Processing method of refractory gold ore

A treatment method and gold ore technology, which is applied in the field of refractory gold ore treatment, can solve problems such as unreasonable microbial compatibility, unfavorable industrial production, and poor gold leaching effect, and achieve the goal of improving crushing efficiency, reducing bondage, and increasing leaching rate Effect

Inactive Publication Date: 2013-05-01
徐希强
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A variety of microbial leaching metallurgical technologies have been disclosed in the prior art, but there are many shortcomings. For example, desulfurization, arsenic, and decarburization cannot be achieved at the same time, and often only one of them is available; the unreasonable compatibility of microorganisms leads to poor gold leaching effect ; The operation process is cumbersome, the energy consumption is high, and it is not conducive to industrial production, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A processing method for refractory gold ore, comprising the steps of:

[0028] The refractory gold ore is crushed by a crusher, then sent to a ball mill, and ground to a particle size of 200 mesh ore powder, wherein an activator is added to the ball mill, and the amount added is one thousandth of the mass of the gold ore; the activator is in accordance with Sodium silicate: kerosene is mixed at a mass ratio of 1:2; water is added to adjust the mineral powder concentration to 30% (w / v) ore slurry, and then hydrogen peroxide is added to the ore slurry, and stirred evenly, wherein hydrogen peroxide and ore The volume ratio of the slurry is 1:200.

[0029] Put the bacterial agent into the ore slurry, wherein the mass ratio of the bacterial agent to the ore slurry is 1:100; stir while feeding the air, the stirring speed is 200 rpm, and the amount of air per minute is 0.5m 3 / m 3 The ore slurry is subjected to microbial catalysis under the condition of 30° C., and the catal...

Embodiment 2

[0034] The gold mine selected as the material is a high-sulfur, high-arsenic and high-carbon gold mine in Shandong Province. The main metallic minerals are arsenopyrite and pyrite, and the main non-metallic minerals are quartz, graphite and carbon. The main element analysis results of the ore samples are shown in Table 1.

[0035] Table 1 Analysis of each element composition

[0036] the element

As

Fe

Cu

S

C

Au

K

Content%

12.6

21.3

0.04

16.1

6.9

0.0048

2.1

[0037] A processing method for refractory gold ore, comprising the steps of:

[0038] The refractory gold ore is crushed by a crusher, then sent to a ball mill, and ground to a particle size of 200 mesh ore powder, wherein an activator is added to the ball mill, and the amount added is one thousandth of the mass of the gold ore; the activator is in accordance with Sodium silicate: kerosene is mixed at a mass ratio of 1:2; water is added to ad...

Embodiment 3

[0049] Bacteria effect test:

[0050] Comparative test: divided into three control groups, specifically Control 1, Control 2, Control 3, and Example 2 of the present invention.

[0051] Control group 1: the bacterial agent is acidophilus Thiobacillus ferrooxidans and acidophilic sulfur bacteria according to the ratio of 1:1, the amount of sodium cyanide is 5kg / t, and the rest are the same as in Example 2; Control group 2: the microbial agent is Acidophilus Thiobacillus ferrooxidans, acidophilus Thiobacillus and Leptospira ferrooxidans were prepared according to the ratio of 1:1:1, the amount of sodium cyanide was 2kg / t, and the rest were the same as in Example 2; Control 3: no addition Hydrogen peroxide, the processing method is general embodiment 2. The desulfurization rate, arsenic removal rate, decarburization rate and gold leaching rate were obtained through detection, see Table 2.

[0052] Table 2

[0053] group

[0054] By comparison, it is found that the de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of gold ore resource dressing and particularly discloses a processing method of refractory gold ore. The method comprises the steps of smash homogenate, oxidation decarbonization, microorganism catalysis, cyanidation gold extraction and the like. The invention also discloses a microorganism microbial agent for processing refractory gold ore. When the method disclosed by the invention is utilized, sulfur, arsenic and carbon elements in the gold ore can be effectively removed, meanwhile, the leaching rate of gold elements is improved, and better application prospects are realized.

Description

technical field [0001] The invention belongs to the field of beneficiation of gold ore resources, and relates to a treatment method of refractory gold ore. Background technique [0002] Refractory gold ores are usually high-arsenic, high-sulfur, and high-carbon disseminated gold ores, which account for about two-thirds of the world's total gold ore resources and more than one-third in my country, mainly distributed in Shandong, Guizhou, Sichuan and Gansu and other provinces. This type of gold deposit has low grade, large scale, indistinct boundary between ore body and surrounding rock, gold is mainly wrapped in the ore in micro-submicroscopic form, it is difficult to be exposed, the leaching rate is low, and the comprehensive recovery rate is difficult . [0003] Various types of gold ore have different beneficiation methods due to their different properties, but gravity separation, flotation, amalgamation, cyanidation and the current resin slurry method, carbon slurry adso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B3/18C22B1/00C22B11/00
CPCY02P10/20
Inventor 徐希强李兆营
Owner 徐希强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com