Ink slab with grinding layer and preparing method thereof

A grinding layer and inkstone technology, which is applied in the direction of inkstands, printing, office supplies, etc., can solve the problems of limited product scope, limited raw materials, low practicability, etc., and achieve the goals of improving performance, fineness, and prolonging service life Effect

Inactive Publication Date: 2013-06-12
SHANGHAI WEIKAI CHEM
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the existing ceramic inkstone, its toughness is poor. When grinding ink, if there are impurities such as sand in the ink stick, sometimes there will be scratches and small pits visible to the naked eye; metal inkstones, such as copper inkstones, have a long history. However, due to corrosion and poor hardness, the practicability has always been low; stone inkstones, because the stone materials for making stone inkstones are carefully selected to make products, greatly limited the raw materials, thereby limiting the scope of application of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink slab with grinding layer and preparing method thereof
  • Ink slab with grinding layer and preparing method thereof
  • Ink slab with grinding layer and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment relates to an inkstone provided with a grinding layer. The inkstone in this embodiment is round or square, such as figure 1 , 2 , 3, and 4, the grinding area of ​​the inkstone 1 is the inkstone hall 2 of the inkstone, and the inkstone hall 2 includes a grinding layer and an inkstone hall matrix, and the grinding layer and the inkstone hall matrix are integrated, which increases firmness and prolongs the Product performance and lifespan.

[0036] This embodiment also relates to a method for preparing the aforementioned inkstone provided with an abrasive layer, comprising the following steps:

[0037] Step 1: preparing the grinding layer material;

[0038] Step 2: Prepare the matrix of the inkstone hall;

[0039] Step 3: Process the abrasive layer material on the surface of the inkstone base by thermal spraying or high-temperature firing to form an abrasive layer;

[0040] Step 4: Grinding the grinding layer.

[0041] In this embodiment, the abrasive ...

Embodiment 2

[0051] This embodiment relates to an inkstone provided with a grinding layer. The inkstone in this embodiment is round or square, such as figure 1 , 2 , 3, and 4, the grinding area of ​​the inkstone 1 is the inkstone hall 2 of the inkstone, and the inkstone hall 2 includes a grinding layer and an inkstone hall matrix, and the grinding layer and the inkstone hall matrix are integrated, which increases firmness and prolongs the Product performance and lifespan.

[0052] This embodiment also relates to a method for preparing the aforementioned inkstone provided with an abrasive layer, comprising the following steps:

[0053] Step 1: preparing the grinding layer material;

[0054] Step 2: Prepare the matrix of the inkstone hall;

[0055] Step 3: Process the abrasive layer material on the surface of the inkstone base by thermal spraying or high-temperature firing to form an abrasive layer;

[0056] Step 4: Grinding the grinding layer.

[0057] In this embodiment, the abrasive ...

Embodiment 3

[0067] This embodiment relates to an inkstone provided with a grinding layer. The inkstone in this embodiment is round or square, such as figure 1 , 2 , 3, and 4, the grinding area of ​​the inkstone 1 is the inkstone hall 2 of the inkstone, and the inkstone hall 2 includes a grinding layer and an inkstone hall matrix, and the grinding layer and the inkstone hall matrix are integrated, which increases firmness and prolongs the Product performance and lifespan.

[0068]This embodiment also relates to a method for preparing the aforementioned inkstone provided with an abrasive layer, comprising the following steps:

[0069] Step 1: Prepare grinding layer material;

[0070] Step 2: Prepare the matrix of the inkstone hall;

[0071] Step 3: Process the abrasive layer material on the surface of the inkstone base by thermal spraying or high-temperature firing to form an abrasive layer;

[0072] Step 4: Grinding the grinding layer.

[0073] In this embodiment, the abrasive layer i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an ink slab with a grinding layer and a preparing method thereof. A grinding area of the ink slab is arranged as an ink hall of the ink slab; the ink hall comprises an ink hall substrate and the grinding layer arranged on the ink hall substrate; and the grinding layer is integrated with the ink hall substrate. The invention also relates to the preparing method for the ink slab with the grinding layer. The preparing method comprises the following steps: 1, preparing a grinding layer material; 2, preparing the ink hall substrate; 3, adopting a hot-spraying method or high-temperature firing method for processing the grinding layer material on the surface of the ink hall substrate, thereby forming the grinding layer; and 4, polishing the grinding layer, thereby finishing the preparation. Aiming at the phenomena of abrasion, flaw, poor fineness and the like caused by long-term use of ceramic ink slabs, metal ink slabs, stone ink slabs and other ink slabs, a grinding layer structure made of the material different from the material of the ink hall substrate is additionally arranged to the ink slab, so that the ink slab has the advantages of long service life, good fineness, excellent toughness, high hardness, abrasion resistance, corrosion resistance, wide practical scope and better application prospect.

Description

technical field [0001] The invention relates to the field of stationery, in particular to an inkstone provided with a grinding layer and a preparation method thereof. Background technique [0002] Inkstone is a unique traditional Chinese writing and painting utensil. It has a history of thousands of years. In the continuous development and use, according to the material of inkstone, it can be divided into the following types, ceramic inkstone, stone inkstone, metal inkstone and so on. With a complete range of styles and a wide variety, it is one of the indispensable main appliances in the "Four Treasures of the Study" and complete sets of stationery. [0003] Modern Western cultural items can be used conveniently, such as fountain pens and ballpoint pens, which have been widely popularized. Traditional Chinese inkstones have been greatly impacted, greatly reducing the scope and number of people used, and gradually withdrawing from the field of daily use. [0004] Existing i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B43L27/00
Inventor 李佩正
Owner SHANGHAI WEIKAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap