Aluminum profile and heating processing technology thereof

An aluminum profile, soaking heat treatment technology, applied in the field of aluminum profile processing, can solve the problems of insufficient fracture toughness and fatigue performance, low strength of aluminum profiles, etc., and achieve the effect of improving performance and metallographic structure

Inactive Publication Date: 2013-01-09
张家港市金邦铝业股份有限公司
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides an aluminum profile and its heat treatment process, the purpose of which is mainly to solve th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum profile and heating processing technology thereof
  • Aluminum profile and heating processing technology thereof
  • Aluminum profile and heating processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example:

[0025] like figure 1 As shown, an aluminum profile, the aluminum profile 1 is a circular shape, the inner diameter of the circular aluminum profile 1 is 31.4 mm±0.2; the wall thickness of the circular aluminum profile 1 is 3.6 mm; and the composition The mass percentage of each component of the aluminum alloy of the aluminum profile is:

[0026]

[0027] like figure 2 As shown, a heat treatment process for an aluminum profile adopts the above-mentioned raw material ratio, and the heat treatment process includes the following steps:

[0028] (1) Smelting and casting the raw aluminum ingots: the casting speed is 85-95mm / min; the casting temperature is 715-730°C; the cooling water pressure is 0.04-0.08MPa;

[0029] (2) Soaking heat treatment: Soak the aluminum ingot after smelting and casting in step (1);

[0030] (3) Long ingot hot shearing: carry out long ingot hot shearing treatment on the aluminum ingot after soaking treatment;

[0031] (4) Extrusio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An aluminum profile is annular and is prepared by components in percentage by weight: 91-93% of Al, 5.5-5.7% of Zn, 0.15-0.2% of Si, 0.80-0.86% of Mg, 0.1-0.14% of Cu, 0.2-0.35% of Fe, 0.1-0.12% of Cr, 0.15-0.2% of Mn, 0.1-0.25% of Zr and 0.1-0.2% of Ti. A heating processing technology comprises following steps of: (1) smelting and casting raw material aluminum ingots, enabling a casting speed to be 85-95mm/min, enabling a pouring temperature to be 715-730 DEG C, and enabling cooling water pressure to be 0.04-0.08MPa; (2) extruding, enabling an extruding temperature to be 440-460DEG C, and enabling an extruding speed to be 3-6M/min; (3) conducting stretcher strengthening, and enabling strengthening deformation quantity to be 0.5%-1.5%; (4) conducting aging furnace heating, enabling a furnace temperature of an aging furnace at a first section of aging to be 100 DEG C, enabling heat preservation time to be 3h, enabling the furnace temperature of the aging furnace at a second section of aging to be 160 DEG C, and enabling heat preservation time to be 5h; and (5) testing and packaging. The aluminum profile mainly solves the problem that the aluminum profile in the prior art is not high in strength, poor in breakage toughness and poor in fatigue performance.

Description

technical field [0001] The invention belongs to the technical field of aluminum profile processing, and relates to an aluminum profile used in bicycle components and a heat treatment process thereof. Background technique [0002] Aluminum profiles are aluminum materials with different cross-sectional shapes obtained by hot-melting and extruding aluminum rods. Aluminum profiles are widely used in various production sectors, such as automobiles, motorcycles, bicycle accessories, building materials (locks and door handles), hardware and electrical appliances, etc. The aluminum profile is easy to damage due to its low strength. In order to improve the strength, fracture toughness and fatigue performance of the aluminum profile, the most direct method is to increase the purity of the raw material and reduce the content of Fe and Si in the aluminum alloy. Costs can only add up and may be difficult to achieve in metallurgical processes. [0003] Therefore, how to improve the stre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/10C22F1/053
Inventor 卢秋虎
Owner 张家港市金邦铝业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap