Lustering preparation for glass, ceramic and porcelain decoration and application thereof

A glossy and ceramic technology, applied in the field of glossy preparations and surface glossy preparations, can solve the problems of inability to improve the similarity between the appearance of the film and the gold

Active Publication Date: 2013-06-19
SHENZHEN YONGFENGYUAN PORCELAIN
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, continuing to increase the gold content beyond a specific content does not improve the similarity of the appearance of the baked film to gold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lustering preparation for glass, ceramic and porcelain decoration and application thereof
  • Lustering preparation for glass, ceramic and porcelain decoration and application thereof
  • Lustering preparation for glass, ceramic and porcelain decoration and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040]

[0041] The components prepared according to the ratio given in Example 1 have relatively high viscosity, and are more suitable for use in silk screen brushing to make ceramic decals. In the spraying or brushing process, components with lower viscosity are required, so it is necessary to use toluene, xylene or other suitable solvents to half-dilute the components of Example 1 according to the weight ratio,

[0042] Concrete composition in the embodiment 1 component is as follows:

[0043] Organic hydrocarbon solution toluene.

[0044]

[0045]

[0046]

[0047] Generally, toluene and turpentine are preferred as solvents. The choice of plasticizer must be suitable for the specific field and practical conditions. Solvents and resins form a paste, and solvents and resins are added to adjust the viscosity requirements of specific applications. Generally, according to the prior art, compositions in the range of 300-2500 mPas are suitable for screen printing app...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lustering preparation for glass, ceramic and porcelain decoration and application thereof. The lustering preparation comprises an iron metal organic compound dissolved in solvent, a cobalt metal organic compound dissolved in the solvent, a chromium metal organic compound dissolved in the solvent and a basic metal fluxing agent dissolved in the solvent, wherein the weight ratio of the iron metal to the chromium metal is (1:1)-(12:1); the sum of the iron, the chromium and the cobalt at least accounts for 1wt% of the components; and the basic metal fluxing agent has a such a content that all the iron, chromium and cobalt can be molten. According to the invention, the components of the lustering preparation do not include gold metal, but decoration effect very similar to the appearance of gold can be achieved by selecting an appropriate mixture of iron, chromium, cobalt and fluxing agent, thus greatly saving the cost of a decoration preparation.

Description

technical field [0001] The invention relates to the field of surface gloss preparations, in particular to a gloss preparation that can be used to decorate the surfaces of glass, pottery and porcelain. Background technique [0002] Gloss preparations for glass, ceramics, and porcelain decoration are usually organometallic compound solutions in an organic carrier medium, and the organic carrier is fully burned and volatilized during the baking process. After baking, gloss formulations form a layer of shiny, colorful and iridescent metal oxides on the decorated substrate. The gloss preparation itself exhibits an extremely high gloss on the glaze. Their film thickness is only 10 -4 - 10 -5 mm, is of the same order of magnitude as the wavelength, and since it has a different refractive index than the substrate being decorated, most gloss formulations appear iridescent white or silver. [0003] The production of colored luster preparations can use compounds of transition met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine