Ceramic sanitary ware product and preparation method thereof

A technology for sanitary ware and products, applied in the field of ceramic sanitary ware products and their preparation, can solve the problems of easy pollution of polished vitrified tiles, and achieve the effects of good promotion and use value, fine texture, pollution resistance, and reasonable process design.

Inactive Publication Date: 2013-04-10
GUANGDONG TREND GROUP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This brings about the problem that polished vitrified tiles are easily polluted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment discloses a ceramic sanitary ware product, which includes glaze and adobe,

[0017] The glaze includes the following components and weight ratio:

[0018] Si0 2 42 parts, Ca0 18 parts, A1 2 0 3 12 parts, ZnO 1 part, Ti0 2 10 copies, K 2 O 0.2 parts, Fe 2 0 3 7.9 parts, Ba0 0.8 parts;

[0019] The adobe includes the following components and weight ratio:

[0020] 30 parts of waste glass, 40 parts of sandstone, 20 parts of clay, and 2 parts of binder.

[0021] The binder is one or a mixture of polyvinyl alcohol PVA, carboxymethyl cellulose CMC and polyvinyl acetate PVAC.

[0022] The invention provides a preparation method of ceramic sanitary ware products, wherein, the preparation method of the glaze is to pulverize the raw materials according to the formula ratio and mix them in a furnace and burn them until they are melted. Coarse raw materials are re-crushed to 200 meshes as glaze raw materials for use; the preparation process of brick a...

Embodiment 2

[0024] This embodiment discloses a ceramic sanitary ware product, which includes glaze and adobe,

[0025] The glaze includes the following components and weight ratio:

[0026] Si0 2 52 parts, Ca0 25 parts, A1 2 0 3 17 parts, ZnO 5 parts, Ti0 2 12 copies, K 2 O 1 part, Fe 2 0 3 9 parts, Ba0 7 parts;

[0027] The adobe includes the following components and weight ratio:

[0028] 40 parts of waste glass, 50 parts of sandstone, 30 parts of clay, and 3 parts of binder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic sanitary ware product. The ceramic sanitary ware product comprises glaze and a green brick, wherein the glaze comprises the following components in part by weight: 42 to 52 parts of SiO2, 18 to 25 parts of CaO, 12 to 17 parts of Al2O3, 1 to 5 parts of ZnO, 10 to 12 parts of TiO2, 0.2 to 1 part of K2O, 7.9 to 9 parts of Fe2O3 and 0.8 to 7 parts of BaO; and the green brick comprises the following components in part by weight: 32 to 38 parts of waste glass, 36 to 47 parts of sandstone, 22 to 28 parts of clay and 2.2 to 3.4 parts of binder.

Description

technical field [0001] The invention relates to a ceramic sanitary ware product and a preparation method thereof. Background technique [0002] Ceramic sanitary ware products are flat, bright and clean, with various designs and colors. However, its glaze is a layer of glass glaze after all. Sand introduced by hard-soled shoes can scratch the glaze. If it is worn for a long time, it may even reveal mottled tire background color. Naturally influenced durable decorative effect. The emergence of polished vitrified tiles has solved the problem of exposed tires on the worn surface, but there are still scratches. Vitrified closed-cell surface becomes open-cell due to polishing process [0003] Gap. This brings about the problem that polished vitrified tiles are easily polluted. Contents of the invention [0004] Aiming at the shortcomings of the prior art, the invention provides a ceramic sanitary ware product and a preparation method thereof. [0005] In order to solve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/24C04B33/132C04B41/86
CPCY02P40/60
Inventor 邱陶松
Owner GUANGDONG TREND GROUP