Ink painting method for porcelain surface in red glaze

A technology of scarlet and ink, which is applied in the field of glazed painting of scarlet ceramics, can solve the problems of inactive chemical reactions and ineffective effects, and achieve a smooth surface effect

Inactive Publication Date: 2013-09-18
长沙锦东瓷业有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] One is that the bright red glaze contains sulfur and selenium that are active at high temperatures, while the toner mainly contains carbon, and the chemical reaction is not active. However, after a high tem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1) Select a bone china happiness bottle body with a size of 25*31, remove the stains and dust on the surface with clean water, and dry it at 100 degrees Celsius before use.

[0026] 2) The porcelain surface of the bone china happiness bottle body is made of red glaze and fired at a high temperature of 1050-1150 degrees, and the preliminary color is observed to make a semi-finished product wrapped with red glaze;

[0027] 3) Color ink source: Japan Izawa pigment

[0028] Model: 66704

[0029] Preparation of basic color ink: Beef glue, color ink and water are prepared according to the mass ratio of 2:1:3. The temperature of the water is 60 degrees Celsius. Serve in hours.

[0030] 4) Oil blending

[0031] Source of frankincense oil: No. 108-5, Xindu Ceramics Private Park, Jingdezhen City, Jiangxi Province

[0032] Camphor oil source: Jingdezhen, Jiangxi

[0033] Stir frankincense oil and camphor oil at a volume ratio of 1:1 for 30 minutes to make oil.

[0034] 5) Pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ink painting method for a porcelain surface in a red glaze. The ink painting method comprises the steps of: 1) selecting, cleaning and baking a bone China body; 2) firing the bone China body to prepare a semi-finished product coated by the red glaze at high temperature of 1050-1150 DEG C by adopting the red glaze; 3) blending gelatin, ink and water according to the mass ratio of 2:1:3; soaking the ink and the gelatin for 60 minutes when the temperature of the water is 60 DEG C, grinding for 30 minutes, and storing for 24 hours to prepare basic ink; 4) agitating olibanum oil with camphorated oil according to the volume ratio of 1:1 for 30 minutes to prepare oil; 5) drawing the outline of landscape on the semi-finished product by the basic ink, achieving gradation through adding amount of the oil; and 6) baking the semi-finished product of the drawn pattern at 40 DEG C for 10 minutes after finishing the pattern, heating to 80-100 DEG C to bake for 40 minutes, and then putting into an electrical kiln at 1050-1250 DEG C to fire for 3 hours, carrying out heat preservation for 50 minutes, and naturally cooling to room temperature.

Description

technical field [0001] The invention belongs to a method for painting glazed surfaces of bright red ceramics, and in particular relates to an ink method for porcelain surfaces in bright red glazes. Background technique [0002] Red symbolizes joy and auspiciousness, and is the favorite color of the Chinese nation. For thousands of years, people have always had a puzzled complex with red porcelain. From the ancient crock bean red, Jihong, Langhong, etc., all the way to today's Chinese red, because red is difficult to blend with other colors, it is prone to discoloration after being fired in a kiln, so a small area of ​​other colors is usually used to blend with it. Especially under the in-glaze process, if the same color of pigment is used in a large area, problems such as foaming will easily occur after the pigment penetrates into the glaze layer and cools down. In recent years, researchers have been devoted to the careful study of this project. [0003] The in-glaze proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 傅涛王伟生龙辉
Owner 长沙锦东瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap