Thermosetting waterproof adhesive and preparation method thereof

A waterproof adhesive and thermosetting technology, applied in adhesive types, ester copolymer adhesives, etc., can solve problems such as inability to bond substrates, high surface drying temperature, poor stability, etc., to achieve good bonding, Low dry temperature and strong adhesion

Active Publication Date: 2013-03-20
重庆瑞福德精细化工科技有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the waterproof glue on the market generally has problems such as high dry temperature (above 130 degrees), poor adhesion, low hardness, etc., cannot be well combined with the substrate, and has poor stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Stir the raw materials evenly according to the following mass percentages to prepare additives for use:

[0034] 1) Polyether 21%;

[0035] 2) Acrylic 30%;

[0036] 3) Methoxyphenol 9%;

[0037] 4) Ether 40%;

[0038] Wherein, the defoamer is polyether GP6303; the leveling agent is acrylic leveling agent 9200; the viscosity stabilizer is methoxyphenol; and the solvent is ether solvent.

[0039] Preparation of thermosetting waterproof adhesive:

[0040] Ether 45%;

[0041] Ethyl acetate 16%;

[0042] Methyl acrylate 37%;

[0043] Methyl methacrylate 1.5%;

[0044] Benzoyl Peroxide 0.2%;

[0045] Additive butyl ether 0.1%;

[0046] Blocked isocyanic acid curing agent MF-K60X 0.2%;

[0047] Weigh it according to the above mass percentage, put it into the reaction kettle to fully react (72~73°C), and then test it with a fineness meter. If the fineness reaches below 5 μm, the thermosetting waterproof adhesive is obtained.

[0048] The above thermosetting waterproo...

Embodiment 2

[0050] Stir the raw materials evenly according to the following mass percentages to prepare additives for use:

[0051] 1) Polyether 35%;

[0052] 2) Acrylic 25%;

[0053] 3) Methoxyphenol 5%;

[0054] 4) Ether 35%;

[0055] Wherein, the defoamer is polyether GP6303; the leveling agent is acrylic leveling agent 9200; the viscosity stabilizer is p-hydroxyanisole; and the solvent is ether solvent.

[0056] Preparation of thermosetting waterproof adhesive:

[0057] Ether 35%;

[0058] Ethyl acetate 6%;

[0059] Methyl acrylate 48%;

[0060] Methyl methacrylate 8%;

[0061] Benzoyl Peroxide 1%;

[0062] Additive butyl ether 0.5%;

[0063] Curing agent 1.5%;

[0064] Weigh it according to the above mass percentage, put it into the reaction kettle to fully react (72~73°C), and then test it with a fineness meter. If the fineness reaches below 5 μm, the thermosetting waterproof adhesive is obtained.

[0065] After a high-temperature baking test at 150°C for 80mins, a high-tem...

Embodiment 3

[0067] Stir the raw materials evenly according to the following mass percentages to prepare additives for use:

[0068] 1) Polyether 40%;

[0069] 2) Acrylic 20%;

[0070] 3) Methoxyphenol 10%;

[0071] 4) Ether 30%;

[0072] Wherein, the defoamer is polyether GP6303; the leveling agent is acrylic leveling agent 9200; the viscosity stabilizer is hydroquinone monomethyl ether; the solvent is ether solvent.

[0073] Preparation of thermosetting waterproof adhesive:

[0074] Ether 40%;

[0075] Ethyl acetate 10%;

[0076] Methyl acrylate 40%;

[0077] Methyl methacrylate 7%;

[0078] Benzoyl Peroxide 1%;

[0079] Additive butyl ether 0.2%;

[0080] Curing agent 1.8%;

[0081] Weigh it according to the above mass percentage, put it into the reaction kettle to fully react (72~73°C), and then test it with a fineness meter. If the fineness reaches below 5 μm, the thermosetting waterproof adhesive is obtained.

[0082] After a high-temperature baking test at 150°C for 80min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention provides a thermosetting waterproof adhesive which is applicable to a silk-screen printing mode of a traditional type, and has very strong adhesive strength after being hardened forcibly. The thermosetting waterproof adhesive is a pressure sensing adhesive of bi-component, and is applicable to the silk-screen printing. The thermosetting waterproof adhesive comprises the following raw materials, by weight, 30% to 60% of pure ethers solvent, 1% to 20% of esters solvent, 30% to 50% of acrylic ester raw materials, 1% to 10% of methacrylic acid raw materials, 0.1% to 1% of initiator, 0.5% to 1% of auxiliary additives and 0.1% to 2% of curing agents.

Description

technical field [0001] The invention relates to a thermosetting waterproof glue and a preparation method thereof. Background technique [0002] Thermosetting waterproof glue is based on the powder particles of insulator materials that are evenly distributed on the printing surface. Through the matching of different proportions of carriers, it can meet the waterproof requirements of products. It is widely used in electronic products and plastic products. [0003] The Chinese invention patent No. 200910040236.7 discloses a white adhesive for flexible printed circuits and its preparation method. The raw material components of the white adhesive include thermosetting resin, filler, thermoplastic resin, rubber, curing agent and curing accelerator. The weight ratio of raw material components is: 20-80 parts of thermosetting resin; 45-150 parts of filler; 0-60 parts of thermoplastic resin; 0-40 parts of rubber; 2-9 parts of curing agent; 0.5-2 parts of curing accelerator ; 40-120 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C08F220/14C08F220/18C08F220/28
Inventor 兰玉彬
Owner 重庆瑞福德精细化工科技有限公司