Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Manufacturing method of hot bent 3D (Three Dimensional) glass white sheet

A manufacturing method, glass white technology, applied in glass manufacturing equipment, glass molding, glass tempering, etc., can solve the problems of large bending curvature error of 3D glass white sheet, cannot meet the needs of actual use, and low processing accuracy, and achieve Novel design, fast production speed, and the effect of eliminating internal stress

Inactive Publication Date: 2017-05-31
DONGGUAN YUANMEI PRECISION ELECTRONICS CO LTD
View PDF1 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the production of the above two processing technologies, it was found that the 3D glass white sheet produced had a large curvature error, low processing accuracy, rough surface, low pass rate, slow production speed, and high processing cost, which could not meet the needs of actual use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The specific embodiment of the present invention is described further below:

[0021] A method for manufacturing a hot-bending 3D glass white sheet, manufactured according to the following steps,

[0022] ①Material cutting, place the glass white flake material on the working table of the three-axis cutting machine, start the coarse grinding wheel knife, and cut the glass white flake material into multiple small glass white flakes of suitable size at a speed of 10,000-12,000 rpm;

[0023] ② Jingdiao, put the small glass white sheet into the CNC engraving machine to punch holes and grind edges. The feeding speed is 550-1500mm / min, preferably 1000mm / min, the feeding speed when the main knife grinds the four sides is 250-2000mm / min, preferably 1200mm / min, the vacuum adsorption pressure is -0.08~-0.06Mpa, and the blowing pressure is 0.5~0.8Mpa;

[0024] ③Sweeping, the glass sweeping machine performs sweeping treatment on the glass white sheet to make the surface smoother a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of a hot bent 3D (Three Dimensional) glass white sheet. The manufacturing method comprises the following steps: (1) cutting a material: cutting a glass white sheet material into a plurality of small glass white sheets with proper sizes; (2) finely engraving: putting the small glass white sheets into a CNC (Computer Numerical Control) fine engraving machine, and punching and grinding edges; (3) cleaning: carrying out cleaning treatment on the glass white sheet by utilizing a glass cleaning machine; (4) carrying out ultrasonic treatment: washing surface residual waste dreg on the surface of the glass white sheet by utilizing an ultrasonic washing machine; (5) hot bending: putting the glass white sheet into a hot bending mold and hotly bending, machining and molding the glass white sheet into a 3D curve surface; (6) tempering: putting the hotly bent glass white sheet into a tempering frame; conveying the tempering frame into a tempering furnace and raising the temperature to 380 DEG C-420 DEG C, wherein the heating time is 4h-8h and the hardness reaches 7H; (7) carrying out plasma spraying: putting the glass white sheet into a fingerprint oil spraying machine and spraying fingerprint oil on a surface through plasmas; baking at a temperature of 140 DEG C-160 DEG C for 25-30 minutes until the fingerprint oil is dried; (8) fitting: fitting release films on upper and lower surfaces of the glass white sheet; and (9) packaging.

Description

technical field [0001] The invention relates to a hot-bent 3D glass white sheet, in particular to a method for manufacturing a hot-bent 3D glass white sheet. Background technique [0002] 3D white glass, also known as 3D curved glass, is often used for screen protection of smartphones, tablet computers, wearable devices, dashboards and industrial computers. There are two main processing technologies for the current 3D glass white film: one is to learn from the processing technology of traditional glass optical lens or glass eyeglass lens, and use CNC numerical control machine tools to process it completely by mechanical cutting and forming. The production efficiency is mainly affected by the 3D glass white film. The radius of curvature and the height of the product are affected; the other is to learn from the processing technology similar to the color crystal glass hot-bending forming. After cutting and blanking the CNC machine tool according to the initial processing size, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B23/03C03B27/012C03C17/28B24B1/00B24B29/02B24B9/10B28D1/14B32B37/10
CPCC03B23/03B24B1/00B24B9/10B24B29/02B28D1/14B32B37/10C03B27/012C03C17/28
Inventor 王美治
Owner DONGGUAN YUANMEI PRECISION ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products