Method for producing a multi-layered sliding bearing

A technology of sliding bearings and sliding layers, applied in the direction of connecting rod bearings, shafts and bearings, bearing components, etc., can solve the problems of violent reaction of dirt particles, breakage, fast wear, etc., achieve embedding and adaptability, improve Economical, and the effect of improving adhesion

Inactive Publication Date: 2013-04-10
MIBA GLEITLAGER GMBH
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A soft friction layer is characterized by its high embedment capacity with respect to dirt and foreign particles, but wears quickly or breaks down under very high loads
The hard friction layer is highly wear-resistant and can carry high loads, but reacts violently to dirt particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing a multi-layered sliding bearing
  • Method for producing a multi-layered sliding bearing
  • Method for producing a multi-layered sliding bearing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] First of all, it should be determined that in the different described embodiments, the same parts are provided with the same reference signs or the same component names, wherein the disclosure content contained in the entire description can be transferred to the parts with the same reference symbols according to the meaning. On the same part of the figure mark or the same component name. Positional indications selected in the description, such as top, bottom, side, etc., also refer to the directly described and illustrated figures and can be transferred to the new position according to the meaning in the event of a position change. Furthermore, individual features or combinations of features from the various exemplary embodiments shown and described can also represent independent solutions according to the invention.

[0034] figure 1 A first embodiment variant of a plain bearing 1 in the form of a plain bearing half shell is shown, which has a support element 2 or a b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for producing a multi-layered sliding bearing (1), according to which method at least one layer, in particular a sliding layer (3), is deposited on a surface of a substrate by a spraying method. The layer is produced from at least two different materials, wherein, in a first step, a first material (5) is sprayed onto the substrate only in at least one defined region (8), wherein regions of the substrate surface that are not intended to be coated by said material (5) are protected with a mask (6) against the deposition of the material (5) and wherein, in at least one second step, the further region(s) (9) is or are coated with at least one of the further materials by spraying.

Description

technical field [0001] The invention relates to a method for producing a multilayer sliding bearing and a sliding bearing comprising a support layer and a sliding layer, according to which method at least one layer, in particular a sliding layer, is deposited on a substrate surface of a substrate by a spraying method , in the sliding bearing the sliding layer is divided in one plane into at least two regions, these regions consist of a first material and a second material different from the first material. Background technique [0002] The friction layer of conventional sliding bearings is formed either by soft materials, such as lead, tin, bismuth, or by hard materials, such as alloys of copper, silver or nickel. A soft friction layer is characterized by its high embedding capacity for dirt and foreign particles, but wears quickly or breaks down under very high loads. Hard friction layers are highly wear-resistant and can carry high loads, but react violently to dirt parti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16C33/14F16C33/24
CPCB05B7/1486B05B7/205B05D5/08B05D2350/63B05B12/28C23C4/04C23C4/08C23C24/04C23C4/01F16C9/04F16C33/14F16C33/24F16C2223/42
Inventor G·莱奥纳尔代利
Owner MIBA GLEITLAGER GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap