A pu high fullness anti-sag bright white topcoat

A fullness and anti-sag technology, applied in coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve the problems of general yellowing resistance, slow drying speed, general adhesion, etc.

Active Publication Date: 2016-01-20
四川巴德士新材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the construction of similar products on the market, the common disadvantages are slow drying speed, poor fullness, general adhesion, general yellowing resistance, etc. This is a difficult problem that has always plagued the coatings industry, and the present invention overcomes the shortcomings of commercially available products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A pu high fullness anti-sag bright white topcoat
  • A pu high fullness anti-sag bright white topcoat
  • A pu high fullness anti-sag bright white topcoat

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of PU high plumpness anti-sag bright white finish paint, and its weight-to-number ratio is:

[0024] Part A 1, Part B 0.8, Part C 0.5;

[0025] Component C does not participate in the chemical reaction, and only plays the role of thinning construction.

[0026] The parts by weight ratio of the first component is as follows:

[0027] Synthetic fatty acid resin 10, saturated polyester resin 10,

[0028] Acrylic resin 15, PU advanced bright white flour paste 60,

[0029] Leveling agent 0.1, defoamer 0.4,

[0030] Auxiliary agent 0.8, n-butyl acetate 3.4;

[0031] When preparing, add and disperse in sequence until fully uniform, and control the viscosity at 4500±200cps / 25℃;

[0032] The parts by weight ratio of the B component is as follows:

[0033] n-Butyl acetate 50, curing agent 50;

[0034] The proportion by weight of the C component is as follows:

[0035] n-Butyl acetate 40, toluene 60;

[0036] The proportion by weight of the PU high-grade bright whi...

Embodiment 2

[0052] A kind of PU high plumpness anti-sag bright white finish paint, and its weight-to-number ratio is:

[0053] Part A 1, Part B 0.8, Part C 0.5;

[0054] The parts by weight ratio of the first component is as follows:

[0055] Synthetic fatty acid resin 15, saturated polyester resin 15,

[0056] Acrylic resin 20, PU advanced bright white flour paste 65,

[0057] Leveling agent 0.3, defoamer 0.6,

[0058] Auxiliary 1, n-butyl acetate 4;

[0059] When preparing, add and disperse in sequence until fully uniform, and control the viscosity at 4500±200cps / 25℃;

[0060] The parts by weight ratio of the B component is as follows:

[0061] n-Butyl acetate 50, curing agent 50;

[0062] The proportion by weight of the C component is as follows:

[0063] n-Butyl acetate 60, toluene 40;

[0064] The proportion by weight of the PU high-grade bright white flour paste is as follows:

[0065] Synthetic fatty acid resin 55, dispersant 1.2,

[0066] Fumed silica 0.6, titanium dioxi...

Embodiment 3

[0070] A kind of PU high plumpness anti-sag bright white finish paint, and its weight-to-number ratio is:

[0071] Part A 1, Part B 0.8, Part C 0.5;

[0072] The parts by weight ratio of the first component is as follows:

[0073] Synthetic fatty acid resin 13, saturated polyester resin 13,

[0074] Acrylic resin 17, PU advanced bright white flour paste 62,

[0075] Leveling agent 0.2, defoamer 0.5,

[0076] Auxiliary 0.9, n-butyl acetate 3.7;

[0077] When preparing, add and disperse in sequence until fully uniform, and control the viscosity at 4500±200cps / 25℃;

[0078] The parts by weight ratio of the B component is as follows:

[0079] n-Butyl acetate 50, curing agent 50;

[0080] The proportion by weight of the C component is as follows:

[0081] n-Butyl acetate 45, toluene 50;

[0082] The proportion by weight of the PU high-grade bright white flour paste is as follows:

[0083] Synthetic fatty acid resin 47, dispersant 1.1,

[0084] Fumed silica 0.5, titanium d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a PU (polyurethane) high-fullness anti-sinking luster white finish paint which is composed of a component A, a component B and a component C, wherein the component A is prepared from saturated polyester resin, synthetic fatty acid resin, acrylic resin, PU high-grade luster white finish slurry, dispersant, leveling agent, defoaming agent, environment-friendly solvent and the like; the component B is prepared from n-butyl acetate and curing agent; and the component C is prepared from n-butyl acetate, methylbenzene and the like. The detection and trial prove that the polyurethane white finish paint provided by the invention has the advantages of excellent yellowing resistance, strong coating adhesive force, high hardness, wear and scratch resistance, high heat resistance, favorable constructability, favorable leveling property, high fullness and excellent anti-sinking capacity; and the environment-friendly property conforms to the index in GB18581.

Description

technical field [0001] The invention relates to a bright white topcoat. Background technique [0002] At present, the PU high-fullness anti-sagging bright white topcoat is an environment-friendly paint with excellent comprehensive properties. It has the characteristics of good sag resistance, high whiteness, good fullness, and excellent yellowing resistance. Finishes for suite furniture and high-end cabinet furniture. After construction of similar products on the market, common shortcomings are shown as slow drying speed, poor fullness, general adhesion, general yellowing resistance, etc. This is a difficult problem that has always plagued the coating industry, and the present invention overcomes the shortcomings of the commercially available products. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to: provide a kind of PU high plumpness anti-sag bright white finish, it forms a layer of high plumpness, excellent sag resistance, extremely high wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D167/00C09D133/00C09D7/12
Inventor 方学平洪僚
Owner 四川巴德士新材料有限公司