Three-dimensional linen bronze printing technology

A linen, three-dimensional technology, applied in the field of three-dimensional gold printing technology on linen, can solve the problems of dull gold powder layer, easy penetration of glue, poor adhesion of metal powder, etc., achieves good gloss and metallic feeling, improves visual effect, and is not easy to fall off. Effect

Active Publication Date: 2015-07-15
浙江赛芙纺织品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional gold printing process on the surface of the fabric is as recorded in the invention patent of CN 102729913 A: it is mainly to apply glue on the surface of the fabric through a screen plate, and then sprinkle metal powder on the glue to remove excess metal powder. The metal luster gold powder layer has the following defects: 1. The three-dimensional effect of the pattern is not good; 2. The distribution uniformity of the metal powder is not good, the luster of the gold powder layer is dull, and the amount of metal powder is large, and there is more waste; 3. The adhesion of the powder is poor and it is easy to fall off; 4. The glue is easy to penetrate into the fabric, which affects the fabric feel. 5. After pressing, white glue dots are easy to appear on the surface of the metal powder, resulting in large appearance defects in the gold powder layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-dimensional linen bronze printing technology
  • Three-dimensional linen bronze printing technology
  • Three-dimensional linen bronze printing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A three-dimensional gold printing process on linen, comprising the steps of:

[0027] ① Make a screen printing screen according to the designed pattern, and the screen mesh of the screen printing screen is 60 mesh.

[0028] ②Fix the linen, use screen printing technology to transfer the foam paste (commercially available, printing foam paste, produced by Jiangshan Gangqi Printing Material Co., Ltd.) to the linen 1 through the screen printing screen produced in step ①, and send The foam paste is transferred to the linen 1 to form a foam coating, which is dried naturally for 10 minutes, and then the metal powder slurry is transferred to the foam coating through the screen printing screen prepared in step ① to form a metal powder coating. The composition is 10 parts by weight of 800-mesh copper powder (commercially available), 90 parts by weight of white latex (commercially available), and the two are mixed evenly to prepare a metal powder slurry.

[0029] ③Send the linen ...

Embodiment 2

[0032] A three-dimensional gold printing process on linen, comprising the steps of:

[0033] ① Make a screen printing screen according to the designed pattern, and the screen mesh of the screen printing screen is 100 mesh.

[0034] ②Fix the linen, use screen printing technology to transfer the foam paste (commercially available, printing foam paste, produced by Jiangshan Gangqi Printing Material Co., Ltd.) to the linen 1 through the screen printing screen produced in step ①, and send After the foam slurry is transferred to the linen 1, a foam coating is formed, which is dried naturally for 15 minutes, and then the metal powder slurry is transferred to the foam coating through the screen printing screen prepared in step ① to form a metal powder coating. The composition is 15 parts by weight of 1000 mesh aluminum powder, 95 parts by weight of white latex, and the two are evenly mixed to form a metal powder slurry.

[0035] ③Send the linen obtained in step ② into a high-temperat...

Embodiment 3

[0038] A three-dimensional gold printing process on linen, comprising the steps of:

[0039] ① Make a screen printing screen according to the designed pattern, and the screen mesh of the screen printing screen is 80 mesh.

[0040] ②Fix the linen, use screen printing technology to transfer the foam paste (commercially available, printing foam paste, produced by Jiangshan Gangqi Printing Material Co., Ltd.) to the linen 1 through the screen printing screen produced in step ①, and send After the foam slurry is transferred to the linen 1, a foam coating is formed, and it is naturally dried for 12 minutes, and then the metal powder slurry is transferred to the foam coating through the screen printing screen prepared in step ① to form a metal powder coating, and the metal powder slurry The composition is 12 parts by weight of 900 mesh copper powder, 93 parts by weight of white latex, and 5 parts by weight of defoamer (commercially available, silicone emulsion defoamer JY-930, Jiangs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a three-dimensional linen bronze printing technology which comprises the steps that (1), a silk screen printing plate is manufactured according to a designed flower type pattern; (2), linen is fixed, foaming slurry is transferred to the linen by the silk screen printing plate manufactured in Step (1) by a silk screen printing technology, a foaming coating layer is formed after the foaming slurry is transferred to the linen, and is dried naturally for 10-15min, and metal powder slurry is transferred to the foaming coating layer by the silk screen printing plate manufactured in Step (1) to form a metal powder coating layer; and (3), the linen treated in Step (2) is sent into a high temperature setting machine for high temperature foaming and allowing the foaming coating layer to expand at a high temperature to form a foaming layer with a three-dimensional pattern, and the metal powder coating layer is solidified and attached to the foaming layer by the high temperature to form a gold power layer. According to the three-dimensional linen bronze printing technology, metal powder can be printed on the surface of the linen, is less in use quantity, and is distributed uniformly; the formed gold power layer is good in glossiness and metallic sense; the adhesive force of the metal powder is good, so that the metal powder does not fall off easily; and a three-dimensional effect of the bronze printing pattern can be improved.

Description

technical field [0001] The invention relates to the technical field of fabric surface printing, in particular to a three-dimensional gold printing process on linen. Background technique [0002] The gold printing process refers to the technology of printing metal powder on the fabric, which can enhance the luster and metallic feeling of the fabric, and is widely used. At present, the use of gold printing technology has become an important process to increase the visual effect and grade of clothing fabrics, curtain fabrics, sofa fabrics and various high-end fabrics. [0003] The traditional gold printing process on the surface of the fabric is as recorded in the invention patent of CN 102729913 A: it is mainly to apply glue on the surface of the fabric through a screen plate, and then sprinkle metal powder on the glue to remove excess metal powder. The metal luster gold powder layer has the following defects: 1. The three-dimensional effect of the pattern is not good; 2. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41M1/12B41M1/22B41M1/26
Inventor 鲁金州
Owner 浙江赛芙纺织品有限公司