High-toughness electric conduction nylon composite material and preparation method thereof

A nylon composite material and composite material technology are applied in the field of high-toughness conductive nylon composite materials, which can solve the problems of difficult to bear heavy load, limited application range, nylon electrical insulation, high water absorption, etc., and achieve improved electrical conductivity and low raw material prices. , the effect of good electrical conductivity

Active Publication Date: 2013-01-09
合肥市和裕达塑业有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with metals, nylon also has disadvantages such as electrical insulation, high water absorption, certain brittleness and difficulty in bearing heavy loads, which limits its application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness electric conduction nylon composite material and preparation method thereof
  • High-toughness electric conduction nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～9

[0040] Take the raw materials according to the ratio shown in Table 1:

[0041] Table 1:

[0042]

polymer matrix

carbon black

liquid paraffin

Example 1

PA6: 500g

Conductive carbon black: 200g

POE-g-MA: 300g

10ml

Example 2

PA6: 550g

Conductive carbon black: 150g

POE-g-MA: 300g

10ml

Example 3

PA6: 600g

Conductive carbon black: 100g

POE-g-MA: 300g

10ml

Example 4

PA6: 700g

Conductive carbon black: 200g

POE-g-MA: 100g

10ml

Example 5

PA6: 800g

Conductive carbon black: 100g

POE-g-MA: 100g

10ml

Example 6

PA66: 500g

Conductive carbon black: 200g

POE-g-MA: 300g

10ml

Example 7

PA6: 500g

Acetylene carbon black: 200g

POE-g-MA: 300g

10ml

Example 8

PA6: 500g

Conductive carbon black: 200g

EPDM-g-MA: 300g

10ml

Example 9

PA6: 500g

Conductive carbon black: 200g

POE-g-...

Embodiment 9

[0046] The preparation method of Example 9 is as follows: Weigh 500g of dried PA6 slices, 200g of conductive carbon black, and 300g of POE-g-MA, add 10ml of liquid paraffin, mix evenly, add to a double-roller mill for mixing, and the mixing temperature is 240°C , The mixing time is 15min. After mixing, the compound was preheated at 245°C for 10 minutes without pressure, and then hot-pressed at 10 MPa for 10 minutes to prepare test samples. The performance test results of the obtained composite materials are shown in Table 2.

[0047] Table 2: Composite performance test results

[0048]

Embodiment 1

[0050] Examples 10-14 weighed the raw materials according to the proportions in Table 3, the preparation method was the same as that of Example 1, and the performance test results of the obtained composite materials were shown in Table 4.

[0051] table 3:

[0052]

[0053]

[0054] Table 4: Composite performance test results

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
impact strengthaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a nylon composite material and particularly relates to a high-toughness electric conduction nylon composite material and a preparation method thereof. The composite material comprises raw materials of 50-80 wt.% of a polymer matrix, 10-20 wt.% of carbon black, 10-30 wt.% of maleic anhydride grafted polyolefin elastomer and 0.5-1.5 wt.% of liquid paraffin. The electric conduction performance of the obtained composite material is better than that of a carbon black / polymer two-phase composite material, and compared with impact strength of a pure matrix and the carbon black / polymer two-phase composite material, the impact strength of the obtained composite material is substantially improved; according to the high-toughness electric conduction nylon composite material and the preparation method thereof, a one-step method preparation process is used, so that industrialization production is easy to achieve, and the composite material is suitable for large-scale popularization and application; and the cheap foundation raw materials are used, so that costs are obviously reduced, and the composite material has a good price advantage.

Description

technical field [0001] The invention relates to a nylon composite material, in particular to a high-toughness conductive nylon composite material and a preparation method of the composite material. Background technique [0002] With the rapid development of science and technology and the electronic industry, the application of conductive polymer composite materials is becoming more and more extensive. In addition to the advantages of light weight, easy processing, high elasticity, corrosion resistance, and wear resistance inherent in polymer materials, this type of material also needs to have certain electrical properties to meet the requirements of antistatic and conductive materials, electromagnetic shielding materials, and self-protection materials. The needs of temperature control heating materials and other fields. Conductive polymer composite materials are a kind of functional polymer composite materials made of insulating polymer matrix and conductive filler in a cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L77/02C08L77/06C08L51/06C08K3/04B29C47/92B29C48/92
CPCB29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 于中振张好斌胡娟何顺伦余莉花
Owner 合肥市和裕达塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com