Complex-calcium-based tetrapolyurea lubricating grease and preparation method thereof
A technology of calcium-based tetrapolyurea grease and composite calcium-based grease, which is applied in lubricating compositions, petroleum industry, thickeners, etc., can solve the problems of poor comprehensive performance of calcium-based polyurea grease, and achieve excellent Comprehensive performance, overcoming hardening, and avoiding the effect of strong volatilization
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0018] The invention provides a preparation method of composite calcium-based tetrapolyurea grease, the method comprising the following steps:
[0019] (1) In the presence of lubricating base oil, contact and react calcium hydroxide, higher fatty acids and dibasic aromatic acids, heat up and dehydrate the mixture obtained after the reaction, and then cool down to 70-80°C to obtain complex calcium-based grease ;
[0020] (2) Add diisocyanate and diamine in sequence to the complex calcium-based grease, add monoamine after mixing and contacting for at least 5 minutes, heat up to 100-120°C for contact reaction, and heat up the mixture obtained after the reaction to refine , wherein the molar ratio of the amount of diisocyanate, diamine and monoamine is (1.9-2.1): 1: (1.9-2.1).
[0021] According to the method of the present invention, in step (1), the lubricating grease obtained after dehydration is cooled to 70-80° C., and in step (2), monoamine is added after adding diisocyanat...
Embodiment 1
[0055] This example is used to illustrate the complex calcium-based tetrapolyurea grease of the present invention and its preparation method.
[0056] Raw material components: naphthenic oil (purchased from China National Offshore Oil Corporation, viscosity at 100°C is 12mm 2 / s): 835g; Terephthalic acid: 30g; Ca(OH) 2 : 22g; 12-hydroxystearic acid (purchased from Tongliao Weining Chemical Co., Ltd.): 60g; octadecylamine (purchased from ACROS): 31.87g; ethylenediamine: 3.56g; Phenylmethane diisocyanate (MDI): 29.58g; Tungsten disulfide: 8g; Selenium disulfide: 12g; Graphite fluoride: 10g; Diisooctyldiphenylamine: 8g; Zinc naphthenate: 10g.
[0057] Mix 500g of naphthenic oil with 60g of 12-hydroxystearic acid and 30g of terephthalic acid, stir evenly, raise the temperature to 80°C, add dropwise a milk of lime solution containing 22g of calcium hydroxide, stir and saponify quickly for 60 minutes, Raise the temperature to 105°C, and after dehydration, cool down to 80°C to obta...
Embodiment 2
[0067] This example is used to illustrate the complex calcium-based tetrapolyurea grease of the present invention and its preparation method.
[0068] Composite calcium-based tetrapolyurea grease was prepared according to the method of Example 1, except that terephthalic acid was replaced with the same molar amount of isophthalic acid to obtain composite calcium-based tetrapolyurea grease.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com