Anacardol glycidyl ether modified aliphatic amine hardener and preparation method thereof

A technology of glycidyl ether and cardanol, which is applied in chemical instruments and methods, preparation of organic compounds, preparation of amino hydroxyl compounds, etc., can solve problems such as unfriendly environment, high requirements for construction environment, and impact on workers' health, so as to reduce toxicity And volatility, improve the effect of paint film whitening

Inactive Publication Date: 2013-06-12
上海美东生物材料股份有限公司
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of cardanol glycidyl ether modified fatty amine curing agent, described this cardanol glycidyl ether modified fatty amine curing agent will solve the aliphatic polyamine curing epoxy resin in the prior art High requirements on the construction environment, prone to paint film diseases, affecting the health of workers and technical problems that are not friendly to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anacardol glycidyl ether modified aliphatic amine hardener and preparation method thereof
  • Anacardol glycidyl ether modified aliphatic amine hardener and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Add 30 parts of triethylenetetramine into the reaction kettle according to parts by weight, and slowly add 70 parts of cardanol glycidyl ether dropwise at 60°C under the stirring condition of 600 to 800 rpm. Disperse for 3-4 hours to obtain the final product.

[0016] The listening plate is polished with sandpaper, cleaned with xylene solvent, degreased and degreased, and dried.

Embodiment 2

[0018] Add 40 parts of tetraethylenepentamine into the reaction kettle according to parts by weight, and slowly add 60 parts of cardanol glycidyl ether dropwise at 60°C under stirring conditions of 600 to 800 revolutions per minute. After 2 hours of dropping, stir Disperse for 3-4 hours to obtain the final product.

[0019] The listening plate is polished with sandpaper, cleaned with xylene solvent, degreased and degreased, and dried.

Embodiment 3

[0021] Preparation of cardanol glycidyl ether modified fatty amine curing agent: Add 20 parts of tetraethylenepentamine into the reaction kettle according to the weight part, and slowly add 80 parts of The cardanol glycidyl ether was added dropwise for 2 hours, and stirred and dispersed for 3 to 4 hours to obtain the final product.

[0022] The listening plate is polished with sandpaper, cleaned with xylene solvent, degreased and degreased, and dried.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
amine valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses anacardol glycidyl ether modified aliphatic amine hardener which is synthesized by anacardol glycidyl ether and aliphatic amine, wherein the weight ratio of the anacardol glycidyl ether to the aliphatic amine is 80:60-20:40. The invention further provides a preparation method of the anacardol glycidyl ether modified aliphatic amine hardener. According to the preparation method of the anacardol glycidyl ether modified aliphatic amine hardener, the the anacardol glycidyl ether and the aliphatic amine are obtained according to the weight percentage, and then the aliphatic amine is put into a reaction still and is heated to the temperature of 55-70 DEG C, the anacardol glycidyl ether is added into the reaction still for 1-3 hours under the stirring condition of 600-800 circles / minute, and stirring and reaction are carried out for 3-4 hours, and finally the anacardol glycidyl ether modified aliphatic amine hardener is obtained. Due to the fact that the modified aliphatic amine hardener is hardener with middle and normal temperature, toxicity and volatility of the low-aliphatic amine can be effectively reduced, and various diseases, such as oil face, albefaction and darkening of film, which easily occur in an epoxy construction process can be avoided at the same time.

Description

Technical field: [0001] The invention relates to the field of organic chemistry, in particular to an epoxy resin curing agent, in particular to a cardanol glycidyl ether modified fatty amine curing agent and a preparation method thereof. Background technique: [0002] All polymer compounds containing epoxy groups in their molecular structure are collectively referred to as epoxy resins. The cured epoxy resin has good physical and chemical properties. It has excellent bonding strength to the surface of metal and non-metal materials, good dielectric properties, small shrinkage rate, good dimensional stability and high hardness. It has good flexibility and is stable to alkali and most solvents, so it is widely used in various sectors of national defense and national economy for casting, impregnating, laminating, adhesive, coating and other purposes. [0003] Aliphatic polyamines can be cured with epoxy resin at room temperature, with fast curing speed and low viscosity. They c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/64C07C213/04C07C217/30
Inventor 黎明沈文俊
Owner 上海美东生物材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap