High-pressure PVC (Poly Vinyl Chloride) hose material
A hose and high-pressure technology, applied in the field of high-pressure PVC hose materials, can solve the problems of reduced service life, oxidation resistance, poor aging performance, and high pressure resistance of PVC hoses, and achieve improved oxidation resistance, low cost, and improved The effect of pressure resistance
Inactive Publication Date: 2013-04-03
QINGDAO XINWANTONG PLASTIC IND
View PDF0 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] At present, the existing PVC pipes include hard and soft pipes, and soft pipes are widely used. However, due to natural factors such as wind and sun, their anti-oxidation and aging properties are worse than PVC hard pipes, and they are not resistant to high pressure. , so the service life of the PVC hose is greatly reduced, which hinders the actual application
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0013] Below in conjunction with specific embodiment the present invention is described in further detail;
[0014] A high-pressure PVC hose material, consisting of the following ingredients in parts by weight:
[0015] Polyvinyl chloride resin 70~80;
[0016] Plasticizer 1~2;
[0017] Stearic acid 10-20;
[0018] Hexamethylphosphoric triamide 3-5;
[0019] Anti-ultraviolet agent 1~2;
[0020] Powdered nitrile 2~3;
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More
Abstract
The invention discloses a high-pressure PVC (Poly Vinyl Chloride) hose material. The hose material consists of the following components in parts by weight: 70-80 parts of polrvinyl chloride resin, 1-2 parts of a plasticizer, 10-20 parts of stearic acid, 3-5 parts of hexamethylphosphoramide, 1-2 parts of an anti-ultraviolet agent, 2-3 parts of powdered butyronitrile and 2-8 parts of zinc oxide. Through the addition of the hexamethylphosphoramide, the antioxidant property of the PVC tubular product is greatly enhanced; and the added powdered butyronitrile is used as a PVC property enhancer, so that the property of the tubular product is obviously enhanced, the tubular product has high strength, the pressure-resistant property is enhanced, the tubular product is especially suitable for a low-temperature environment and the cost is low.
Description
technical field [0001] The invention relates to a high-pressure PVC hose material. Background technique [0002] At present, the existing PVC pipes include hard and soft pipes, and soft pipes are widely used. However, due to natural factors such as wind and sun, their anti-oxidation and aging properties are worse than PVC hard pipes, and they are not resistant to high pressure. , so the service life of the PVC hose is greatly reduced, hindering the actual application. Contents of the invention [0003] In view of the deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a PVC material formula with low cost, good anti-aging effect and high pressure resistance. [0004] In order to solve the above technical problems, the technical solution adopted by the present invention is: a high-pressure PVC hose material, which consists of the following components by weight: [0005] Polyvinyl chloride resin 70~80; [0006] Plast...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L9/02C08K13/02C08K5/09C08K3/22C08K5/5399F16L11/04
Inventor 高义金
Owner QINGDAO XINWANTONG PLASTIC IND
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com