Two-liquid mixed type organopolysiloxane composition

A technology of polysiloxane and silane compounds, which is applied in the direction of adhesive additives, non-polymer adhesive additives, and other chemical processes, and can solve problems such as the position of the pasting substrate cannot be adjusted finely, and the bonding time is short. , to achieve the effect of good deep curing and long bonding time

Active Publication Date: 2017-05-24
SHIN ETSU CHEM IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the rapid curing property of this composition is indeed greatly improved, but because the curing after mixing is too fast, there are disadvantages such as a short potable time for bonding, and the position cannot be finely adjusted after the substrate is pasted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-liquid mixed type organopolysiloxane composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0100] A reaction product of 2-ethylhexyl acrylate and dimethoxymethylsilane was added to 100 parts by mass of polydimethylsiloxane with a viscosity of 20,000 mPa·s at the end end-blocked with silanol groups ( Product name: OCMS-2, manufactured by Shin-Etsu Chemical Co., Ltd.) 3 parts by mass, 1,1,3,3-tetramethyl-2-[3-(trimethoxysilyl)propyl]guanidine 0.6 mass After the reaction, add 1 part by mass of methyltrimethoxysilane partial hydrolysis condensate (trade name: KC-89E, manufactured by Shin-Etsu Chemical Co., Ltd.), 1 part by mass of vinyltrimethoxysilane Parts were mixed completely under reduced pressure to obtain the first composition.

[0101] In addition, 2 parts by mass of ethyl acetoacetate and 0.2 parts by mass of dioctyltin ditertiary carboxylate were added to 100 parts by mass of polydimethylsiloxane terminated with silanol groups at the end with a viscosity of 20,000 mPa·s at 25°C. , mixed with a mixer to obtain the second composition.

[0102] Sample 1 was obt...

Embodiment 2

[0104] A reaction product of 2-ethylhexyl acrylate and dimethoxymethylsilane was added to 100 parts by mass of polydimethylsiloxane with a viscosity of 20,000 mPa·s at the end end-blocked with silanol groups ( Product name: OCMS-2, manufactured by Shin-Etsu Chemical Co., Ltd.) 3 parts by mass, 1,1,3,3-tetramethyl-2-[3-(trimethoxysilyl)propyl]guanidine 0.6 mass After the reaction, add 1 part by mass of methyltrimethoxysilane partial hydrolysis condensate (trade name: KC-89E, manufactured by Shin-Etsu Chemical Co., Ltd.), 1 part by mass of vinyltrimethoxysilane parts and 5 parts by mass of 3-aminopropyltriethoxysilane were completely mixed under reduced pressure to obtain the first composition.

[0105] In addition, 1 part by mass of ethyl acetoacetate and 0.2 part by mass of dioctyltin ditertiary carboxylate were added to 100 parts by mass of polydimethylsiloxane terminated with silanol groups at the end with a viscosity of 20,000 mPa·s at 25°C. , mixed with a mixer to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

PROBLEM TO BE SOLVED: To provide a two-liquid mixed type organopolysiloxane composition of dealcoholization type that acquires a moderate pot life after mixing and is excellent in deep-section curability.SOLUTION: A two-liquid mixed type organopolysiloxane composition comprises a first composition and a second composition and is produced by mixing them and curing the resultant material, wherein the first composition comprises (A) an organopolysiloxane, (B) a compound chosen from a ketene silyl acetal compound, a 2-methyldialkoxysilylpropionic ester and a partial hydrolyzate thereof, (C) an organic compound and / or a silane compound each having one or more nitrogen atoms in the molecule and (D) a silane compound having two or more alkoxy groups within the molecule and / or a partial hydrolysis-condensation product thereof. The second composition comprises (E) an organopolysiloxane, (F) an organotin catalyst and (G) an ester compound.

Description

technical field [0001] The present invention relates to a dealcoholized two-liquid mixing type organopolysiloxane composition having a moderate pot life after mixing and excellent deep curability. Background technique [0002] As for the condensation-curable room-temperature rapid-curing organopolysiloxane composition, it is known that the cross-linking agent generated by hydrolysis is reduced to the limit with respect to the two-terminal hydroxyl organopolysiloxane as the base polymer. A one-component type composition with improved coupling speed and a two-component type composition in which both terminal hydroxyorganopolysiloxane as a base polymer and a crosslinking agent are packaged separately and mixed at the time of use. [0003] The one-component type of the above-mentioned composition only has a fast curing speed from the surface, and since it takes a certain time for deep curing, it is difficult to call it fast curing. Therefore, when rapid curing is required, a tw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/06C08K5/101C09K3/10C09J183/06C09J11/06