Special material for regenerating and modifying heel by recycling ABS plastic housing of household appliance and preparation method of special material

A technology for ABS plastics and plastic shells, which is applied in the field of reclaimed ABS home appliance plastic shells for regenerated modified shoe heels and its preparation, can solve the problems of waste of resources, failure of home appliance ABS plastic shells to be recycled, etc., to reduce raw material costs, reduce Effects on product cost, guaranteed efficiency and quality

Active Publication Date: 2014-06-25
四川塑金科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a reclaimed ABS home appliance plastic shell regeneration modified shoe heel special material and its preparation method, to solve the problem that the home appliance ABS plastic shell has not been recycled and waste resources in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Recycled ABS home appliance plastic shell recycled modified shoe heel material, by weight, is composed of 100 parts of home appliance ABS plastic shell crushed material, 15 parts of high-grade rubber powder, 0.15 part of calcium stearate, 0.15 part of EBS, and 0.3 part of toner.

[0028] The specific preparation method is as follows:

[0029] First of all, the recovered home appliance ABS plastic shell is crushed, cleaned, rinsed, dried, and labeled to obtain the home appliance ABS plastic shell crushed material.

[0030] Then the home appliance ABS plastic shell crushing material and high rubber powder are added into the high mixer according to the above parts by weight, and mixed for 1.5min at a medium speed; then the EBS, calcium stearate and Toner, mixed at a medium speed for 2 minutes to obtain a premix; add the premix to a twin-screw extruder to heat, melt, extrude and plasticize to obtain a semi-finished product. The working conditions are: the temperature is kep...

Embodiment 2

[0033] The difference between this embodiment and Example 1 is that the parts by weight of each component are different, and the parts by weight of each component in this embodiment are as follows:

[0034] 100 parts of home appliance ABS plastic shell crushing material, 20 parts of high rubber powder, 1 part of calcium stearate, 1 part of EBS, 0.5 parts of color powder.

Embodiment 3

[0036] The difference between this embodiment and Example 1 is that the parts by weight of each component are different, and the parts by weight of each component in this embodiment are as follows:

[0037] 100 parts of home appliance ABS plastic shell crushing material, 5 parts of high-grade rubber powder, 0.1 part of calcium stearate, 0.1 part of EBS, 0.1 part of toner.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a special material for regenerating and modifying a heel by recycling an ABS (Acrylonitrile Butadiene Styrene) plastic housing of a household appliance and a preparation method of the special material in order to solve the problem that a resource is wasted due to the fact that an ABS plastic housing of a household appliance is not recycled in the prior art. The special material comprises the following components in parts by weight: 100 parts of broken material of the ABS plastic housing of the household appliance, 5-20 parts of ABS, 0.1-1 part of calcium stearate, 0.1-1 part of EBS (Ethylene Bis Stearamide) and 0.1-0.5 parts of toner, wherein the broken material of the ABS plastic housing of the household appliance is obtained by breaking, cleaning, rinsing and drying the recycled ABS plastic housing of the household appliance and sucking a label of the recycled ABS plastic housing. The invention further provides the preparation method of the special material for regenerating and modifying the heel by recycling the ABS plastic housing of the household appliance. The special material and the preparation method can effectively recycle the ABS plastic housing of the household appliance, and have the advantages of resource saving, environmental protection, cost reduction, preparation process simplification and the like.

Description

technical field [0001] The invention specifically relates to a special material for regeneration and modification of heels of recycled ABS home appliance plastic shells and a preparation method thereof. Background technique [0002] At present, the main common heel material in the market is polyurethane plastic (PU). Most of the heels of women’s high-heeled shoes are mainly new material ABS, which is expensive and has a single color. When the color requirements are diversified, the price of using modified ABS is even higher. Thereby the economic burden of consumers is increased, and at the same time, the ABS plastic shells of home appliances are not fully recycled, resulting in a waste of resources. Contents of the invention [0003] The purpose of the present invention is to provide a regenerated and modified special material for heels of recycled ABS home appliance plastic shells and a preparation method thereof, so as to solve the problem in the prior art that the ABS ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08K5/098A43B21/20B29C47/92B29C48/92
Inventor 乔江浩陈道明
Owner 四川塑金科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap