A decorative board and fluorocarbon technology, applied in the field of decorative materials, can solve the problems of difficult construction, poor pigment dispersion, and poor light resistance, and achieve the effects of easy renovation, excellent light resistance, and easy operation

Inactive Publication Date: 2013-08-21
霍志明
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the extremely high liquefaction temperature required during use, the dispersion of pigments is poor, so it has only been used in non-stick pans, medical, aviation and other fields, and has not entered the construction field.
[0003] However, the application of fluorocarbon coatings in building decoration materials has never been involved. Traditional paints and coatings have poor light resistance, low weather resistance, relatively difficult construction, and heavy weight, which is a greater burden on the overall board.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV fluorocarbon decorating plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0014] see figure 1 , the embodiment of the present invention includes:

[0015] A UV fluorocarbon decorative board, comprising: a substrate 1, the surface of which is coated with a UV putty layer 2.

[0016] At least two layers of fluorocarbon paint layers 3 are rolled on the UV putty layer 2, and a topcoat layer 4 is coated on the surface of the roller coating, and the topcoat can be used as a finish according to requirements.

[0017] The base plate 1 is a cement fiber board or a composite insulation board, and the structure of the present invention is suitable for application to base plates 1 of various materials.

[0018] This is to use th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a UV fluorocarbon decorating plate which comprises a base plate. A UV putty layer is coated on the surface of the base plate, at least two layers of fluorocarbon paint layers are rolled and coated on the UV putty layer, finish paint layers are coated on the surfaces of the rolled coated layers, and the base plate is fixedly connected with an outer wall face. By means of the method, the UV fluorocarbon decorating plate has excellent light resistance and weather resistance, is simple to operate and easy to refinish, cannot be limited by building shapes, can enable designers to fully imagine, is low in construction cost and light in weight, avoids bringing burden to a wall body and has no risk of falling.

Description

technical field [0001] The invention relates to the field of decorative materials, in particular to a UV fluorocarbon decorative board. Background technique [0002] The earliest "fluorocarbon coating" was actually born as early as 1938. It is the well-known DuPont Teflon coating, that is, polytetrafluoroethylene (PTFE), polyperfluoropropylene (FEP) and other copolymers. This kind of material is known as "corrosion-resistant, non-stick Teflon" due to its unique and excellent heat resistance (180°C-260°C), low temperature resistance (-200°C), self-lubrication and chemical stability. , Fluorocarbon paint is generally divided into trifluoro and tetrafluoro, tetrafluoro anti-corrosion performance is higher. Due to the extremely high liquefaction temperature required for use, the dispersion of pigments is poor, so it has only been used in non-stick pans, medical, aviation and other fields, and has not entered the construction field. [0003] However, the application of fluoroca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04F13/077
Inventor 霍志明
Owner 霍志明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap