Solid wood composite geothermal floor with carbonized surface and manufacturing method of solid wood composite geothermal floor

A solid wood composite, geothermal floor technology, applied in the direction of floor, building structure, construction, etc., can solve the problems of poor stability, prone to degumming and tiles, etc., to achieve good stability, fast production speed and long service life. Effect

Active Publication Date: 2013-03-13
ZHEJIANG SHIYOU TIMBER
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solid wood composite floor made by the above-mentioned patent has poor stability, and the surface and the surface are prone to degumming and tile phenomenon during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid wood composite geothermal floor with carbonized surface and manufacturing method of solid wood composite geothermal floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1, see attached figure 1 , a surface carbonized solid wood composite geothermal floor, comprising a skin 1 and a base material 2, the skin 1 and the base material 2 are bonded together by glue, the glue is formaldehyde-free glue, forming a glue layer with a thickness of 0.1-0.2mm , the skin 1 is made of fast-growing wood or hardwood, the substrate 2 is made of fast-growing wood, the thickness of the skin 1 is 1.2-6.2mm, and the hardwood is oak, ash, teak, elm, etc.; The fast-growing materials are poplar, willow, eucalyptus, southern pine, sylvestris pine and Douglas fir.

[0045] A method for manufacturing a surface-carbonized solid wood composite geothermal floor, comprising the following steps:

[0046] (1) Production steps of the skin and the base material; according to the needs, the skin 1 and the base material 2 are made from blanks, the thickness of the skin 1 is 1.2-6.2 mm, and the thickness of the base material 2 is 10-20 mm; the stability of the sk...

Embodiment 2

[0061] Example 2, a surface carbonized solid wood composite geothermal floor, comprising a skin 1 and a base material 2, the skin 1 and the base material 2 are bonded together by glue, and the skin 1 and the base material 2 are made of fast-growing Fast-growing wood is poplar, willow, eucalyptus, southern pine, sylvestris pine and Douglas fir.

[0062] A method for manufacturing a surface-carbonized solid wood composite geothermal floor, comprising the following steps:

[0063] (1) The production step of the skin and the base material; the skin and the base material are made from blanks as required, wherein the skin is a fast-growing material with a thickness of 1.2-6.2 mm, and the base material is a fast-growing material; the width direction of the skin is stable property ε table, the stability ε group in the width direction of the substrate, wherein, the range of the stability ε table in the width direction of the skin is: 99.875% ε group ≤ ε table ≤ 100.632% ε group;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a solid wood composite geothermal floor with a carbonized surface and a manufacturing method of the solid wood composite geothermal floor. The solid wood composite geothermal floor comprises a skin and a base material which are integrally bonded through glue water. The manufacturing method comprises the steps as follows: (1) making the skin and the base material; (2) carrying out heat treatment on the skin; (3) carrying out heat treatment on the base material; (4) gluing and coldly pressing; and (5) machining. According to the solid wood composite geothermal floor and the manufacturing method, the manufacturing speed is high, the manufacturing efficiency is high, the energy consumption is low, the energy is saved, and the environment is protected; and the manufactured solid wood composite floor is good in stability and long in service life, and the phenomenon of adhesive failure and tiles is reduced when the skin is used.

Description

technical field [0001] The invention relates to the technical field of composite floors, and more specifically relates to a carbonized solid wood composite geothermal floor and a manufacturing method thereof. Background technique [0002] With the shortage of hardwood raw materials, the use of fast-growing wood is becoming more and more popular, especially the field of solid wood utilization of fast-growing wood is becoming more and more extensive. Therefore, improving the comprehensive utilization rate of fast-growing wood and solid wood has become a need for the next stage of fast-growing wood solid wood utilization. problems faced. The authorized announcement number is CN201517278U, and the Chinese utility model patent on June 30, 2010 discloses a double-layer solid wood composite floor, which consists of veneer and base material; both veneer and base material are made of fast-growing materials; The materials are poplar, willow, eucalyptus, southern pine, sylvestris pine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F15/04
Inventor 涂登云于学利劳奕旻杨莎莎朱月虎王明俊郑峰峰杜春烨
Owner ZHEJIANG SHIYOU TIMBER
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com