Method for casting box-type complex water-cooling exhaust pipe by using iron mold coated sand

A technology for iron mold sand-covered casting and exhaust pipe, which is applied in casting molding equipment, casting molds, cores, etc. to achieve the effects of high tensile strength, stable and reliable quality, and broad prospects for popularization and use.

Active Publication Date: 2015-04-08
GUANGXI YUCHAI MACHINE PARTS MFG CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a method for casting box-type complex water-cooled exhaust pipes with sand-covered iron molds to solve the microscopic loose defects, improve the surface quality and internal cleanliness of castings, and the overall mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] The iron mold sand-covered casting process of water-cooled exhaust pipe is different from the previous sand casting process in the molding process and process design. Water-cooled exhaust pipe iron mold sand-covered molding is to choose different types of sand-coated molding machines according to the shape and size of the product. For example, the water-cooled exhaust pipe MKJ and 6CA we produce are three shorter exhaust pipe products. The XTF-Z-1350*740 molding machine is selected, while the T9000 water-cooled exhaust pipe with a length of 1236mm is selected from the XTF-Z-2000*740 molding machine. According to the requirements of iron type specifications, the water-cooled exhaust pipe is generally designed and arranged as 2 pieces / type, divided into upper and lower molds, and the two ends are reversed, and the two products are symmetrical and consistent. A special design is made for the exhaust design of the core head position. For water-cooled exhaust pipes with a l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A method for casting a box-type complex water-cooling exhaust pipe by using an iron mold coated sand is disclosed. By using the water-free coated sand mold, the method helps to realize rapid cooling and mold filling, eliminate the defects of nail-passing-hole structure loosening and casting deformation often happening in the water-cooling exhaust pipe; and the prepared water-cooling exhaust pipe has higher tensile strength, higher hardness, better graphite morphology and better graphite grade, and the amount of stable pearlites is 98% or more. The yield of castings is improved from 54% to 96% or more. The finished product is good in texture compactness, good in texture refining capability, good in surface quality, and stable and reliable in quality. Also, during the production, the method has the advantages of being small in use level of the sand and paints, small in equipment investment, small in equipment occupied area, high in production efficiency, low in manufacture cost, good in environmental protection property, wide in prospect, and applicable to production of various engine exhaust pipes with high quality demands and complex thin-wall double-layer walls.

Description

technical field [0001] The invention belongs to a casting process for a box-type complex thin-walled water-cooled exhaust pipe of an engine, in particular to a method for casting a box-type complex water-cooled exhaust pipe with iron molds covered with sand. Background technique [0002] Iron mold sand-covered casting water-cooled exhaust pipe is a product with complex internal structure, thin casting wall (5mm) and uniform requirements. [0003] Domestically and even internationally, most of the applied research on iron mold sand-covered casting is used in the production of crankshafts or important castings. However, the use of iron mold casting technology to produce castings with complex structures and thin wall thickness requirements, such as water-cooled exhaust pipe castings, is still blank at present. [0004] Due to the higher and higher requirements for automobile emission and noise, the technical requirements for exhaust pipes of various automobile manufacturers ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C9/26
Inventor 李文彬
Owner GUANGXI YUCHAI MACHINE PARTS MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products