Two-liquid type rapid stripping synthetic leather composite overlay

A two-component, synthetic leather technology, applied in the field of synthetic leather, can solve the problems of cold resistance, low hydrolysis resistance, large floor area, scratch resistance and poor wear resistance of synthetic leather surface

Active Publication Date: 2009-08-12
ANHUI ANLI MATERIAL TECH
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is simple to operate and the production is easy to control, but the surface of the synthetic leather veneered by this process has poor scratch resistance and wear resistance, low cold resistance and hydrolysis resistance, and unsatisfactory durability
Poor control can also lead to stiff, false sticky and other phenomena
[0003] The composite veneer production process of foreign high-grade synthetic leather mostly adopts the two-component aging veneer process for vene...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-liquid type rapid stripping synthetic leather composite overlay
  • Two-liquid type rapid stripping synthetic leather composite overlay
  • Two-liquid type rapid stripping synthetic leather composite overlay

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] Microfiber veneer for sports shoes.

[0086] The formulation of the dry slurry is by weight:

[0087] Top coat:

[0088] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0089] Solvent 30~80 parts

[0090] Colorant 20-30 parts

[0091] Leveling agent 0.5~1 part

[0092] 0.5~1 parts of peeling aid

[0093] Functional additives 1 to 5 parts

[0094] Adhesive layer:

[0095] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0096] Solvent 10~50 parts

[0097] Colorant 20-30 parts

[0098] Leveling agent 0.5~1 part

[0099] Functional additives 0.5~3 parts

[0100] 8-10 parts of cross-linking agent

[0101] Catalyst 1-3 parts

[0102] Superfine lignin (800-1000 mesh) 5-10 parts

[0103] The physical properties of the made microfiber leather are: wear-resistant H-22*1000 times, peeling>100N / 3cm, cold resistance:>-20℃*80,000,

[0104] Bending at room temperature: >2 million times. If one-component phys...

Embodiment 2

[0106] High-performance space leather veneer.

[0107] The formulation of the dry slurry is by weight

[0108] Top coat:

[0109]Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0110] Solvent 30~80 parts

[0111] Colorant 20-30 parts

[0112] Leveling agent 0.5~2 parts

[0113] 0.5~1 parts of peeling aid

[0114] Functional additives 1 to 5 parts

[0115] middle layer:

[0116] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0117] Solvent 30~50 parts

[0118] Color 0.5~15 parts

[0119] Leveling agent 0.5~1 part

[0120] Functional additives 1 to 5 parts

[0121] Adhesive layer:

[0122] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0123] Solvent 10~50 parts

[0124] Colorant 20-30 parts

[0125] Leveling agent 0.5~1 part

[0126] Functional additives 0.5~3 parts

[0127] Crosslinker 12-16

[0128] Catalyst 1-3

[0129] The physical properties of the leather prod...

Embodiment 3

[0132] High performance sofa leather veneer

[0133] The formulation of the dry slurry is by weight

[0134] Top coat:

[0135] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0136] Solvent 30~80 parts

[0137] Colorant 20-30 parts

[0138] Leveling agent 0.5~2 parts

[0139] 0.5~1 parts of peeling aid

[0140] Functional additives 1 to 5 parts

[0141] middle layer:

[0142] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0143] Solvent 30~50 parts

[0144] Color 0.5~15 parts

[0145] Leveling agent 0.5~1 part

[0146] Functional additives 1 to 5 parts

[0147] Adhesive layer:

[0148] Polyether, polyester polycarbon copolymer polycarbonate type resin 100 parts

[0149] Solvent 10~50 parts

[0150] Colorant 20-30 parts

[0151] Leveling agent 0.5~1 part

[0152] Functional additives 0.5~3 parts

[0153] Crosslinker 14-16

[0154] Catalyst 1-3

[0155] The physical properties of the leather produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a two-liquid type quick forming instant peeling synthetic leather composite veneer, which is mainly characterized in that bonding layer resin is added with a quick crosslinker and a crosslinking catalyst, so that the two-component bonding layer resin achieves quick crosslinking, and can achieve proper degree of crosslinking through normal veneering process so as to achieve the aim of instant peeling. The high peeling hydrolysis resistant non-woven fabric polyurethane synthetic leather produced by the process has good physical and mechanical properties such as high peeling strength, tearing strength and bursting strength, bending resistance, low temperature resistance, hydrolysis resistance, acid and alkali resistance and the like.

Description

technical field [0001] The invention belongs to the field of synthetic leather, and in particular relates to a two-component instant peel-off synthetic leather composite veneer. Background technique [0002] At present, the common synthetic leather veneer process in China is a one-component composite veneer process, commonly known as a single-component composite veneer process. The process is simple to operate, and the production is easy to control. However, the surface of the synthetic leather veneered by this process has poor scratch resistance and wear resistance, low cold resistance and hydrolysis resistance, and unsatisfactory durability. Poor control can also lead to stiff, false sticky and other phenomena. [0003] The composite veneer production process of foreign high-grade synthetic leather mostly adopts the two-component aging veneer process for veneer compounding. Although this process has greatly improved the performance of synthetic leather, due to the need fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/14C09J175/04B32B27/12B32B27/40
Inventor 黄万里笪丽红唐涛刘兵惠坚强
Owner ANHUI ANLI MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap