Organic feather biodegradable plastic

A technology for degrading plastics and feathers, which is applied in the field of plastics manufacturing, can solve the problems of long processing time, high cost, and low nutritional value of poultry feather feed, and achieve great economic value, market prospects, and good quality results

Inactive Publication Date: 2013-11-20
张很文
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reason is that the processing time of poultry feather feed is long, the nutritional value is low, and the cost is high
Processing plastic from feathers has not yet been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Raw material formula:

[0019] 40 parts of puffed feather powder; 35 parts of triethyl citrate; 4 parts of calcium zinc stabilizer; 8 parts of softener and 6 parts of water. Wherein the puffed feather powder adopts the mixture of chicken feather, duck feather and pig hair as raw material, wherein the weight percentages of chicken feather, duck feather and pig hair are respectively 40% of chicken feather, 40% of duck feather and 20% of pig hair.

[0020] Puffed feather meal adopts the following production methods:

[0021] 1) Grinding the mixture of chicken feathers, duck feathers and pig feathers through a pulverizer;

[0022] 2) Feed through the feeding device;

[0023] 3) Add 15% of the weight of the mixture raw material for conditioning, the boiler working pressure is 2Mpa, and the conditioning time is 5min;

[0024] 4) Extrusion is carried out by single-screw extrusion extrusion technology.

[0025] The raw materials are mixed and distributed evenly, and plastic...

Embodiment 2

[0027] Raw material formula:

[0028] 50 parts of puffed feather powder; 30 parts of triethyl citrate; 4 parts of calcium zinc stabilizer; 7 parts of softener and 8 parts of water. Wherein the puffed feather powder adopts the mixture of chicken feather, duck feather and pig hair as raw material, wherein the weight percentages of chicken feather, duck feather and pig hair are respectively 50% of chicken feather, 35% of duck feather and 15% of pig hair.

[0029] Puffed feather meal adopts the following production methods:

[0030] 1) Grinding the mixture of chicken feathers, duck feathers and pig feathers through a pulverizer;

[0031] 2) Feed through the feeding device;

[0032] 3) Add 20% of the weight of the mixture raw material for conditioning, the boiler working pressure is 2Mpa, and the conditioning time is 7 minutes;

[0033] 4) Extrusion is carried out by single-screw extrusion extrusion technology.

[0034] The raw materials are mixed and distributed evenly, and pl...

Embodiment 3

[0036] Raw material formula:

[0037] 60 parts of puffed feather powder; 25 parts of triethyl citrate; 4 parts of calcium zinc stabilizer; 6 parts of softener and 8 parts of water. Wherein the puffed feather powder adopts the mixture of chicken feather, duck feather and pig hair as raw material, wherein the weight percentages of chicken feather, duck feather and pig hair are respectively 60% of chicken feather, 20% of duck feather and 20% of pig hair.

[0038] Puffed feather meal adopts the following production methods:

[0039] 1) Grinding the mixture of chicken feathers, duck feathers and pig feathers through a pulverizer;

[0040] 2) Feed through the feeding device;

[0041] 3) Add 30% of the weight of the mixture raw material for conditioning, the boiler working pressure is 2Mpa, and the conditioning time is 10min;

[0042] 4) Extrusion is carried out by single-screw extrusion extrusion technology.

[0043] The raw materials are mixed and distributed evenly, and plasti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides organic feather biodegradable plastic. The organic feather biodegradable plastic is prepared from the follow raw materials in parts by weight: 30-70 parts of puffing feather meal, 15-45 parts of a plasticizer, 3-5 parts of a calcium zinc stabilizer, 5-10 parts of a softening agent and 5-10 parts of water. The organic feather biodegradable plastic provided by the invention has the advantages that the obtained plastic quality is good, the plastic is degraded and has no harm to environment, and the organic feather biodegradable plastic develops a new pathway for the utilization of bird feathers and has great economic values and market prospects.

Description

technical field [0001] The invention belongs to the field of plastic manufacturing, in particular to an organic feather degradable plastic. Background technique [0002] my country is rich in poultry feather resources. At present, there are two main ways to comprehensively utilize poultry feathers. One is that a small part of poultry feather resources is used to process down products; the other is that a part of poultry feathers are processed into poultry feathers Add feed to replace imported fishmeal protein feed, but the current output is not large; there are also a considerable amount of poultry feathers that are discarded as waste. The reason is that the processing time of poultry feather feed is long, the nutritional value is low, and the cost is high. Processing plastics from feathers has not been reported so far. [0003] Contents of the invention [0004] In order to solve the above technical problems, the present invention provides an organic feather degradable ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C47/00
Inventor 张很文
Owner 张很文
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com