Highlight anodizing process of aluminum product

A technology for aluminum products and processes, applied in the field of high-gloss anode technology for aluminum products, can solve problems such as high cost and small processing area, and achieve the effect of improving decorative effects and enriching colors.

Active Publication Date: 2013-09-04
KUNSHAN ESON PRECISION ENGINEERING CO LTD
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are few high-gloss anode products for aluminum alloy products on the market. Most of the high-gloss effects need to be done after the anode with a high-gloss drilling and cutting machine, and the processing area is small and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A high-gloss anode process for aluminum products, comprising the following steps:

[0025] Step 1): Grinding the surface of the aluminum product with a 600# abrasive belt;

[0026] Step 2): Use a 600# nylon wheel to polish the surface of the aluminum product;

[0027] Step 3): Use a sackcloth wheel with green wax for initial polishing;

[0028] Step 4): Use a cloth wheel with white wax for fine polishing;

[0029] Step 5): anode reaction;

[0030] The anode reaction specifically includes the following steps: a. wax removal; b. polishing and neutralization; c. oxidation; d. dyeing;

[0031] a Wax removal: add wax removal water into the wax removal tank, turn on the air to stir, heat up to 55°C and fully dissolve, fix the aluminum product on the hanger, immerse the hanger with the aluminum product in the wax remover tank for 1 minute, and then take it out Enter the washing tank for washing;

[0032] B chemical throwing, neutralization:

[0033] Chemical polishing: a...

Embodiment 2

[0042] Aluminum products were processed according to the same process as in Example 1, except that step 5): anodic reaction:

[0043] a Dewaxing: Add dewaxing water into the dewaxing tank, turn on the air and stir, heat up to 50°C and fully dissolve, then fix the aluminum product on the hanger, immerse the hanger with the aluminum product in the dewaxer tank for 2 minutes, and then take it out Enter the washing tank for washing;

[0044] B chemical throwing, neutralization:

[0045] Chemical polishing: add chemical polishing agent into the chemical polishing tank, turn on the air stirring, and heat up to 105°C; immerse the aluminum product in the chemical polishing tank to react for 60 seconds, then take it out and wash it in the washing tank; the chemical polishing agent is 85 % phosphoric acid, and 160 ml / L of 98% sulfuric acid mixed solution;

[0046] Neutralization: Then add a nitric acid solution with a nitric acid concentration of 260g / L into the neutralization tank; i...

Embodiment 3

[0051] Aluminum products were processed according to the same process as in Example 1, except that step 5): anodic reaction:

[0052] a Dewaxing: Add dewaxing water into the dewaxing tank, turn on the air to stir, heat up to 60°C and fully dissolve, fix the aluminum product to the hanger, immerse the hanger with the aluminum product in the dewax tank for 1.5min, then Take it out and wash it in the washing tank;

[0053] B chemical throwing, neutralization:

[0054] Chemical polishing: add chemical polishing agent into the chemical polishing tank, turn on the air stirring, and raise the temperature to 120°C; immerse the aluminum product in the chemical polishing tank to react for 20 seconds, then take it out and wash it in the washing tank; the chemical polishing agent is 85 % phosphoric acid, and 140 ml / L of 98% sulfuric acid mixed solution;

[0055] Neutralization: Then add a nitric acid solution with a nitric acid concentration of 300g / L into the neutralization tank; immer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a highlight anodizing process of an aluminum product. The process comprises the following steps of: grinding and processing the surface of the aluminum product by using a sanding belt; grinding and processing the surface of the aluminum product by using a nylon wheel; carrying out primary polishing by using a linen wheel and green polishing wax in combination; carrying out light polishing by using a cloth wheel and white polishing wax in combination; carrying out an anodic reaction; carrying out wax removal, chemical polishing, neutralization, oxidization, dyeing and hole sealing; carrying out light polishing by using a polishing machine, a consumable cloth wheel and white polishing wax in combination; and carrying out a wiping inspection on the surface of the aluminum product. According to the highlight anodizing process of the aluminum product disclosed by the invention, the physical polishing and the chemical polishing are combined, chemical polishing agents in specific proportions are used, a large-area anode highlight effect can be achieved, a highlight surface processing effect after the aluminum product is anodized is achieved, the aluminum product can be dyed with rich colors, and the provided aluminum product surface processing process is suitable for large-scale industrial production.

Description

technical field [0001] The invention relates to a high-gloss anode process for aluminum products, which belongs to the technical field of aluminum product processing. Background technique [0002] At present, there are few high-gloss anode products for aluminum alloy products on the market. Most of the high-gloss effects need to be processed after the anode with a high-gloss drilling and cutting machine, and the processing area is small and the cost is high. Contents of the invention [0003] Purpose: In order to overcome the deficiencies in the prior art, the present invention provides a high-gloss anode process for aluminum products. [0004] Technical solution: In order to solve the above-mentioned technical problems, the technical solution adopted in the present invention is: [0005] A high-gloss anode process for aluminum products, characterized in that it includes the following steps: [0006] Step 1): Grinding the surface of the aluminum product with an abrasive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/16C25D11/18C23F3/03B24B21/00B24B37/00
Inventor 蔡佳桦
Owner KUNSHAN ESON PRECISION ENGINEERING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com