 10min, then get out of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
drop melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
drop melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wire rope lubricating grease composition having dual effects of lubrication and anti-corrosion. The composition comprises the following components: 51.0 % to 72.5 % of No. 2 composite calcium sulfonate grease, 25.0 to 38.0 % of low-freezing-point base oil, 0.2 to 1.0 % of diphenylamine, 1.3 to 5.5 % of colloidal graphite and 1.0 to 4.5 % of ozocerite. According to the invention, the composite uses the specific composite calcium sulfonate grease as a base oil, and is added with the low-freezing-point base oil and various additives to further improve performance such as low-temperature resistance, anti-oxidation, wear resistance, and water resistance of the product, so that the wire rope lubricating grease having dual effects of lubrication and anti-corrosion can be obtained. The lubricating grease has dual effects of lubrication and anti-corrosion, and can delay corrosion and wearing speed of the wire rope. The product is suitable for lubrication and protection of various wire ropes under ocean climate conditions such as seaport, marine ship, offshore drilling platforms, etc.

Description

technical field [0001] The invention belongs to the technical field of lubricating grease, and in particular relates to a steel wire rope grease composition with dual functions of lubricating and antirust. Background technique [0002] In marine climate conditions, various corrosion problems can be caused to various metal parts. Especially for marine operating environments such as seaports, shipping ships, and offshore drilling platforms, the corrosion problem of steel wire ropes used in various lifting or traction machinery is more prominent due to long-term exposure. Most of the failure modes of wire ropes working in this environment are two types of wear and corrosion. The waste of steel wire ropes due to wear and corrosion is staggering. The survey shows that due to serious corrosion, a set of ropes will be replaced every 2 to 3 months. Compared with the relatively dry climate on land, marine climate conditions will significantly accelerate the degree and speed of ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/06C10N40/32C10N50/10C10N30/06C10N30/00
CPCD07B1/144D07B2501/2061
Inventor 王先会田宁宁刘翠苹刘在均
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com